基于声压反射系数相位谱的涂层密度和纵波声速双参数反演
          
Simultaneous Inversion of Density and Longitudinal Wave Velocity of Coatings Based on Ultrasonic Reflection Coefficient Phase Spectrum Matching Analysis

摘    要
提出一种基于声阻抗测量,采用相关系数法对涂层的声压反射系数相位谱二元非线性方程进行双参数反演,同时确定涂层密度和纵波声速的方法。采用超声脉冲回波法,采集厚度为1.929 mm铝板和厚度为0.2~0.5 mm、掺杂质量百分比30%~50%铁粉的环氧树脂涂层的超声回波信号,在有效频带范围内采用相关系数法对试样理论和试验声压反射系数相位谱进行匹配分析,利用声阻抗条件约束相关系数矩阵,约束后的相关系数矩阵最大值对应的密度和纵波声速即为涂层的最优表征结果,纵波声速和密度的反演误差均在±3.2%以内。
标    签 涂层   声压反射系数相位谱   密度   纵波声速   反演   coating   ultrasonic reflection coefficient phase spectrum   density   longitudinal wave velocity   inversion  
 
Abstract
An inversion method based on ultrasonic reflection coefficient phase spectrum (URCPS) combined with acoustic impedance constraint was proposed to simultaneously measure density and longitudinal wave velocity of thin coatings. Ultrasonic pulse echo method was employed on aluminum alloy plate with thickness of 1.929 mm and epoxy resin coatings containing 30%-50% iron powder with thickness between 0.2-0.5 mm to obtain ultrasonic signals. Then an inverse algorithm based on the correlation coefficient method was introduced to retrieve the density and longitudinal wave velocity by comparing the theoretical and experimental URCPS and searching maximum in correlation coefficient matrix constrained by acoustic impedance measured by ultrasonic method. The relative errors of the retrieved density and longitudinal wave velocity were less than ±3.2%.

中图分类号 TG115.28 TB52   DOI 10.11973/wsjc201810009

 
  购买该论文  中国光学期刊网论文下载说明


所属栏目 科研成果与学术交流

基金项目 国家自然科学基金面上项目(51675083);国家自然科学基金重点项目(U1508218)

收稿日期 2018/3/31

修改稿日期

网络出版日期

作者单位点击查看


备注高剑英(1993-),男,硕士研究生,主要从事材料无损检测与评价工作

引用该论文: GAO Jianying,ZHANG Wei,MA Zhiyuan,HE Lihua,LUO Wen,LIN Li,LEI Mingkai. Simultaneous Inversion of Density and Longitudinal Wave Velocity of Coatings Based on Ultrasonic Reflection Coefficient Phase Spectrum Matching Analysis[J]. Nondestructive Testing, 2018, 40(10): 39~44
高剑英,张伟,马志远,赫丽华,罗文,林莉,雷明凯. 基于声压反射系数相位谱的涂层密度和纵波声速双参数反演[J]. 无损检测, 2018, 40(10): 39~44


论文评价
共有人对该论文发表了看法,其中:
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
分享论文
分享到新浪微博 分享到腾讯微博 分享到人人网 分享到 Google Reader 分享到百度搜藏分享到Twitter

参考文献
【1】宣天鹏. 材料表面功能镀覆层及其应用[M]. 北京:机械工业出版社, 2008.
 
【2】胡传炘, 宋幼慧. 涂层技术原理及应用[M]. 北京:化学工业出版社, 2000.
 
【3】侯进, 陈国华. 吸波剂含量和涂层厚度对微波吸收性能的影响[J]. 功能材料, 2007, 38(7):1064-1066.
 
【4】ZHANG F F, KRISHNASWAMY S, FEI D, et al. Ultrasonic characterization of mechanical properties of Cr-and W-doped diamond-like carbon hard coatings[J]. Thin Solid Films, 2006, 503(1/2):250-258.
 
【5】HESS P. Laser diagnostics of mechanical and elastic properties of silicon and carbon films[J]. Applied Surface Science, 1996, 106(1):429-437.
 
【6】龚裕, 谭博涛, 宋国荣, 等. V(f,z)分析方法在小尺寸材料弹性常数测量中的应用[J]. 北京工业大学学报, 2012, 38(9):1298-1301.
 
【7】陈剑. 基于超声显微镜的薄层材料多参量一体化定征关键技术研究[D]. 杭州:浙江大学, 2012.
 
【8】BESCOND C, KRUGER S E, LÉVESQUE D, et al. In-situ simultaneous measurement of thickness, elastic moduli and density of thermal sprayed WC-Co coatings by laser-ultrasonics[J]. Journal of Thermal Spray Technology, 2007, 16(2):238-244.
 
【9】BREKHOVSKIKH L. Waves in layered media[M]. New York:McGraw-Hill, 1957.
 
【10】KINRA V K, IYER V R. Ultrasonic measurement of the thickness, phase velocity, density or attenuation of a thin-viscoelastic plate. Part Ⅱ:the inverse problem[J]. Ultrasonics, 1995, 33(2):111-122.
 
【11】ZHAO Y, LI X M, LIN L, et al. Measurements of coating density using ultrasonic reflection coefficient phase spectrum[J].Ultrasonics,2011,51(5):596-601.
 
【12】ZHAO Y, LIN L, LI X M, et al. Simultaneous determination of the coating thickness and its longitudinal velocity by ultrasonic nondestructive method[J]. NDT & E International, 2010, 43(7):579-585.
 
【13】MA Z Y, ZHAO Y, LUO Z B, et al. Ultrasonic characterization of thermally grown oxide in thermal barrier coating by reflection coefficient amplitude spectrum[J]. Ultrasonics, 2014, 54(4):1005-1009.
 
【14】张伟, 马志远, 高剑英, 等. 考虑孔隙细观特征的热障涂层脱粘缺陷超声检测数值模拟[J]. 中国表面工程, 2017, 30(3):115-121.
 
【15】张伟, 马志远, 赫丽华, 等. 基于声压反射系数幅度谱匹配分析的薄层厚度和超声纵波声速双参数反演[J]. 材料工程, 2016, 44(10):74-79.
 
【16】MA Z Y, ZHANG W, DU P C, et al. Nondestructive measurement of elastic modulus for thermally sprayed WC-Ni coatings based on acoustic wave mode conversion by small angle incidence[J]. NDT & E International, 2017,94:38-46.
 
【17】MA Z Y, ZHANG W, GAO J Y, et al. Characterization of the interface roughness of coatings based on ultrasonic reflection coefficient amplitude spectrum[C]//Atlanta:AIP Publishing, 2017.
 
相关信息
   标题 相关频次
 基于超声声压反射系数相位谱法的热障涂层非均匀性表征
 4
 大型储罐器壁腐蚀减薄的自动超声扫查
 3
 涂料密度测定的不确定度评定
 3
 20#钢在三元复合驱弱碱体系采出液中的腐蚀与防护
 2
 55CrMo钢热物性参数的测定
 2
 6156铝合金疲劳裂纹的扩展速率
 2
 800 MPa级高强钢埋弧焊用烧结焊剂的研制及性能
 2
 ASTM SMO254板式换热器腐蚀的原因
 2
 C/C复合材料高温抗烧蚀涂层的研究进展
 2
 CFRP复合材料孔隙形貌特征的统计分析
 2
 FBE与聚苯胺粉末共混涂层的防腐蚀性能
 2
 HIPIB辐照前后Cr2O3陶瓷涂层超声衰减特性研究
 2
 ICT技术测试炭/炭复合材料内部密度分布
 2
 Lamb波在薄铝板无损评价中的模态识别与应用
 2
 NbSe2纳米颗粒的合成及减摩性能
 2
 S135钻杆刺漏失效分析及疲劳验证试验
 2
 SA210C无缝中碳钢管带状组织的评定方法
 2
 U形振动管法测定原油密度的影响因素
 2
 X射线荧光光谱法测定废塑料表面涂层中8种元素的含量
 2
 ZG06Cr13Ni4Mo不锈钢超音速火焰喷涂WC-10Co-4Cr涂层的抗磨蚀性能
 2
 编织-嵌槽型金属橡胶的力学性能和阻尼性能
 2
 玻璃纤维和硫脲缓蚀剂对涂层缓蚀行为的影响
 2
 不同表面处理对输电线路铁塔涂层性能的影响
 2
 材料及防护涂层在淡水环境中的腐蚀试验研究
 2
 测定陶瓷材料密度及其气孔率的方法
 2
 长庆油田原油储罐腐蚀现状与防腐蚀技术
 2
 长输管线外防护涂层技术的现状与发展探讨
 2
 超声波涂层测厚仪示值误差的不确定度评定
 2
 储罐底板漏磁检测腐蚀缺陷轮廓反演方法
 2
 次高压燃气储罐适用内涂层
 2