石墨烯类粉体比表面积的氮气吸附法测量条件与不确定度评定
          
Measurement Conditions and Uncertainty Evaluation of Specific Surface Area of Graphene Powder by Nitrogen Adsorption Method

摘    要
采用氮气吸附静态容量法(氮气吸附法),以氧化还原石墨烯/金属氧化物粉体为研究对象,利用ASAP 2460型比表面积和孔隙度分析仪测量了其比表面积,确定了测量比表面积的理想测试条件,并对测量不确定度进行评定。结果表明:氮气吸附法测量石墨烯类粉体比表面积的理想样品用量为0.2~0.4 g。比表面积不确定度的评定仅考虑测量重复性、天平称量样品质量及标样引入的标准不确定度,在置信水平p为95%,自由度Vrel为32时,采用氮气吸附法物理吸附仪测量石墨样品比表面积的扩展不确定度为14.55 m2·g-1
标    签 石墨烯   比表面积   氮气吸附法   不确定度   graphene   specific surface area   nitrogen adsorption method   uncertainty  
 
Abstract
Specific surface area of redox graphene/metal oxide powder was measured by ASAP 2460 specific surface area and porosity analyzer using nitrogen adsorption static capacity method (nitrogen adsorption method). The ideal test conditions were determined, and the measurement uncertainty was evaluated. The results show that the ideal sample amount for measuring the specific surface area of graphene powder by nitrogen adsorption method is 0.2~0.4 g. The uncertainty evaluation of specific surface area only considers the standard uncertainty introduced by measurement repeatability, the weight of sample weighed by the balance and the standard sample. When the confidence level p is 95% and the degree of freedom Vrel is 32, the expanded uncertainty of specific surface area of graphite sample measured by nitrogen adsorption method physical adsorption instrument is 14.55 m2·g-1.

中图分类号 TB99   DOI 10.11973/lhjy-wl202107001

 
  中国光学期刊网论文下载说明


所属栏目 试验与研究

基金项目 内蒙古自治区科技创新引导项目(KCBJ2018032)

收稿日期 2021/3/17

修改稿日期

网络出版日期

作者单位点击查看


备注侯渊(1985-),男,博士,主要从事复合材料的制备与表征方法研究工作,houyuan@imust.edu.cn

引用该论文: HOU Yuan,WU Yiwen,WU Xiaoliang,ZHU Wenguang,ZHANG Bangwen. Measurement Conditions and Uncertainty Evaluation of Specific Surface Area of Graphene Powder by Nitrogen Adsorption Method[J]. Physical Testing and Chemical Analysis part A:Physical Testing, 2021, 57(7): 1~5
侯渊,吴益文,武晓亮,朱文广,张邦文. 石墨烯类粉体比表面积的氮气吸附法测量条件与不确定度评定[J]. 理化检验-物理分册, 2021, 57(7): 1~5


论文评价
共有人对该论文发表了看法,其中:
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
分享论文
分享到新浪微博 分享到腾讯微博 分享到人人网 分享到 Google Reader 分享到百度搜藏分享到Twitter

参考文献
【1】GEIM A K,NOVOSELOV K S. The rise of graphene[J]. Nature Materials,2007,6(3):183-191.
 
【2】HUANG X,QI X Y,BOEY F,et al. Graphene-based composites[J]. Chemical Society Reviews,2012,41(2):666-686.
 
【3】LI X,ZHI L. Graphene hybridization for energy storage applications[J]. Chemical Society Reviews,2018,47(9):3189-3216.
 
【4】STANKOVICH S,DIKIN D A,PINER R D,et al. Synthesis of graphene-based nanosheets via chemical reduction of exfoliated graphite oxide[J]. Carbon,2007,45(7):1558-1565.
 
【5】SMITH A T,LACHANCE A M,ZENG S S,et al. Synthesis,properties,and applications of graphene oxide/reduced graphene oxide and their nanocomposites[J]. Nano Materials Science,2019,1(1):31-47.
 
【6】曾燕飞,辛国祥,布林朝克,等. 一步法制备三维还原氧化石墨烯/NiO超级电容器电极材料及其性能研究[J]. 无机材料学报,2018,33(10):1070-1076.
 
【7】闫晓英,高原,郭延军. 氮气吸附静态容量法测定固体材料比表面积不确定度评定[J]. 计量学报,2017,38(5):543-547.
 
相关信息
   标题 相关频次
 不同比表面积石墨烯对水性环氧富锌防腐蚀涂层性能的影响
 4
 洛氏硬度B标尺测量不确定度的评定及分析
 3
 30CrMnSiA钢激光再制造件的性能
 2
 CeO2-MnO2纳米氧化物/石墨烯复合电极材料的制备及其超级电容性能
 2
 Excel在最小二乘法不确定度评定中的应用
 2
 ISO 8794:2020《钢丝绳插编索具》国际标准的修订及技术创新
 2
 S355J2+N钢板拉伸试验测量结果的不确定度评定
 2
 TC4钛合金棒材拉伸试验结果的不确定度评定
 2
 TCS345型不锈钢板Rp0.2测量结果的不确定度评定
 2
 TiN和TiCrN膜层对氢燃料电池双极板材料316L不锈钢性能的影响
 2
 X射线衍射法测定圆棒表面残余应力的影响因素
 2
 标距对电工圆铜线拉力试验结果的影响
 2
 薄壁管涡流检测的不确定度评定
 2
 不同比表面积SiO2对磁流变液流变特性和沉降稳定性的影响
 2
 不同方法测量截面积求铜合金圆导线电阻系数的不确定度评定
 2
 不同厚度电镀铬层的组织及性能
 2
 不同形态二氧化钛-石墨烯复合材料的表征及光催化性能研究
 2
 残余应力测试结果的定性分析与判断
 2
 测量方法确认技术及其指标评价
 2
 长春地辛在硫化铜纳米花/石墨烯修饰玻碳电极上的电化学行为
 2
 超声波涂层测厚仪示值误差的不确定度评定
 2
 单层完美石墨烯的理论比表面积推导
 2
 低地轨道空间中原子氧对聚酰亚胺的侵蚀及其防护措施
 2
 低蠕变砖压蠕变率测试结果的不确定度评定
 2
 定型隔热制品导热系数(水流量平板法)不确定度的评定
 2
 分析方法不确定度评定的通用数学模型
 2
 复合材料结构超声检测的不确定度评定
 2
 钢丝绳张力测量仪的校准及不确定度评定
 2
 钢丝绳整绳破断力测定方法国际标准ISO 3108:2017的修定过程及技术改进
 2
 硅砖线膨胀率和平均线膨胀系数测定的不确定度评定
 2