15Cr低合金钢和N80钢的二氧化碳腐蚀性能对比
          
Contrast on CO2 Corrosion Performance between 15Cr Low Alloy Steel and N80 Steel

摘    要
采用电化学方法对比研究了不同温度下15Cr低合金钢和N80钢在模拟CO2腐蚀介质中的耐蚀性能。结果表明, 随着温度的升高, 两种材料的腐蚀电流密度(Jcorr)有所增大, 电荷传递电阻(Rt)不断减小; 中高频区的容抗弧不断缩小, 低频区的感抗弧也不断萎缩, 低频区小容抗弧出现; 15Cr低合金钢的耐蚀性能在较低温度下比N80钢稍差, 而在较高温度下比N80钢稍强。
标    签 CO2腐蚀   15Cr低合金钢   N80钢   极化曲线   电化学阻抗谱   CO2 corrosion   15Cr low alloy steel   N80 steel   polarization curve   electrochemical impedance spectroscopy  
 
Abstract
The CO2 corrosion performance of 15Cr low alloy steel and N80 steel were investigated by electrochemical methods at various temperatures in simulated CO2 corrosion medium. The results indicated that with the increase of temperature, the corrosion current density decreased, the charge transfer resistance decreased, and the capacitance arc at intermediate-high frequency and inductance arc at low frequency gradually dwindled, while small capacitance arc at low frequency occurred. In addition, 15Cr low alloy steel had a little worse anti-corrosion performance than N80 steel at lower temperature, inversely at higher temperature.

中图分类号 TG174

 
  中国光学期刊网论文下载说明


所属栏目 试验研究

基金项目 “863计划”(2012AA050103);国家科技支撑计划项目(2012BAC26B00)

收稿日期 2013/6/9

修改稿日期

网络出版日期

作者单位点击查看


备注杨志刚(1973-), 高级工程师, 博士后, 从事油田材料腐蚀与防护工作,

引用该论文: YANG Zhi-gang,YIN Zhi-fu,ZHAO Liang,ZHANG Yong-qiang,LIU Jie. Contrast on CO2 Corrosion Performance between 15Cr Low Alloy Steel and N80 Steel[J]. Corrosion & Protection, 2014, 35(4): 321


论文评价
共有人对该论文发表了看法,其中:
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
分享论文
分享到新浪微博 分享到腾讯微博 分享到人人网 分享到 Google Reader 分享到百度搜藏分享到Twitter

参考文献
【1】路民旭, 赵新伟, 赵国仙, 等. 油气采集储运中的腐蚀现状及典型案例[J]. 腐蚀与防护, 2003, 23(3):36-40.
 
【2】KERMAN M B, MORSHED A. Carbon dioxide corrosion in oil gas production compendium critical review of corrosion science and engineering[J]. Corrosion 2003, 59(8):659-683.
 
【3】WAARD C de, MILLIAMS D E. Carbonic acid corrosion of steel[J]. Corrosion, 1975, 31(5):175-181.
 
【4】王霞, 马发明, 陈玉祥, 等. 注CO2提高采收率工程中的腐蚀机理及防护措施[J]. 钻采工艺, 2006, 29(6):73-76.
 
【5】LINNE C P, BLANCHARD F, GUNTZ G C. Corrosion performances of modified 13Cr for OCTG in oil and gas environments[C]//Corrosion 1997. Houston:NACE, 1997:Paper No 28.
 
【6】ABAYARATHNA D, KRME R D. Definition of safe service use limits for use of stainless alloys in petroleum production[C]//Corrosion 1997. Houston:NACE, 1997:Paper No 34.
 
【7】JUTTNER K. Electrochemical impedance spectroscopy (EIS) of corrosion process on inhomogeneous surfaces[J]. Electrochimica Acta, 1990, 35(10):1501-1508.
 
【8】曹楚南. 腐蚀电化学原理[M]. 北京:化学工业出版社, 2004.
 
相关信息
   标题 相关频次
 N80和3Cr油管钢在CO2驱油环境中的腐蚀行为
 6
 二氧化碳驱油环境中典型管柱材料的腐蚀行为与特征
 6
 模拟CO2驱油环境下温度对J55油管钢腐蚀行为的影响
 6
 温度对N80钢在CO2饱和的NaCl溶液中的腐蚀电化学行为的影响
 6
 CO2分压对N80油管钢CO2腐蚀行为的影响
 4
 CO2驱油地面集输管道的腐蚀电化学行为
 4
 HEDP-ATMP-TTA缓蚀剂对HSn70-1A铜合金强激光与粒子束腐蚀行为的影响
 4
 J55钢在气液双相流NaCl溶液中的腐蚀行为
 4
 Q235钢在煤浸出液中的腐蚀行为
 4
 X70钢在常压和高压环境中的腐蚀电化学行为对比
 4
 X70钢在含硫酸盐还原菌喷气燃料中的腐蚀行为
 4
 X80管线钢在不同pH满洲里土壤模拟溶液中的腐蚀行为
 4
 磁化水对金属耐蚀性能的影响
 4
 大气环境中SO2和H2S对铜的电化学腐蚀行为比较
 4
 单氟磷酸钠在混凝土模拟孔隙液中的缓蚀特性
 4
 改性聚酰胺对CO2环境中N80钢的缓蚀作用
 4
 含氮杂环双季铵盐在高温酸性溶液中的缓蚀性能
 4
 缓蚀剂MJ对碳钢在硫离子介质中的缓蚀性能
 4
 黄铜在含硫酸盐还原菌的模拟冷却水中的腐蚀行为
 4
 硫脲改性咪唑啉对不同显微组织钢的抗CO2腐蚀性能
 4
 模拟CO2驱环境中咪唑啉类缓蚀剂对J55钢腐蚀性能的影响
 4
 模拟混凝土孔隙液中N, N-二甲基乙醇胺的阻锈作用
 4
 热处理对N80钢表面镍基合金涂层CO2腐蚀性能的影响
 4
 热轧钢板表面氧化层对基体耐蚀性的影响
 4
 食品级磷酸浓度对国产904L不锈钢耐蚀性的影响
 4
 铈盐掺杂GPTMS/TEOS硅烷杂化膜腐蚀电化学行为随时间的变化
 4
 酸性NaCl溶液中CuNi2Si合金的电化学腐蚀行为
 4
 温度对J55油管CO2腐蚀行为的影响
 4
 温度对N80钢在CO2/O2共存环境中腐蚀行为的影响
 4
 乌洛托品对超纯铁素体不锈钢酸洗的缓蚀效果
 4