3A21铝合金在乙二醇水溶液中的腐蚀行为
          
Corrosion Behavior of 3A21 Aluminum Alloy in Ethylene Glycol-water Solution

摘    要
采用电化学方法研究了3A21铝合金在乙二醇水溶液中在不同浓度、温度和浸泡时间条件下的腐蚀电化学行为。采用扫描电子显微镜研究了腐蚀前后3A21铝合金的形貌及表面腐蚀产物。结果表明,随着乙二醇水溶液浓度的增加,铝合金腐蚀速率下降; 随着溶液温度升高,铝合金腐蚀速率增大; 随着铝合金浸泡时间的延长,一方面,氧化膜的生成和溶解达到动态平衡,另一方面氧化膜薄弱区出现点蚀,点蚀的发展伴随着点蚀的自愈合,并向点蚀加剧方向发展。
标    签 3A21铝合金   乙二醇水溶液   浸泡时间   点蚀   腐蚀产物   3A21aluminum alloy   ethylene glycol aqueous solution   immersion time   pitting corrosion   corrosion product  
 
Abstract
The electrochemical corrosion behaviors of 3A21 aluminum alloy in ethylene glycol-water solutions at different temperatures, concentrations and immersion times were studied by electrochemical methods. The surface characteristics and corrosion products were examined by scanning electron microscopy (SEM). It was found that with increasing the ethylene glycol concentration, the corrosion rate of the aluminum alloy decreased, and with increasing the temperature, the corrosion rate of the alloy increased. With increasing the immersion time, the formation and dissolution of oxide film on the alloy achieved dynamic equilibrium, and pitting appeared at the weak areas on the oxide film. The development of pitting was accompanied by pitting self-healing and pitting aggravation.

中图分类号 TG174.4

 
  中国光学期刊网论文下载说明


所属栏目 试验研究

基金项目 四川理工学院省级大学生创新创业训练计划项目(201310622026); 四川理工学院研究生创新基金(y2012012)

收稿日期 2013/12/27

修改稿日期

网络出版日期

作者单位点击查看


备注龚敏(1963-),教授,硕士,从事材料腐蚀与防护研究,

引用该论文: FAN Jin-long,GONG Min,HOU Xiao,LI Xing-qiang,LUO Yan-guang,KANG Bo,SUN Wei,GUO Mei-bo,LIANG Xian-zhong. Corrosion Behavior of 3A21 Aluminum Alloy in Ethylene Glycol-water Solution[J]. Corrosion & Protection, 2014, 35(11): 1116


论文评价
共有人对该论文发表了看法,其中:
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
分享论文
分享到新浪微博 分享到腾讯微博 分享到人人网 分享到 Google Reader 分享到百度搜藏分享到Twitter

参考文献
【1】LIU Y,CHENG Y F. Characterization of passivity and pitting corrosion of 3003 aluminum alloy in ethylene glycol-water solutions[J]. J Appl Electrochem,2011,41:151-159.
 
【2】金星,饶楚仪,高立新,等. 铝合金在乙二醇-水模拟冷却液中的腐蚀行为[J]. 材料保护,2011,44(9):15-17.
 
【3】NIU L,CHENG Y F. Electrochemical characterization of metastable pitting of 3003 aluminum alloy in ethylene glycol-water solution[J]. J Mater Sci,2007,42:8613-8617.
 
【4】OLUSEGUN K A,OTAIGBE J O E. Effect of common water contaminants on the corrosion of aluminium alloys in ethylene glycol-water solution[J]. Corrosion Science,2008,50:242-247.
 
【5】XU L Y,CHENG Y F. Electrochemical characterization and CFD simulation of flow-assisted corrosion of aluminum alloy in ethylene glycol-water solution[J]. Corrosion Science,2008,50:2094-2100.
 
【6】胡丽华,常炜,路民旭,等. 乙二醇对海底管道CO2腐蚀的抑制作用[J]. 腐蚀与防护,2012,33(6): 463-469.
 
相关信息
   标题 相关频次
 腐蚀产物对6061铝合金海洋大气腐蚀过程的影响
 4
 2205双相不锈钢在卤水环境中的腐蚀行为
 3
 HEDP对1Cr18Ni9Ti在硝酸中腐蚀行为的影响
 3
 0Cr13铁素体不锈钢在FeCl3溶液中的点蚀行为
 2
 2205双相不锈钢在HCl溶液中点蚀的AFM和电化学分析
 2
 304、316不锈钢和Inconel 617镍基合金在硝酸熔盐中的腐蚀行为
 2
 316L不锈钢在FeCl3溶液中点蚀行为的电化学噪声检测
 2
 316L钢内衬复合管焊接接头的耐点蚀性能
 2
 316NG不锈钢在高纯水环境中的腐蚀行为
 2
 3A12、5052、6063铝合金在沿海大气环境中的腐蚀行为
 2
 3PE防腐蚀层联合阴极保护对管道的保护效果
 2
 3-甲基-2-噻唑硫酮对HCl溶液中碳钢的缓蚀作用
 2
 7075-TiB2原位铝基复合材料的腐蚀性能
 2
 Cl-,CO2和微量H2S共存时13Cr不锈钢的腐蚀性能
 2
 Cl-对304L不锈钢从点蚀到应力腐蚀转变行为的影响
 2
 Cl-浓度对2A12铝合金电化学行为的影响
 2
 CO2/H2S分压比对BG90SS材质腐蚀行为的影响
 2
 CO2驱采出井井下附件材料的腐蚀评价与优选
 2
 EB104/EB202涂层对904L不锈钢的防腐蚀效果
 2
 EH36级平台钢耐海洋大气腐蚀性能
 2
 NaCl对Q235钢早期腐蚀行为的影响
 2
 NiAl-31Cr-3Mo合金的低温热腐蚀性能
 2
 P110钢和TP110SS钢在含不同饱和气体NaCl溶液中的腐蚀行为
 2
 P110油管腐蚀穿孔原因分析
 2
 PPy/α-Fe2O3复合材料的合成及其耐蚀性
 2
 S2O2-3对Cu-15Ni-8Sn合金在NaCl溶液中点蚀的影响
 2
 S32750双相不锈钢六角头螺栓腐蚀失效分析
 2
 SO2-4对X80管线钢在含Cl-的NaHCO3溶液中点蚀行为影响
 2
 SS411NS型杀菌剂对Q235钢在循环冷却水中腐蚀行为的影响
 2
 TA2在卤水环境中的缝隙腐蚀电化学行为
 2