H13钢表面电火花沉积Deloro 50合金层的组织和性能
          
Microstructure and Properties of Deloro 50 Alloy Layer Deposited on H13 Steel by Electro Spark Deposition

摘    要
利用电火花沉积技术在H13钢基体表面制备了Deloro 50合金层,采用扫描电镜和X射线衍射仪研究了沉积层的微观结构和物相组成,并采用显微硬度计测试了沉积层的硬度。结果表明: 沉积层与基体呈良好的冶金结合,平均厚度约35 μm;沉积层主要由FeNi3,Ni3(CrFe),C6(Co,Cr,Ni)23相组成;沉积层的表层显微硬度为954.4 HV0.05,约为H13钢基体硬度的2倍。
标    签 H13钢   电火花沉积   Deloro 50合金   微观结构   硬度   H13 steel   electro spark deposition   Deloro 50 alloy   microstructure   hardness  
 
Abstract
Deloro 50 alloy layer was deposited on H13 steel by electro spark deposition(ESD) process, and the microstructure and phase compositions of Deloro 50 alloy layer were characterized by scanning electronic microscope(SEM) and X-ray diffractionmeter(XRD) and the alloy layer hardness was tested by a microhardness tester. The results show that excellent metallurgical bonding between the alloy layer and the substrate was obtained by ESD. The alloy layer had an average thickness of about 35 μm. The microstructure of the alloy layer was mainly composed of FeNi3, Ni3(CrFe) and C6(Co,Cr,Ni)23 phases. The microhardness of the surface layer was 954.4 HV0.05 which was two times of hardness of the substrates.

中图分类号 TG142.1 TG174.4

 
  中国光学期刊网论文下载说明


所属栏目 试验与研究

基金项目

收稿日期 2013/11/29

修改稿日期

网络出版日期

作者单位点击查看

备注贾元伟(1975-),男,工程师。

引用该论文: JIA Yuan-wei. Microstructure and Properties of Deloro 50 Alloy Layer Deposited on H13 Steel by Electro Spark Deposition[J]. Physical Testing and Chemical Analysis part A:Physical Testing, 2014, 50(10): 723~726
贾元伟. H13钢表面电火花沉积Deloro 50合金层的组织和性能[J]. 理化检验-物理分册, 2014, 50(10): 723~726


论文评价
共有人对该论文发表了看法,其中:
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
分享论文
分享到新浪微博 分享到腾讯微博 分享到人人网 分享到 Google Reader 分享到百度搜藏分享到Twitter

参考文献
【1】刘英坤,朱峰,伍超群,等. 不同表面处理工艺下H13钢的高温耐磨性能[J]. 理化检验-物理分册,2012,48(10):645-648.
 
【2】ZHANG Ping,MA Lin,LIANG Zhi-jie,et al. Preparation and mechanical properties of two nickel base alloy coating achieved by electrospark deposition[J]. Acta Metallurgical Sinica: English Letters,2011,24(4):309-314.
 
【3】高文文,吴玉萍,杜海清,等. 纳米Al2O3封孔对电弧喷涂3Cr13涂层耐腐蚀性能的影响[J]. 理化检验-物理分册,2013,49(12):785-789.
 
【4】CHEN Z,ZHOU Y. Surface modification of resistance welding electrode by electro-spark deposited composite coatings-Part Ⅰ:Coating characterization[J]. Surface and Coatings Technology,2006,201:1503-1510.
 
【5】WANG R J,QIAN Y Y,LIU J. Structural and interfacial analysis of WC92-Co8 coating deposited on tita-nium alloy by electrospark deposition[J]. Applied Surface Science,2004,228:405-409.
 
【6】LI X,SUN D Q,ZHENG X Y,et al. Microstructures and wear properties of TiN-based cermet coating deposited on 1Cr18Ni9Ti stainless steel by electrospark process[J]. Materials Science and Engineering:A,2008,490(1/2):126-130.
 
【7】BROCHU M,PORRILLO J G,MILLIGAN J,et al. Development of metastable solidification structure using the electrospark deposition process[J]. The Open Surface Journal,2011,3:105-114.
 
【8】JOHNSON R N,SHELDON G L. Advance in the electrospark deposition coating process[J]. Journal of Vacuum Science and Technolog A:Vacuum,Surfaces,Films,1986,4(6):2740-2746.
 
【9】张鲲,何业东,王德仁. 电火花沉积MCrAlY涂层及其高温氧化行为[J]. 材料热处理学报,2008,29(4):143-147.
 
【10】ZAMULAEVA E I,LEVASHOV E A,KUDRYASHOV A E,et al. Electrospark coating deposited onto an armco iron substrate with nano-and microstructured WC-Co electrodes:Deposition process,structure,and properties[J]. Surface and Coatings Technology,2008,202:3715-3722.
 
相关信息
   标题 相关频次
 纳米压痕技术表征Al2O3/3%TiO2爆炸喷涂涂层的各向异性
 4
 氧化石墨烯质量浓度对超临界镍基石墨烯复合电铸层性能的影响
 4
 102钢的显微组织形态与室温力学性能的关系
 3
 13MnNiMoNbR与00Cr19Ni10异种钢焊接接头的组织与性能
 3
 16MND5/309L/308L/Z2CND18-12N异种金属焊接件的组织和性能
 3
 2507双相不锈钢模拟焊接热影响区的组织与性能
 3
 4种成分车轮钢与U71Mn钢轨钢间的磨损行为
 3
 C300马氏体时效钢等离子弧焊接接头的组织与硬度
 3
 ZG45铸钢表面Ni/ZrO2复合铸渗层的组织与耐磨性能
 3
 稠油热采注汽管网的组织和性能
 3
 穿孔顶头的表面凹陷分析
 3
 大规格H13热作模具钢锻件的组织和性能
 3
 堆焊工艺对高铬合金粉体堆焊层组织及耐磨性能的影响
 3
 钒添加量对Mo2FeB2基金属陶瓷显微组织和力学性能的影响
 3
 高温变形后的停留处理对不含铌、钛元素超低碳钢中温相变的影响
 3
 高温时效Super304H耐热钢的组织、硬度及其关系模型
 3
 钴对AlFeCuCrNi高熵合金组织和性能的影响
 3
 国产X80管线钢管焊接接头的力学性能
 3
 含硅中碳钢热轧过程中表面脱碳的控制
 3
 焊后热处理对T122钢焊接接头组织及硬度的影响
 3
 焊接电流对镍基铌复合堆焊层组织及性能的影响
 3
 激光冲击强化对LY2铝合金残余应力、显微组织及疲劳性能的影响
 3
 激光熔覆碳纳米管增韧铁基非晶涂层的组织与力学性能
 3
 激光熔凝处理高碳高铬轧辊钢的组织及硬度
 3
 铝含量对Cu-5.6Ni-2.5Mn-2Sn合金组织与性能的影响
 3
 满滚子轴承滚柱脱落与掉块原因分析
 3
 锰、铜含量对锌铝合金组织与性能的影响
 3
 热处理工艺对3Cr2W8V热作模具钢高温磨损性能的影响
 3
 热处理工艺对Cr12W钢组织和硬度的影响
 3
 热处理工艺对GCr15钢轴承外环淬火组织和性能的影响
 3