NAK80模具钢表面激光熔覆钴基合金涂层的组织和摩擦磨损性能
          
Microstructure and Friction and Wear Properties of Laser Clad Co-Based Alloy Coating on Surface of NAK80 Mold Steel

摘    要
采用激光熔覆方法在NAK80模具钢表面制备钴基合金熔覆层, 用扫描电镜、X射线衍射仪分析了熔覆层的显微组织, 通过干滑动摩擦试验研究了熔覆层的摩擦磨损性能, 分析了其磨损机制, 并用三维表面形貌仪观察磨损试样的表面形貌。结果表明: 熔覆层的主要组成相为Cr23C6、Co3Mo2Si、MoC、FeCr和γ-Co; 熔覆层由涂层与基体界面处的平面晶区、涂层中部的胞状树枝晶区和表层的网状等轴晶粒区组成; 经激光熔覆处理后的NAK80模具钢表面硬度和耐磨性得到了显著改善, 与NAK80模具钢相比, 熔覆层表面的平均摩擦因数降低了约34%, 比磨损率下降了约91.3%; 熔覆层的磨损机制为粘着磨损和轻微的显微切削。
标    签 激光熔覆   钴基合金   NAK80模具钢   组织   摩擦磨损性能   laser cladding   Co-based alloy   NAK80 mold steel   microstructure   friction and wear property  
 
Abstract
The Co-based alloy cladding coating was successfully fabricated on the surface of NAK80 mold steel by laser cladding technology. The microstructure of the coating was analyzed by scanning electron microscopy (SEM), X-ray diffraction (XRD). The property of friction and wear, and the wear mechanism were studied by the dry sliding friction test. The morphology of wear samples were measured by 3D surface profilometer. The results show that the cladding coating was mainly composed of Cr23C6, Co3Mo2Si, MoC, FeCr and γ-Co. The plane crystal in the interface of the coating and the substrate, cellular dendrite at the central zone and reticular equiaxed crystal near top surface were observed in the cladding coating. The microhardness and wear resistance of NAK80 mold steel surface were improved noticeably by laser cladding technology. Compared with NAK80 mold steel, the average friction coefficient of the cladding coating decreased by about 34%, and the wear rate reduced by about 91.3%. The wear mechanism for the laser cladding coating was adhesive wear and slight micro-cutting.

中图分类号 TG174.4

 
  中国光学期刊网论文下载说明


所属栏目 试验研究

基金项目 国家自然科学基金资助项目(51002101); 台州学院培育基金资助项目(2011PY31)

收稿日期 2011/8/1

修改稿日期 2012/4/21

网络出版日期

作者单位点击查看

备注程虎(1981-), 男, 江西九江人, 讲师, 硕士。

引用该论文: CHENG Hu,DAI Sheng,FANG Zhi-gang,ZHAO Xian-rui,GAO Yu-xin. Microstructure and Friction and Wear Properties of Laser Clad Co-Based Alloy Coating on Surface of NAK80 Mold Steel[J]. Materials for mechancial engineering, 2012, 36(8): 37~41
程虎,戴晟,方志刚,赵先锐,高玉新. NAK80模具钢表面激光熔覆钴基合金涂层的组织和摩擦磨损性能[J]. 机械工程材料, 2012, 36(8): 37~41


论文评价
共有人对该论文发表了看法,其中:
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
分享论文
分享到新浪微博 分享到腾讯微博 分享到人人网 分享到 Google Reader 分享到百度搜藏分享到Twitter

参考文献
【1】曲庆文, 党军建, 郭秀萍. 模具寿命与摩擦学设计[J].山东理工大学学报:自然科学版, 2004, 18(1):34-37.
 
【2】WANG H Y, ZUO D W, YAN J, et al. Effects of nanometer Al2O3 particles on oxidation behaviors of laser cladding low Al NiCoCrAlY coatings[J].Oxidation of Metals, 2010, 74(1/2):49-60.
 
【3】WANG H, ZUO D, LI X, et al. Effects of CeO2 nanoparticles on microstructure and properties of laser cladded NiCoCrAlY coatings[J].Journal of Rare Earths, 2010, 28(2):246-250.
 
【4】NAVAS C, CONDE A, FERNNDEZ B J, et al. Laser coatings to improve wear resistance of mould steel[J].Surface and Coatings Technology, 2005, 194(1):136-142.
 
【5】骆芳, 陈智君, 楼程华, 等.塑料模具钢表面激光熔覆陶瓷复合涂层的性能研究[J].兵工学报, 2010, 31(7):933-938.
 
【6】CHEN J Y, CONLON K, XUE L, et al. Experimental study of residual stresses in laser clad AISI P20 tool steel on pre-hardened wrought P20 substrate[J].Materials Science and Engineering A, 2010, 527(27/28):7265-7273.
 
【7】赵洪运, 刘喜明, 连建设, 等.辊锻模具表面送粉激光熔覆WC陶瓷层的高温组织与性能[J].焊接学报, 2002, 23(5):12-14.
 
【8】温良英, 陈洪, 白晨光, 等.10Ni3MnCuAl模具钢中厚板生产工艺优化[C] // 2006年全国冶金物理化学学术会议论文集.济南: 中国金属学会, 2006.
 
【9】唐庆江, 莫敦.10Ni3MnCuAl的脱氧工艺研究[J].特钢技术, 2002, 10(3):11-13.
 
【10】MIAO H, ZUO D W, WANG H J. Surface characteristics of 10Ni3MnCuAl steel by shot peening[J].Transactions of Nanjing University of Aeronautics & Astronautics, 2009, 26(3):178-183.
 
【11】汪洪峰, 左敦稳, 邵定林, 等.退火温度对7022铝合金干摩擦性能的影响[J].深圳大学学报:理工版, 2010, 27(2):131-136.
 
【12】李志远, 赵伟毅, 聂登攀, 等.TiN对Co基合金激光熔覆层组织与性能的影响[J].强激光与粒子束, 2010, 22(7):1657-1660.
 
【13】王红颖, 崔承云, 周杰. 工具钢表面激光熔覆Co基合金涂层的组织及性能[J].吉林大学学报:工学版, 2010, 40(4):1000-1004.
 
相关信息
   标题 相关频次
 CeO2加入含量对激光熔覆WC增强镍基合金涂层组织与性能的影响
 4
 激光熔覆NiCrBSi/WC-Co复合涂层的组织与耐磨性能
 4
 激光熔覆碳纳米管增韧铁基非晶涂层的组织与力学性能
 4
 镍包SiCp增强Ni35合金激光熔覆层的显微组织及摩擦磨损性能
 4
 钛合金表面激光熔覆Ti/Ni+ZrO2涂层的组织与性能
 4
 添加Y2O3对激光熔覆原位合成TiB2和TiC增强镍基复合涂层组织的影响
 4
 真空环境与基体预热对激光熔覆WC增强镍基合金涂层组织和性能的影响
 4
 35CrMo钢表面铁基激光熔覆层的组织和耐磨性能
 3
 AlSi7Mg铝合金表面激光熔覆WC增强镍基合金熔覆层的组织与性能
 3
 Ni60合金包覆WC粉激光熔覆涂层的组织与性能
 3
 不同温度固溶+时效处理对6082铝合金锻件组织和摩擦磨损性能的影响
 3
 工业纯钛板多道次搅拌摩擦加工区的组织及摩擦磨损性能
 3
 铌对镍基合金激光熔敷层组织和显微硬度的影响
 3
 球墨铸铁表面激光熔覆铁基合金层的组织与性能
 3
 热处理前后镍基高温合金激光熔覆层的组织和力学性能
 3
 06CuNiCrMoNb钢模拟焊接热影响区的组织和性能
 2
 0Cr18Ni9钢表面等离子铌合金化层的显微组织和摩擦磨损性能
 2
 20Cr钢与B级钢焊接接头的组织和性能
 2
 2205双相不锈钢/Q345低合金钢爆炸复合板的组织与力学性能
 2
 316不锈钢表面等离子熔敷硼化物覆层的组织与性能
 2
 5083/6063不等厚铝合金双丝CMT角焊接头的组织与性能
 2
 6061-T6铝合金超声辅助搅拌摩擦焊接头的组织与力学性能
 2
 630 ℃长时时效对G112钢组织和力学性能的影响
 2
 Al-Cu合金片对钢/铝异种金属激光-MIG复合焊接头组织和性能的影响
 2
 AZ31镁合金表面Al-Ti-TiB2激光熔覆层的组织和性能
 2
 C300马氏体时效钢等离子弧焊接接头的组织与硬度
 2
 CNTs/AZ91复合材料的摩擦磨损性能
 2
 Cr3C3/镍基合金等离子堆焊层的组织及耐磨性能
 2
 Fe-Al/TiC激光熔覆层的高温摩擦磨损和氧化性能
 2
 GCr15轴承钢在盐酸溶液中的点蚀行为
 2