T91钢在碱金属氯化物介质中的高温腐蚀行为
          
High Temperature Corrosion Behavior of T91 in Alkali Metal Chloride Medium

摘    要
模拟生物质电厂锅炉过热器的烟气侧环境, 对过热器材料T91进行了高温腐蚀研究。采用试样腐蚀增重试验, 测得了腐蚀动力学曲线; 采用扫描电镜(SEM)、能谱仪(EDS)和X射线衍射仪(XRD)等, 对T91试样腐蚀后的形貌、结构、元素含量和腐蚀产物的组成进行了分析。结果表明,T91的腐蚀对KCl蒸汽和反应温度比较敏感, 随着温度的增高, 腐蚀速率增加, 腐蚀动力学曲线基本符合抛物线规律; T91的主要腐蚀产物为Fe2O3和(Fe0.6Cr0.4)2O3, 同时含有少量的Fe3O4和K2Fe4O7。
标    签 T91   生物质电厂   过热器   碱金属氯化物   高温腐蚀   T91   biomass power plant   super-heater   alkali metal chloride   high-temperature corrosion  
 
Abstract
The corrosion behavior of T91 was studied by simulating the gas-side condition in super-heater of a biomass power plant. The corrosion kinetics curves were obtained through mass gain. By SEM, EDS and XRD, the appearance, microstructure, element contents and composition of corrosion products on the samples after corrosion were analyzed. The results showed that the corrosion of T91 was very sensitive to the gaseous-phase of KCl and the reaction temperature, as the reaction temperature increased, the corrosion-resistant behavior of T91 reduced and the corrosion kinetics of T91 steel was in line with parabolic law. The main components of the corrosion product were Fe2O3 and (Fe0.6Cr0.4)2O3, a small amount of Fe3O4 and K2Fe4O7.

中图分类号 TG172.8   DOI 10.11973/fsyfh-201511003

 
  中国光学期刊网论文下载说明


所属栏目 试验研究

基金项目 广东电网有限责任公司电力科学研究院项目(14430101000950)

收稿日期 2014/11/3

修改稿日期

网络出版日期

作者单位点击查看


备注李宇春(1972-), 教授, 博士, 从事电厂化学、材料腐蚀与防护等方面研究,

引用该论文: HE Yu-wu,LI Yu-chun,ZHANG Hong-liang,LI Mei,XU Zhao-jin,ZHONG Feng,YANG Fan. High Temperature Corrosion Behavior of T91 in Alkali Metal Chloride Medium[J]. Corrosion & Protection, 2015, 36(11): 1021


论文评价
共有人对该论文发表了看法,其中:
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
分享论文
分享到新浪微博 分享到腾讯微博 分享到人人网 分享到 Google Reader 分享到百度搜藏分享到Twitter

参考文献
【1】YUTAKA S M H N. Accelerated oxidiation of chromiun by trace of sodium chloride vapor[J]. Materials Transactions,1991,32(10):969-972.
 
【2】HARA M,NAKAGAWA T. Effect of trace amount of NaCl vapor on high-temperature oxidation of TiAl[J]. Oxidation of Metals,1999,52(1/2).
 
【3】MOTOI H,KYOU S,YOSHIRO K. Effect of preoxidation in oxygen containing a trace amount of NaCl vapor on the oxidation resis-tance of TiAl[J]. J Japan InstMetals,2000,64(12):1196-1205.
 
【4】MICHIO I,MOTOI H,TOKIKO N,et al. Effect of trace of NaCl vapor on high temperature oxidation of pure Ti and Ti-6% Al alloy[J]. Japan InstMetals,1997,61(6):511-518.
 
【5】MOTOI H,MICHIO I,TOKIKO N. Effect of trace NaCl vaporon high-temperature oxidation of Ti-6Al-4V alloy[J]. J Japan Inst-Metals,1998,62(8):691-700.
 
【6】孟庆若. P92钢埋弧焊焊接工艺[J]. 焊接技术,2008, 37(4):36-39.
 
【7】罗比雄. TP316L在生物质锅炉过热器气相条件下的腐蚀特性[J]. 热力发电,2011,40(3):34-38.
 
【8】李美栓. 金属的高温腐蚀[M]. 北京:冶金工业出版社, 2001.
 
【9】潘葱英. 垃圾焚烧炉内过热器区HCl高温腐蚀研究[D]. 杭州:浙江大学, 2007.
 
【10】胡荣祖, 史启祯. 热分析动力学[M]. 北京:科学出版社,2001.
 
【11】马海涛. 纯铁在含KCl蒸汽的O2气氛中的高温腐蚀行为[J]. 腐蚀科学与防护技术,2005,17(1):21-23.
 
【12】庞飞飞. 620 ℃条件下T/P92耐热钢的腐蚀行为[J]. 腐蚀与防护,2013,34(12):1086-1089.
 
【13】马海涛. 高温氯盐环境中金属材料的腐蚀[D]. 大连:大连理工大学, 2003.
 
【14】缪筱玲, 刘光明, 于斐,等. 超超临界锅炉用TP310HCbN不锈钢的热腐蚀行为研究[J]. 表面技术, 2012, 41(3):31-39.
 
相关信息
   标题 相关频次
 Al-6XN不锈钢在模拟烟气冷凝液中的耐蚀性
 6
 316L不锈钢在沉积盐碱混合物下的高温腐蚀
 2
 3种介质对T92钢高温腐蚀行为的影响
 2
 620 ℃条件下T/P92耐热钢的腐蚀行为
 2
 CR及DR射线检测技术在长输管道中的应用实效对比
 2
 ETA水工况下SO2-4对690合金腐蚀行为的影响
 2
 Fe/Cr涂层抗热腐蚀性能研究
 2
 LM231在管道爬行器电池电压控制中的应用
 2
 Mg-12Gd-3Y-0.5Zr镁合金的不同疲劳行为
 2
 PipeWizard管道环焊缝超声自动检测系统中时间门和波幅门的理解
 2
 不同速率变形后WE54合金的显微组织及力学性能
 2
 不锈钢1.4529的耐蚀性
 2
 不锈钢在NaCl溶液中点蚀的数值模拟
 2
 超临界水冷壁管材T23在弱碱性S2-溶液中的腐蚀行为
 2
 低压配电网的结构特点与理论线损计算
 2
 顶空-气相色谱法测定富马酸伊布利特原料药中5种溶剂残留量
 2
 镀锌钢在东莞大气及模拟大气中的腐蚀行为
 2
 防腐蚀菌与油田常用化学剂的配伍性评价及协同作用
 2
 废热锅炉系统蒸发器支撑板异常断裂的失效分析
 2
 高仿真X射线机假负载
 2
 高速电弧喷涂Fe-Cr-B-C-Al涂层的组织结构及其高温腐蚀行为
 2
 高效液相色谱-串联质谱法测定牛奶中3种糖肽类抗生素
 2
 高效液相色谱-串联质谱法同时测定染发剂中的1-萘酚和2-萘酚
 2
 管道对接环焊缝DR平板中心曝光法透照的图像变形问题
 2
 锅炉过热器管爆裂原因分析
 2
 核电站海水冷却系统的腐蚀与防腐蚀设计
 2
 核电站蒸汽发生器传热管与管板胀管段的涡流检测
 2
 环保无氰电刷镀银工艺及其实践应用
 2
 换热器传热管缺陷的涡流检测信号幅值与深度定量误差的关系
 2
 基于发动机台架的热电发电机的测试与评价
 2