12Cr1MoV钢在高温混合碱金属氯盐中的热腐蚀行为
          
Hot Corrosion Behavior of 12Cr1MoV Steel in High Temperature Mixed Alkali Chloride Salt

摘    要
采用腐蚀动力学分析法,研究了12Cr1MoV低合金钢在高温(600,700℃)70%NaCl-30%KCl、50%NaCl-50%KCl、30%NaCl-70%KCl(质量分数)混合盐中的热腐蚀行为,观察了表面及截面腐蚀形貌,分析了腐蚀产物成分并研究了其腐蚀机制。结果表明:12Cr1MoV钢在高温混合盐中会发生严重的表面与内部腐蚀,其内部产生的氯气是导致裂纹与孔洞等缺陷萌生和扩展的主要原因;随混合盐中KCl含量的增多和温度的升高,试样的腐蚀速率明显增大;较高含量的KCl使钢内部由沿晶腐蚀转变为整体性侵蚀。
标    签 12Cr1MoV钢   碱金属混合氯盐   热腐蚀   微观结构   12Cr1MoV steel   mixed alkali chloride salt   hot corrosion   microstructure  
 
Abstract
Hot corrosion behavior of 12Cr1MoV low alloy steel in mixed salts of 70%NaCl-30%KCl, 50%NaCl-50%KCl, 30%NaCl-70%KCl (mass fraction) at 600 ℃ and 700 ℃ was studied by the corrosion kinetic method, respectively. The corrosion morphology at the surface and cross section was observed, the composition of the corrosion products was analyzed and the corrosion mechanism was investigated. The results show that the 12Cr1MoV steel was corroded seriously at the surface and in the substrate in the high temperature mixed salts. The produced Cl2 inside the steel was the main reason for the initiation and propagation of defect structure such as cracks and pores. With the increase of KCl content in mixed salts and of the temperature, the corrosion rate of sample increased rapidly. The corrosion mode in the substrate changed from intergranular corrosion to integral corrosion due to the relatively high content of KCl.

中图分类号 TG178   DOI 10.11973/jxgccl201704013

 
  中国光学期刊网论文下载说明


所属栏目 材料性能及应用

基金项目 国家自然科学基金资助项目(51275058);湖南省高校创新平台开放基金资助项目(13k052);2015年湖南省研究生创新项目(CX2015B383)

收稿日期 2015/12/22

修改稿日期 2017/2/20

网络出版日期

作者单位点击查看

备注熊维舟(1992-),男,江西南昌人,硕士研究生.

引用该论文: XIONG Wei-zhou,HE Jian-jun,ZHANG Wei,REN Yan-jie. Hot Corrosion Behavior of 12Cr1MoV Steel in High Temperature Mixed Alkali Chloride Salt[J]. Materials for mechancial engineering, 2017, 41(4): 58~63
熊维舟,何建军,张炜,任延杰. 12Cr1MoV钢在高温混合碱金属氯盐中的热腐蚀行为[J]. 机械工程材料, 2017, 41(4): 58~63


论文评价
共有人对该论文发表了看法,其中:
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
分享论文
分享到新浪微博 分享到腾讯微博 分享到人人网 分享到 Google Reader 分享到百度搜藏分享到Twitter

参考文献
【1】LI Z Q, HAN J, LI W J, et al. Low cycle fatigue behavior of Cr-Mo-V low alloy steel used for railway brake discs [J]. Materials & Design, 2014, 56: 146-157.
 
【2】牛锐锋, 尚亮, 朱一乔, 等. 12Cr1MoVG钢焊接接头粗晶区的再热脆化行为 [J]. 机械工程材料, 2015, 39(6): 79-83.
 
【3】GRUBER T, SCHULZE K, SCHARLER R, et al. Investigation of the corrosion behavior of 13CrMo4-5 for biomass fired boilers with coupled online corrosion and deposit probe measurements [J]. Fuel, 2015, 144: 15-24.
 
【4】ANTUNES R A, DE-OLIVEIRA M C L. Corrosion in biomass combustion. A materials selection analysis and its interaction with corrosion mechanisms and mitigation strategies[J]. Corrosion Science, 2013, 76: 6-26.
 
【5】LIU S, LIU Z D, WANG Y T, et al. A comparative study on the high temperature corrosion of TP34H stainless steel, C22 alloy and laser-cladding C22 coating in molten chloride salts [J]. Corrosion Science, 2014, 83: 396-408.
 
【6】MOHANTY B P, SHORES D A. Role of chlorides in hot corrosion of a cast Fe-Cr-Ni alloy. Part I: Experimental studies [J]. Corrosion Science, 2004, 46(12): 2893-2907.
 
【7】TSAUR C C, ROCK J C, WANG C J, et al. The hot corrosion of 310 stainless steel with pre-coated NaCl/Na2SO4 mixtures at 750 ℃ [J]. Materials Chemistry and Physics, 2005, 89(2): 445-453.
 
【8】石照夏, 宋志刚, 郑文杰, 等. 镍铬钼合金在真空熔融CaCl2-20%CaF2盐中的腐蚀行为 [J]. 机械工程材料, 2010, 34(10): 9-13.
 
【9】YANG X G, LI S L, QI H Y. Effect of high-temperature hot corrosion on the low cycle fatigue behavior of a directionally solidified nickel-base superalloy [J]. International Journal of Fatigue, 2015, 70: 106-113.
 
【10】METSÄJOKI J, HUTTUNEN-SAARIVIRTA E, LEPISTÖ T. Elevated temperature corrosion of uncoated and aluminized 9-12% Cr boiler steels beneath KCl deposite [J]. Fuel, 2014, 133: 173-181.
 
【11】SURYANARAYANAN V, IYER K J L, RADHAKRISHNAN V M. Interaction of low temperature hot corrosion and creep [J]. Materials Science & Engineering A, 1989, 112: 107-116.
 
【12】刘广录, 周晓龙, 陈敬超. Ti3SiC2/SiC在Na3AlF6/Al2O3高温熔盐中的热腐蚀行为[J]. 材料保护, 2007, 40(12): 57-59.
 
相关信息
   标题 相关频次
 颗粒粒径对喷射沉积制备SiC颗粒增强铝硅合金复合材料显微组织及拉伸性能的影响
 5
 基于免疫算法的316L不锈钢高温低周疲劳寿命预测
 4
 12Cr1MoV钢过热器爆管的显微组织和力学性能
 3
 12Cr1MoV钢在碱金属硫氯盐中的腐蚀行为
 3
 15CrMo钢和12Cr1MoV钢的快速金相制样方法
 3
 高温运行后12Cr1MoV钢焊接接头的显微组织和力学性能
 3
 垃圾焚烧炉热管用12Cr1MoVG钢在不同碱金属混合熔盐中的热腐蚀行为
 3
 热处理工艺对12Cr1MoV钢显微组织和力学性能的影响
 3
 0.95K0.47Na0.47Li0.06NbO3-0.05BaxSr1-xTiO3无铅压电陶瓷的微观结构与性能
 2
 12Cr1MoV钢高温过热器管爆裂分析
 2
 12Cr1MoV珠光体耐热钢长期服役中碳化物的变化及对性能的影响
 2
 310S和AL-6XN不锈钢在熔融MgCl2中的腐蚀行为
 2
 Al2O3/TiC/Mo/Ni微纳陶瓷复合材料的微观结构与性能
 2
 Al-10%Cr合金的固液混合压铸工艺
 2
 AlFeCoNiCrTiVx系高熵合金的组织结构及电化学性能
 2
 CaCO3含量对自保护药芯焊丝脱渣性的影响
 2
 H13钢表面电火花沉积Deloro 50合金层的组织和性能
 2
 Na2O含量对金刚石砂轮用Na2O-SiO2-Al2O3-B2O3系陶瓷结合剂性能的影响
 2
 NiCrAlY涂层在模拟烟气中的热腐蚀行为
 2
 SiCp增强复合钎料薄膜活性钎焊SiC陶瓷接头的微观结构及力学性能
 2
 Y2O3掺杂对CaTiO3陶瓷烧结性能和微观结构的影响
 2
 箔片动压气体轴承系统中箔片表面涂层材料的测试表征
 2
 掺杂CuO的(1-x)Ca0.61Nd0.26TiO3+xNd(Mg1/2Ti1/2)O3复合陶瓷的微波介电性能
 2
 超声波对Ni-ZrO2纳米复合镀层微观结构和显微硬度的影响
 2
 超音速等离子喷涂WC-10Co4Cr涂层的力学性能及冲蚀磨损失效分析
 2
 超音速火焰喷涂Cr3C2-NiCr涂层的显微组织与磨损性能
 2
 导弹发动机的热波无损检测
 2
 等温时效模拟研究12Cr1MoV钢在长期高温服役过程中碳化物的转变规律
 2
 典型腐蚀损伤形态对结构材料性能的影响
 2
 电解液中Na2CO3/C6H12O6对AZ31镁合金阳极氧化膜结构与耐腐蚀性能的影响
 2