锡对Mg-5Zn-1Mn合金显微组织及拉伸性能的影响
          
Influence of Sn on Microstructure and Tensile Property of Mg-5Zn-1Mn Alloy

摘    要
对铸态Mg-5Zn-1Mn-xSn(x分别为0,0.3,0.6,0.9,质量分数/%)合金进行了330℃×24 h+400℃×2 h的均匀化处理,然后在应变速率为9.1 s-1条件下轧制成厚度为2 mm的合金板,研究了锡添加量对铸态和轧制态合金显微组织和拉伸性能的影响。结果表明:锡的添加可以细化试验合金的铸态及其均匀化处理后的显微组织,并形成高熔点Mg2Sn相,促进后续轧制过程中试验合金的动态再结晶并细化晶粒;经轧制后,试验合金的拉伸性能优于其铸态的,且随着锡含量的增加,轧制态合金的强度与塑性呈先上升后下降的变化趋势,其断裂形式从准解理断裂逐渐向延性断裂转变;Mg-5Zn-1Mn-0.6Sn合金的拉伸性能最佳,其抗拉强度和伸长率分别为337 MPa和21%。
标    签 Mg-Zn-Mn-Sn合金   动态再结晶   显微组织   拉伸性能   Mg-Zn-Mn-Sn alloy   dynamic recrystallization   microstructure   tensile property  
 
Abstract
The as-cast Mg-5Zn-Mn-xSn (x=0, 0.3, 0.6, 0.9, mass fraction/%) alloys were homogenized with process of 330℃×24 h+400℃×2 h, and then rolled into 2 mm thick alloy plates at the strain rate of 9.1 s-1. The influence of Sn addition on the microstructures and tensile properties of as-cast and as-rolled alloys was studied.The results show that the Sn addition can refine the microstructure of the as-cast alloys and homogenized alloys, leading to the formation of the Mg2Sn phase with high melting point, which can promote the dynamic recrystallization and refine the grain size during the subsequent rolling process. After rolling, the tensile property of the tested alloy was better than that of as-cast alloy. Meanwhile with the increase of Sn content, the strength and plasticity of as-rolled alloy first increased then decreased, and the fracture mode transformed from quasi-cleavage fracture to plastic fracture. The tensile property of Mg-5Zn-1Mn-0.6Sn alloy was the best with the tensile strength and elongation of 337 MPa and 21%, respectively.

中图分类号 TG146.2   DOI 10.11973/jxgccl201705001

 
  中国光学期刊网论文下载说明


所属栏目 试验研究

基金项目 国家自然科学基金资助项目(51471066);高等学校博士学科点专项科研基金资助项目(20120161110040);国家级创新计划项目

收稿日期 2016/3/13

修改稿日期 2017/3/8

网络出版日期

作者单位点击查看

备注佘庆元(1990-),男,湖南娄底人,硕士研究生.

引用该论文: SHE Qingyuan,YAN Hongge,CHEN Jihua,SU Bin,CHEN Chao,LU Mei,CAO Mengxin,YU Lang. Influence of Sn on Microstructure and Tensile Property of Mg-5Zn-1Mn Alloy[J]. Materials for mechancial engineering, 2017, 41(5): 1~6
佘庆元,严红革,陈吉华,苏斌,陈潮,陆梅,曹梦馨,余浪. 锡对Mg-5Zn-1Mn合金显微组织及拉伸性能的影响[J]. 机械工程材料, 2017, 41(5): 1~6


论文评价
共有人对该论文发表了看法,其中:
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
分享论文
分享到新浪微博 分享到腾讯微博 分享到人人网 分享到 Google Reader 分享到百度搜藏分享到Twitter

参考文献
【1】刘龙飞, 姜炳春, 赵俊,等. 冲击载荷下AZ31镁合金的变形行为和组织演变[J]. 机械工程材料, 2015, 39(1):24-28.
 
【2】郜瑞,温彤,季筱玮,等. 工艺参数对AZ31镁合金板拉深成形性能的影响[J]. 机械工程材料, 2013, 37(3):87-89.
 
【3】陈鼎,蒋琼,姜勇,等. 深冷处理对铸态ZK60镁合金显微组织和力学性能的影响[J]. 机械工程材料, 2011, 35(2):16-19.
 
【4】张丁非,齐福刚,石国梁,等. Mn含量对Mg-Zn-Mn变形镁合金显微组织和力学性能的影响[J]. 稀有金属材料与工程,2010,39(12):2205-2210.
 
【5】CHEN J H, CHEN Z H,YAN H G, et al. Effects of Sn addition on microstructure and mechanical properties of Mg-Zn-Al alloys[J]. Journal of Alloys & Compounds, 2008, 461(1/2):209-215.
 
【6】HOU X L, SUN X, WANG L M,et al. Effects of microstructure and texture on the mechanical properties of extruded Mg-Gd-Nd-Y-Zn alloy[J]. Advanced Materials Research, 2012, 509:68-74.
 
【7】QI F G, ZHANG D F, ZHANG X H,et al. Effect of Sn addition on the microstructure and mechanical properties of Mg-6Zn-1Mn alloy[J]. Journal of Alloys and Compounds, 2013, 585(3):656-666.
 
【8】ZHU S Q, YAN H G, CHEN J H, et al. Feasibility of high strain-rate rolling of a magnesium alloy across a wide temperature range[J]. Scripta Materialia, 2012, 67(4):404-407.
 
【9】ZHU S Q, YAN H G, CHEN J H,et al. Effect of twinning and dynamic recrystallization on the high strain rate rolling process[J]. Scripta Materialia, 2010, 63(10):985-988.
 
【10】WATANABE H, TSUTSUI H, MUKAI I,et al. Grain size control of commercial wrought Mg-Al-Zn alloys utilizing dynamic recrystallization[J]. Materials Transactions-JIM, 2001, 42(7):1200-1205.
 
【11】MUZYK M, PAKIELA Z, KURZYDLOWSKI K J. Generalized stacking fault energy in magnesium alloys:Density functional theory calculations[J]. Scripta Materialia, 2012, 66(5):219-222.
 
【12】ZHANG H Y, WANG H Y, WANG C,et al. First-principles calculations of generalized stacking fault energy in Mg alloys with Sn, Pb and Sn+Pb dopings[J]. Materials Science & Engineering A, 2013, 584:82-87.
 
【13】陈振华. 变形镁合金[M]. 北京:化学工业出版社,2005.
 
【14】BEER A G, BARNETT M R. Microstructural development during hot working of Mg3Al1Zn[J]. Metallurgical & Materials Transactions A, 2007, 38(8):1856-1867.
 
【15】PARK S H, YU H, BAE J H,et al. Microstructural evolution of indirect-extruded ZK60 alloy by adding Ce[J]. Journal of Alloys & Compounds, 2012, 545(51):139-143.
 
相关信息
   标题 相关频次
 轧制工艺参数对ZK60镁合金组织和拉伸性能的影响
 12
 Fe-17Mn-8Cr合金在多向锻造过程中显微组织与性能的变化
 8
 真空感应熔炼水冷铜模铸造对2024铝合金形变热处理组织及性能的影响
 6
 12Cr1MoV钢管在长时服役后组织及拉伸性能的退化
 4
 3mm厚6061铝合金板固定双轴肩搅拌摩擦焊接头的显微组织与拉伸性能
 4
 5A06铝合金超薄板交流冷金属过渡焊接头的组织与拉伸性能
 4
 6061铝合金热轧厚板的形变硬化特性
 4
 6061铝合金在多向锻造过程中显微组织与拉伸性能的演变
 4
 AZ61镁合金的热压缩变形行为及组织演变
 4
 G20Mn5铸钢MAG焊接接头的组织与力学性能
 4
 MnO含量对SJ612焊剂焊接18-8不锈钢接头组织和性能的影响
 4
 NaCl-KCl基排杂熔剂对A356铝合金熔体的净化及净化后的组织和性能
 4
 SiC粒径对SiCp/2024铝合金复合材料显微组织和力学性能的影响
 4
 T23、T91、TP347H钢管长时服役后的显微组织和拉伸性能
 4
 WE43镁合金的热变形行为及热加工图
 4
 不同变形量下20CrNi2Mo钢的热压缩变形行为
 4
 不同固化压力下制备碳纤维增强铝层板的拉伸性能
 4
 不同焊接速度下ZK60镁合金自持式搅拌摩擦焊接头的显微组织
 4
 不同显微组织套管钻井用钢的拉伸性能与疲劳裂纹扩展性能
 4
 不同应变速率下D1车轮钢的拉伸性能与断口形貌
 4
 不同状态Mg-9Li-3Al-2.0Gd合金的显微组织及性能
 4
 充型压力对石膏型反重力铸造ZM5镁合金组织和拉伸性能的影响
 4
 淬火冷却速率对Zr-4合金显微组织和耐腐蚀性能的影响
 4
 大变形轧制制备超细晶镍基合金的显微组织与拉伸性能
 4
 电弧轨迹对CMT电弧增材制造Inconel 625合金厚壁件组织与性能的影响
 4
 电子束选区熔化成形Ti-6Al-4V合金不同沉积高度上的组织与性能
 4
 复合添加稀土钕和铒的AZ91D镁合金显微组织与拉伸性能
 4
 钙对Mg-6Al变形镁合金显微组织和拉伸性能的影响
 4
 高铁螺纹道钉用TD16钢的动态再结晶行为
 4
 固溶时效工艺参数对TA19钛合金显微组织与拉伸性能的影响
 4