Fe-17Mn-8Cr合金在多向锻造过程中显微组织与性能的变化
          
Microstructure and Property Changes of Fe-17Mn-8Cr Alloy during Multi-directional Forging Process

摘    要
采用拉伸试验机和动态机械热分析仪等仪器测试了Fe-17Mn-8Cr合金在多向锻造过程中显微组织、力学性能和阻尼性能等的变化。结果表明:随着多向锻造过程的进行,ε马氏体和γ奥氏体片明显细化,分布更加均匀;合金中的位错密度急剧增大,屈服强度显著提高;多向锻造态合金的阻尼对数衰减率有所下降,但仍具有较高的阻尼性能,其阻尼机制主要是ε马氏体变体交叉程度对γ/ε界面移动以及高密度位错对层错运动的相互作用。
标    签 Fe-17Mn-8Cr合金   多向锻造   力学性能   阻尼性能   显微组织   Fe-17Mn-8Cr alloy   multi-directional forging   mechanical property   damping capacity   microstructure  
 
Abstract
The changes of microstructure, mechanical and damping properties of Fe-17Mn-8Cr alloy during multi-directional forging process were investigated by tensile testing and dynamic thermal mechanical analyzer. The results show that during multi-directional forging process the ε-martensite and γ-austenite plates were greatly refined and more uniformly distributed. Meanwhile, a high density of dislocations was introduced and yield strength was improved obviously. The logarithmic decrement of Fe-17Mn-8Cr alloy after multi-directional forging declined but the alloy still had a high damping capacity. The damping mechanism of this alloy was interaction between the effect of variant crossing degree of ε-martensite on γ/ε interface movement and the effect of high density of dislocations on stacking fault movement.

中图分类号 TG135.7   DOI 10.11973/jxgccl201707004

 
  中国光学期刊网论文下载说明


所属栏目 试验研究

基金项目

收稿日期 2016/1/27

修改稿日期 2017/3/23

网络出版日期

作者单位点击查看

备注冉敏(1989-),男,四川南充人,硕士研究生

引用该论文: RAN Min,YAN Hongge,CHENG Xiangfei,CHEN Jihua,SU Bin,XIA Weijun,ZHANG Ming. Microstructure and Property Changes of Fe-17Mn-8Cr Alloy during Multi-directional Forging Process[J]. Materials for mechancial engineering, 2017, 41(7): 18~23
冉敏,严红革,程相飞,陈吉华,苏斌,夏伟军,张明. Fe-17Mn-8Cr合金在多向锻造过程中显微组织与性能的变化[J]. 机械工程材料, 2017, 41(7): 18~23


论文评价
共有人对该论文发表了看法,其中:
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
分享论文
分享到新浪微博 分享到腾讯微博 分享到人人网 分享到 Google Reader 分享到百度搜藏分享到Twitter

参考文献
【1】BAIK S H. High damping Fe-Mn martensitic alloys for engineering applications[J]. Nuclear Engineering and Design, 2000, 198(3):241-252.
 
【2】GIRISH B M, SATISH B M, MAHESH K. Effect of stacking fault probability and ε martensite on damping capacity of Fe-16%Mn alloy[J]. Materials and Design, 2010, 31(4):2163-2166.
 
【3】HUANG S K, WEN Y H, LI N, et al. Application of damping mechanism model and stacking fault probability in Fe-Mn alloy[J]. Materials Characterization, 2008, 59(6):681-687.
 
【4】KIM J C, HAN D W, BAIK S H, et al. Effects of alloying elements on martensitic transformation behavior and damping capacity in Fe-17Mn alloy[J]. Materials Science and Engineering A, 2004, 378(1):323-327.
 
【5】黎为, 李宁, 腾劲, 等. 时效温度对Fe-19Mn合金阻尼性能的影响[J]. 金属热处理, 2010, 35(12):67-70.
 
【6】于学勇, 李宁, 胥永刚, 等. 固溶处理温度对Fe-14Mn-0.22 C减振合金阻尼性能的影响[J]. 四川大学学报(工程科学版), 2003, 35(5):84-87.
 
【7】黄姝珂, 刘建辉, 李昌安, 等. 预变形对Fe-Mn合金层错几率和阻尼性能的影响[J]. 金属学报, 2009, 45(8):937-942.
 
【8】SONG C, XIA W, ZHANG J, et al. Microstructure and mechanical properties of Fe-Mn based alloys after sub-rapid solidification[J]. Materials and Design, 2013, 51(5):262-267.
 
【9】于学勇. Fe-Mn系高阻尼合金阻尼性能的研究[D]. 成都:四川大学, 2004.
 
【10】郭强,严红革, 陈振华, 等. 多向锻造技术研究进展[J]. 材料导报, 2007, 21(2):106-108.
 
【11】屈啸, 许晓嫦, 陈振湘, 等. 多向压缩变形对时效态铝铜合金组织和硬度的影响[J]. 机械工程材料, 2011, 35(3):64-75.
 
【12】JUN J H, KONG D K, CHOI C S. The influence of Co on damping capacity of Fe-Mn-Co alloys[J]. Materials Research Bulletin, 1998, 33(10):1419-1425.
 
【13】KIM G-H, NISHIMURA Y, WATANABE Y, et al. Effects of ε-martensite and dislocations behavior by thermo-mechanical treatment on Fe-Cr-Mn damping alloy[J]. Materials Science and Engineering A, 2009, 521:368-371.
 
【14】LÜCKE K. Thermally assisted unpinning of a dislocation double loop[J]. Journal of Applied Physics, 1968, 39(11):5181-5191.
 
【15】田铁, 毛星子, 米林. 镁及镁合金阻尼机理的研究现状[J]. 机械工程材料, 2011, 35(6):1-3.
 
【16】OKADA H, SAHASHI H, KIM I-S, et al. Effect of epsilon martensite on the damping of high strength Fe-Cr-Mn alloys[J]. Materials Science and Engineering A, 2004, 370(1/2):519-523.
 
【17】WEN Y, XIAO H, PENG H, et al. Relationship between damping capacity and variations of vacancies concentration and segregation of carbon atom in an Fe-Mn alloy[J]. Metallurgical and Materials Transactions A, 2015, 46(11):4828-4833.
 
【18】LEE Y K, BAIK S H, KIM J C, et al. Effects of amount of ε martensite, carbon content and cold working on damping capacity of an Fe-17% Mn martensitic alloy[J]. Journal of Alloys and Compounds, 2003, 355(1/2):10-16.
 
【19】BLIZNUK V V, GLAVATSKA N I, SÖDERBERG O, et al. Effect of nitrogen on damping, mechanical and corrosive properties of Fe-Mn alloys[J]. Materials Science and Engineering A, 2002, 338(1):213-218.
 
相关信息
   标题 相关频次
 轧制工艺参数对ZK60镁合金组织和拉伸性能的影响
 10
 锡对Mg-5Zn-1Mn合金显微组织及拉伸性能的影响
 8
 焊丝药粉中镍铬质量比对双相不锈钢焊缝显微组织与力学性能的影响
 6
 喷射沉积SiCp/Al-20Si-4.5Cu梯度复合材料的优化热处理工艺
 6
 轧制温度对大应变轧制AZ61镁合金板材组织与力学性能的影响
 6
 真空感应熔炼水冷铜模铸造对2024铝合金形变热处理组织及性能的影响
 6
 等径角轧制AM60镁合金板材的显微组织与力学性能
 5
 快速凝固结合粉末冶金法制备SiCp/AZ91复合材料的组织及性能
 5
 06Cr19Ni10不锈钢/A283低碳钢扩散焊接接头的显微组织和力学性能
 4
 06Cr20Ni11钢埋弧焊焊缝的显微组织和性能
 4
 10Ni5CrMoV钢MAG焊接接头的显微组织与力学性能
 4
 12Cr13钢预热处理工艺参数优化
 4
 12Cr1MoV钢过热器爆管的显微组织和力学性能
 4
 16Mo3钢大直径大变形量试制中频弯管的组织与性能
 4
 2024铝合金电子束焊接接头的显微组织与力学性能
 4
 240 MPa级高强IF钢的冷轧压下率和退火温度
 4
 300 MW机组锁口叶片断裂原因分析
 4
 3003铝合金无缝管制备过程中的显微组织与力学性能变化
 4
 3D打印18Ni300模具钢的显微组织及力学性能
 4
 3mm厚6061铝合金板固定双轴肩搅拌摩擦焊接头的显微组织与拉伸性能
 4
 5 mm厚6005A-T6铝合金双轴肩搅拌摩擦焊接头的组织及性能
 4
 5 mm厚6082-T6铝合金双轴肩搅拌摩擦焊接头的组织与性能
 4
 550 MPa级高强度高延性汽车方管用钢的显微组织与力学性能
 4
 600 MPa级热轧双相钢的动态连续冷却转变行为及其热轧卷取工艺的优化
 4
 600 MW机组次末级叶片断裂原因分析
 4
 6061-T6铝合金搅拌摩擦焊接头的组织和性能
 4
 6061铝合金激光填丝焊接接头的组织与力学性能
 4
 6061铝合金在多向锻造过程中显微组织与拉伸性能的演变
 4
 6082-T6铝合金搅拌摩擦焊接头的显微组织与力学性能
 4
 7075/6009铝合金层状复合板材的固溶时效热处理工艺
 4