几种耐热钢在超(超)临界水中抗氧化性能的比较
Comparison of Oxidation Resistance of Several Heat Resistant Steels in Supercritical Water
摘 要
采用电化学阻抗试验、氧化增重法分析了Super304H、P92、15CrMo钢在554, 645 ℃及24 MPa超(超)临界水中氧化44 h后的电化学性能和抗氧化性能, 并用SEM和XRD对氧化膜的表面形貌及物相组成进行了分析。结果表明: Super304H 钢氧化后没有明显的质量变化, P92钢和15CrMo钢有氧化增重现象, 但氧化增重的差异不明显; Super304H钢表面由细小的针状或颗粒状的含铁和铬的氧化物组成, P92钢和15CrMo钢表面为相对较大的颗粒状Fe3O4组成; 554 ℃超临界水氧化后在NaCl溶液中的阻抗由小至大顺序为P92、Super304H、15CrMo钢, 随温度升高阻抗增大; 电化学阻抗可在短时氧化条件下有效分析耐热钢的抗氧化特性。
超临界水
氧化
电化学阻抗
heat resistant steel
supercritical water
oxidation
electrochemical impedance spectra
Abstract
The electrochemical property and oxidation resistance of Super304H, P92 and 15CrMo steels after being oxidized in supercritical water at temperature of 554, 645 ℃ and pressure of 24 MPa for 44 h were studied by electrochemistry impedance spectra (EIS) and weight increment test. The surface morphology and phase analysis of oxide films were examined by SEM and XRD. The results show that the mass of Super304H steel had no obvious change. The mass increment of P92 steel and 15CrMo steel was evident after oxidation, but there was no obvious difference between them. Surface product on Super304H was composed of tiny acicular or granular oxides containing Fe and Cr elements, while the oxide scales on P92 steel and 15CrMo steel were composed of Fe3O4 particles. The impedance sequence of the samples in NaCl solution after oxidation in supercritical water at 554 ℃ was P92
中图分类号 TG142.71 TG171
所属栏目 材料性能及其应用
基金项目 国家自然科学基金—神华集团煤炭联合基金资助项目(51134013); 国家自然科学基金资助项目(51171037)
收稿日期 2013/3/27
修改稿日期 2014/2/10
网络出版日期
作者单位点击查看
备注程从前(1982—), 男, 重庆人, 讲师, 博士。
引用该论文: CHENG Cong-qian,LIU Yi-xuan,ZHAO Jie. Comparison of Oxidation Resistance of Several Heat Resistant Steels in Supercritical Water[J]. Materials for mechancial engineering, 2014, 38(4): 55～58
程从前,刘宜萱,赵杰. 几种耐热钢在超(超)临界水中抗氧化性能的比较[J]. 机械工程材料, 2014, 38(4): 55～58
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】黄兴德,周新雅,游喆, 等.超( 超) 临界锅炉高温受热面蒸汽氧化皮的生长与剥落特性［J］.动力工程,2009,29(6):602-608.
【2】纪世东, 周荣灿, 王生鹏, 等.700 ℃等级先进超超临界发电技术研发现状及国产化建议［J］.热力发电,2011,40(7):86-88.
【3】唐丽英,贾建民 蔡晖,等.超超临界机组HR3C不锈钢蒸汽侧氧化层的微观结构和生长机理［J］.腐蚀与防护,2011,32(10):775-778.
【4】CHEN Y, SRIDHARAN K, ALLEN T. Corrosion behavior of ferritic-martensitic steel T91 in supercritical water［J］.Corros Sci,2006,48:2843-2854.
【5】尹开锯,邱绍宇,唐睿,等.P92 钢在超临界水中的腐蚀行为［J］.腐蚀与防护,2010,31(5):334-410.
【6】BETOVA I, BOJINOV M, KINNUNEN P, et al. In situ characterisation of the oxidation of Ni in ultrasupercritical water［J］.Electrochem Commun,2006,8:311-316.
【7】FULGER M, MIHALACHE M, OHAI D, et al. Analyses of oxide films grown on AISI 304L stainless steel and Incoloy 800HT exposed to supercritical water environment［J］.J Nucl Mater,2011,415:147-157.
【8】乔岩欣,任爱,刘飞华,等.奥氏体不锈钢AL-6XN在超临界水中的腐蚀行为［J］.腐蚀与防护,2012,33(11):960-963.
【9】SUN M C, WU X Q, HAN E H, et al. Microstructure characteristics of oxide scales grown on stainless steel exposed to supercritical water ［J］.Script Mater,2009,61:996-999.
【10】林富生,王治政,王宝忠,等.中国电站用耐热钢及合金的研制、应用与发展［J］.动力工程学报,2010,30(4):235-244.
【11】TAN L, REN X, ALLEN T R. Corrosion behavior of 9-12% Cr ferritic-martensitic steels in supercritical water［J］.Corros Sci, 2010,52:1520-1528.
【2】纪世东, 周荣灿, 王生鹏, 等.700 ℃等级先进超超临界发电技术研发现状及国产化建议［J］.热力发电,2011,40(7):86-88.
【3】唐丽英,贾建民 蔡晖,等.超超临界机组HR3C不锈钢蒸汽侧氧化层的微观结构和生长机理［J］.腐蚀与防护,2011,32(10):775-778.
【4】CHEN Y, SRIDHARAN K, ALLEN T. Corrosion behavior of ferritic-martensitic steel T91 in supercritical water［J］.Corros Sci,2006,48:2843-2854.
【5】尹开锯,邱绍宇,唐睿,等.P92 钢在超临界水中的腐蚀行为［J］.腐蚀与防护,2010,31(5):334-410.
【6】BETOVA I, BOJINOV M, KINNUNEN P, et al. In situ characterisation of the oxidation of Ni in ultrasupercritical water［J］.Electrochem Commun,2006,8:311-316.
【7】FULGER M, MIHALACHE M, OHAI D, et al. Analyses of oxide films grown on AISI 304L stainless steel and Incoloy 800HT exposed to supercritical water environment［J］.J Nucl Mater,2011,415:147-157.
【8】乔岩欣,任爱,刘飞华,等.奥氏体不锈钢AL-6XN在超临界水中的腐蚀行为［J］.腐蚀与防护,2012,33(11):960-963.
【9】SUN M C, WU X Q, HAN E H, et al. Microstructure characteristics of oxide scales grown on stainless steel exposed to supercritical water ［J］.Script Mater,2009,61:996-999.
【10】林富生,王治政,王宝忠,等.中国电站用耐热钢及合金的研制、应用与发展［J］.动力工程学报,2010,30(4):235-244.
【11】TAN L, REN X, ALLEN T R. Corrosion behavior of 9-12% Cr ferritic-martensitic steels in supercritical water［J］.Corros Sci, 2010,52:1520-1528.
相关信息