库尔勒土壤中阴离子对X80管线钢腐蚀行为的影响
Effect of Anions in Korla Soil on Corrosion Behavior of X80 Pipeline Steel
摘 要
采用浸泡、极化曲线和电化学阻抗谱等方法研究了库尔勒土壤模拟溶液中HCO3-, Cl-及SO42-等阴离子对X80钢腐蚀行为的影响。结果表明, 在HCO3-溶液中分别加入Cl-, SO42-后, X80钢的腐蚀速率明显增大, 且Cl-比SO42-对X80钢腐蚀速率的促进作用更强; 在HCO3-溶液中同时加入Cl-和SO42-后, 两种离子对腐蚀速率的促进作用大于Cl-或SO42-单独时的作用, 但低于两者单独添加时促进作用的加和。
库尔勒土壤
阴离子
腐蚀
X80 steel
Korla soil
anion
corrosion
Abstract
Effects of anions in Korla soil simulated solution on corrosion behaviors of X80 pipeline steel were investigated using immersion test, polarization curves and electrochemical impedance spectroscopy. The results showed that Cl- and SO42- added respectively in HCO3- solution increased the corrosion rate of X80 steel. Moreover, the role of Cl- in promoting corrosion rate was more obvious than that of SO42-. When Cl- and SO42- were added togther into HCO3- solution, the corrosion rate of X80 steel was bigger than that when Cl- or SO42- was added respectively, but the promoting effect of both ions on corrosion rate was lower than the sum value of Cl- and SO42-.
中图分类号 TG174.2
所属栏目 试验研究
基金项目 辽宁省教育厅2012年科学研究一般项目(L2012127); 辽宁石油化工大学2011年度教育教学改革研究项目(J2011068)
收稿日期 2013/3/17
修改稿日期
网络出版日期
作者单位点击查看
备注梁平(1974-), 副教授, 博士, 从事材料的腐蚀与防护研究,
引用该论文: ZHANG Shu-yan,LIANG Ping,HU Chuan-shun,QIN Hua. Effect of Anions in Korla Soil on Corrosion Behavior of X80 Pipeline Steel[J]. Corrosion & Protection, 2014, 35(1): 14
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】曹楚南. 中国材料的自然环境腐蚀[M]. 北京:化学工业出版社,2005.
【2】李晓刚,杜翠薇,董超芳,等. X70钢的腐蚀行为与试验研究[M]. 北京:科学出版社,2006.
【3】刘文霞,孙成. 土壤中阴离子对碳钢腐蚀的影响[J]. 石油化工与腐蚀防护,2006,23(5):12-15.
【4】廖家兴,蒋益明,吴玮巍,等. 含Cl-溶液中SO42-对316不锈钢临界点蚀温度的影响[J]. 金属学报,2006,42(11):1187-1190.
【5】梁平,杜翠薇,李晓刚. SO42-对X80管线钢在含Cl-的NaHCO3溶液中点蚀行为影响[J]. 腐蚀与防护,2010,31(5):362-364.
【6】LEE W J,PYUN S I. Effects of sulphate ion additives on the pitting corrosion of pure aluminium in 0.01 M NaCl solution[J]. Electrochimica Acta,2000,45(12):1901-1910.
【7】MOAYED M H,NEWMAN R C. Aggressive effects of pitting “inhibitors” on highly alloyed stainless steels[J]. Corrosion Science,1998,40(2/3):519-522.
【8】吴荫顺. 金属腐蚀研究方法[M]. 北京:冶金工业出版社,1993.
【9】曹楚南,张鉴清. 电化学阻抗谱导论[M]. 北京:科学出版社,2002.
【10】梁平,李晓刚,杜翠薇,等. 溶解氧对X80管线钢在NS4溶液中腐蚀行为的影响[J]. 腐蚀科学与防护技术,2009,21(1):20-23.
【11】安洋,徐强,吴子涛,等. 模拟循环冷却水中几种离子对碳钢腐蚀的影响[J]. 电镀与精饰,2011,33(4):35-39.
【12】LEE C T,QIN Z,ODZIEMKOWSKI M. The influence of groundwater anions on the impedance behavior of carbon steel corroding under anoxic conditions[J]. Electrochimica Acta,2006,51(8):1558-1568.
【13】张治国,吴明,陈旭. 侵蚀性阴离子对A3钢腐蚀电化学行为的影响[J]. 腐蚀与防护,2011,32(8):609-612.
【14】李素芳,陈宗璋,曹红明,等. 碳钢在黄土中的腐蚀研究[J]. 四川化工与腐蚀控制,2002,5(6):12-15.
【2】李晓刚,杜翠薇,董超芳,等. X70钢的腐蚀行为与试验研究[M]. 北京:科学出版社,2006.
【3】刘文霞,孙成. 土壤中阴离子对碳钢腐蚀的影响[J]. 石油化工与腐蚀防护,2006,23(5):12-15.
【4】廖家兴,蒋益明,吴玮巍,等. 含Cl-溶液中SO42-对316不锈钢临界点蚀温度的影响[J]. 金属学报,2006,42(11):1187-1190.
【5】梁平,杜翠薇,李晓刚. SO42-对X80管线钢在含Cl-的NaHCO3溶液中点蚀行为影响[J]. 腐蚀与防护,2010,31(5):362-364.
【6】LEE W J,PYUN S I. Effects of sulphate ion additives on the pitting corrosion of pure aluminium in 0.01 M NaCl solution[J]. Electrochimica Acta,2000,45(12):1901-1910.
【7】MOAYED M H,NEWMAN R C. Aggressive effects of pitting “inhibitors” on highly alloyed stainless steels[J]. Corrosion Science,1998,40(2/3):519-522.
【8】吴荫顺. 金属腐蚀研究方法[M]. 北京:冶金工业出版社,1993.
【9】曹楚南,张鉴清. 电化学阻抗谱导论[M]. 北京:科学出版社,2002.
【10】梁平,李晓刚,杜翠薇,等. 溶解氧对X80管线钢在NS4溶液中腐蚀行为的影响[J]. 腐蚀科学与防护技术,2009,21(1):20-23.
【11】安洋,徐强,吴子涛,等. 模拟循环冷却水中几种离子对碳钢腐蚀的影响[J]. 电镀与精饰,2011,33(4):35-39.
【12】LEE C T,QIN Z,ODZIEMKOWSKI M. The influence of groundwater anions on the impedance behavior of carbon steel corroding under anoxic conditions[J]. Electrochimica Acta,2006,51(8):1558-1568.
【13】张治国,吴明,陈旭. 侵蚀性阴离子对A3钢腐蚀电化学行为的影响[J]. 腐蚀与防护,2011,32(8):609-612.
【14】李素芳,陈宗璋,曹红明,等. 碳钢在黄土中的腐蚀研究[J]. 四川化工与腐蚀控制,2002,5(6):12-15.
相关信息