喷丸对800合金在高温碱性溶液中应力腐蚀开裂敏感性的影响
Effect of Surface Shot Peening on Stress Corrosion Cracking Properties of Alloy 800
摘 要
在315 ℃ 10%的NaOH溶液中采用恒应变法加载的C型环试样, 研究了喷丸工艺对国产800合金管材料应力腐蚀开裂(SCC)敏感性的影响。结果表明, 在腐蚀试验进行500 h后, 未喷丸以及喷丸覆盖率较低的试样管均出现了不同程度的应力腐蚀开裂。随着喷丸覆盖率的提高, 800合金的抗SCC能力明显增强。
喷丸
应力腐蚀开裂
alloy 800 tube
shot peening
stress corrosion cracking
Abstract
The effect of shot peening on stress corrosion cracking properties of alloy 800 was tested using C-ring specimens under constant loads in 10% NaOH solution at 315 ℃ for 500 h. The results show that specimens without shot peening and with lower peening coverages showed different levels of stress corrosion cracking. With the increase of shot peening coverage, the resistance to stress corrosion cracking increases obviously.
中图分类号 TG174
所属栏目 试验研究
基金项目
收稿日期 2013/3/19
修改稿日期
网络出版日期
作者单位点击查看
备注张乐福(1967-),副教授,博士,从事核电材料研究,
引用该论文: LI Ming-xing,ZHANG Le-fu,YANG Chen. Effect of Surface Shot Peening on Stress Corrosion Cracking Properties of Alloy 800[J]. Corrosion & Protection, 2014, 35(1): 40
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】HARROD D,GOLD R,JACKO R. Alloy optimization for PWR steam generator heat-transfer tubing[J]. Journal of the Minerals:Metals and Materials Society,2011,53(7): 14-17.
【2】李明星. 喷丸对800合金腐蚀性能的影响[J]. 腐蚀与防护, 2013,34(6): 495-498.
【3】唐辉,张乐福,孙华. 表面喷丸对800合金点蚀性能影响[J]. 腐蚀与防护, 2012,33(10): 859-855.
【4】HICKLING J. Electrochemical aspects of the stress corrosion cracking of Fe-Cr-Ni alloys in caustic solutions[J]. Corrosion Science,1980,20(2):269.
【5】BRIANT C L,TOOLE C S O,HALL E L. The effect of microstructure on thecorrosion and stress corrosion cracking of alloy 600 in acidic and neutral environments[J]. Corrosion,1986,42:15.
【6】黄春波, 吕战鹏, 杨武. 改性800合金碱性SCC机理研究[J]. 腐蚀与防护, 2003, 24(1): 1-5.
【7】朱小明, 黄红波, 林俊,等. 用XPS分析喷丸处理后800合金在强碱溶液中的腐蚀产物[J]. 中国腐蚀与防护学报, 2004, 24(4): 213-217.
【8】戈大钫, 郑经纮, 丁亚平, 等. 喷丸改善800合金传热管在高温苛性碱溶液中的应力腐蚀性能的研究[J]. 理化检验-物理分册,1996,32(5):34-36.
【2】李明星. 喷丸对800合金腐蚀性能的影响[J]. 腐蚀与防护, 2013,34(6): 495-498.
【3】唐辉,张乐福,孙华. 表面喷丸对800合金点蚀性能影响[J]. 腐蚀与防护, 2012,33(10): 859-855.
【4】HICKLING J. Electrochemical aspects of the stress corrosion cracking of Fe-Cr-Ni alloys in caustic solutions[J]. Corrosion Science,1980,20(2):269.
【5】BRIANT C L,TOOLE C S O,HALL E L. The effect of microstructure on thecorrosion and stress corrosion cracking of alloy 600 in acidic and neutral environments[J]. Corrosion,1986,42:15.
【6】黄春波, 吕战鹏, 杨武. 改性800合金碱性SCC机理研究[J]. 腐蚀与防护, 2003, 24(1): 1-5.
【7】朱小明, 黄红波, 林俊,等. 用XPS分析喷丸处理后800合金在强碱溶液中的腐蚀产物[J]. 中国腐蚀与防护学报, 2004, 24(4): 213-217.
【8】戈大钫, 郑经纮, 丁亚平, 等. 喷丸改善800合金传热管在高温苛性碱溶液中的应力腐蚀性能的研究[J]. 理化检验-物理分册,1996,32(5):34-36.
相关信息