海南省博物馆馆藏出水古铁炮腐蚀产物分析
Analysis of Corrosion Products on Underwater Iron Cannon Artifacts from Hainan Province Museum
摘 要
海南省博物馆馆藏了7门明清时期的铁炮, 这些铁炮曾长久沉没在海水中, 且由于各个时期冶铸技术的差异导致铁炮的腐蚀程度不一。保存修复这些腐蚀严重的出水古铁炮是个重要课题。采用X射线荧光仪(XRF)、X射线衍射仪(XRD)等分析了出水古铁炮腐蚀产物的成分和物相组成。结果表明, 铁炮腐蚀产物含有Fe3O4, α-FeOOH, β-FeOOH(或Fe8(O,OH)16Cl1.3)和γ-FeOOH, 其中γ-FeOOH对铁炮具有破坏作用, 属于有害锈, 必须除去。腐蚀产物的确定为中国海洋出水铁炮的下一步除锈、脱盐等保护处理提供依据。
铁炮
腐蚀产物
underwater artifact
iron cannon
corrosion product
Abstract
There are 7 iron cannons conserved in Hainan Province Museum, these iron cannons sunk in the sea for a long time. Different metal working technologies in various periods results in different levels of corrosion of iron cannons. To conserve and restore the underwater iron cannons is an important issue The composition and structure of the corrosion products from these iron cannons were analyzed using X-ray fluorescence (XRF) and X-ray diffraction (XRD). The results show that the rust includes Fe3O4,α-FeOOH,β-FeOOH or Fe8(O,OH)16Cl1.3 and γ-FeOOH. The harmful rust γ-FeOOH must be removed. All the information will be useful to guide the desalination after the surface rust is moved.
中图分类号 TG174
所属栏目 应用技术
基金项目 2011年国家重点文物保护专项经费(财教2011第39号; 琼财政2011第2000号)
收稿日期 2013/1/20
修改稿日期
网络出版日期
作者单位点击查看
备注包春磊(1979-),助理研究员,博士,从事化学与文物保护研究,
引用该论文: BAO Chun-lei,JIA Shi-jie,FU Yan,LIU Ai-hong. Analysis of Corrosion Products on Underwater Iron Cannon Artifacts from Hainan Province Museum[J]. Corrosion & Protection, 2014, 35(1): 83
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】包春磊. 华光礁Ⅰ号出水铁器文物的腐蚀与保护措施[J]. 腐蚀与防护, 2012,33(7):614-617.
【2】STAHL Kenny, NIELSEN Kurt, JIANG J Z,et al. On the akaganeite crystal structure,phase transformations and possible role in post-excavations corrosion of iron artifacts[J]. Corrosion Science,2003,45(11): 2563-2575.
【3】JOHNSON D L, WILSON B M, CARR J D,et al. Corrosion of steel shipwrecks in the marine environment[J]. Materials Selection & Design,2006,45:54-57.
【4】欧阳维真. 沉于海底的铁器文物腐蚀机理与脱氯技术的基础研究[D]. 北京:北京化工大学博士论文,2005: 2-9.
【5】田正昭,秋山隆保,等. 水中遗物保护研究之二——论碱性溶液对铁器进行脱盐处理的方法[J]. 文物保护与考古科学,1990,2:53-55.
【6】REFAIT P H,GNIN J M R. The mechanisms of oxidation of ferrous hydroxychloride β-Fe2(OH)3Cl in aqueous solution: the formation of akaganeite vs goethite[J]. Corrosion Science,1997,39:539-553.
【7】成小林,陈淑英, 潘路,等. 不同保存环境下铁质文物中氯含量的分析[J]. 中国历史文物,2010,5:25-31.
【2】STAHL Kenny, NIELSEN Kurt, JIANG J Z,et al. On the akaganeite crystal structure,phase transformations and possible role in post-excavations corrosion of iron artifacts[J]. Corrosion Science,2003,45(11): 2563-2575.
【3】JOHNSON D L, WILSON B M, CARR J D,et al. Corrosion of steel shipwrecks in the marine environment[J]. Materials Selection & Design,2006,45:54-57.
【4】欧阳维真. 沉于海底的铁器文物腐蚀机理与脱氯技术的基础研究[D]. 北京:北京化工大学博士论文,2005: 2-9.
【5】田正昭,秋山隆保,等. 水中遗物保护研究之二——论碱性溶液对铁器进行脱盐处理的方法[J]. 文物保护与考古科学,1990,2:53-55.
【6】REFAIT P H,GNIN J M R. The mechanisms of oxidation of ferrous hydroxychloride β-Fe2(OH)3Cl in aqueous solution: the formation of akaganeite vs goethite[J]. Corrosion Science,1997,39:539-553.
【7】成小林,陈淑英, 潘路,等. 不同保存环境下铁质文物中氯含量的分析[J]. 中国历史文物,2010,5:25-31.
相关信息