压水堆核电厂蒸汽发生器老化机理及其影响因素
Ageing Mechanisms and Influencing Factors of Steam Generator in PWR Nuclear Power Plants
摘 要
蒸汽发生器是核电厂重要的核安全设备，其管束是最易发生失效的部位。基于国外核电厂实际运行经验与试验研究结果，概述了蒸汽发生器主要老化机理及其影响因素，明确了老化机理、老化缺陷、老化起因间的相互关系。该成可果为我国制定相应的压水堆核电厂蒸汽发生器老化管理大纲、实施定期安全审查，进而开展系统的寿命管理起参考作用。
蒸汽发生器
自然循环式
老化机理
传热管
pressurized water reactor (PWR)
steam generator
recirculating
ageing mechanism
heat exchanger tube
Abstract
Steam generator is one of the major nuclear power plant components important to safety, and its tube bundle is also the weakest site susceptible to failures. Based on the previous worldwide operating histories and experimental research results, the ageing mechanisms and their influencing factors of steam generators are addressed, and the correlations among the ageing mechanisms, ageing defects and ageing causes are identified in this paper, which would have the reference value for the establishment of ageing management programs, implementation of periodic safety review (PSR) and the systematic life management of steam generators in pressurized water reactors in China.
中图分类号 TG172
所属栏目 专论
基金项目 大型先进压水堆核电重大专项支撑项目(2010ZX06004-018)
收稿日期 2013/11/30
修改稿日期
网络出版日期
作者单位点击查看
备注龚嶷(1984-)，工程师，博士，从事核电厂寿命管理，核电、火电、石化设备管材的腐蚀性能研究及其失效分析,
引用该论文: GONG Yi,XU Xue-lian. Ageing Mechanisms and Influencing Factors of Steam Generator in PWR Nuclear Power Plants[J]. Corrosion & Protection, 2014, 35(2): 163
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】杨振国. 核电装置换热器的失效分析及其解决对策[J]. 金属热处理,2007,32(S1):28-35.
【2】窦一康. 核电厂生命周期全过程的老化管理[J]. 金属热处理,2011,36(S1):10-14.
【3】丁亚平,徐雪莲. 压水堆核电厂长寿命化的腐蚀损伤问题[J]. 腐蚀与防护,2001,22(11):489-494.
【4】龚嶷. 石化、火电工业用换热管的腐蚀失效分析及其性能评价[D]. 上海: 复旦大学博士学位论文,2012.
【5】乔培鹏,张乐福,徐雪莲,等. 形变及热处理对国产690合金晶间腐蚀性能影响[J]. 腐蚀与防护,2010,31(5):331-334.
【6】丁训慎. 核电站蒸汽发生器传热管的腐蚀与防护[J]. 腐蚀与防护,2000,21(1):15-19.
【7】IAEA TECDOC-1668Assessment and management of ageing of major nuclear power plant components important to safety:steam generators[R]. Vienna,Austria:IAEA,2011.
【8】臧希年,申世飞. 核电厂系统及设备[M]. 北京:清华大学出版社,2003.
【9】EPRI TR-103824Steam generator reference book,vol.1[R]. Palo Alto,CA,USA:EPRI,1994.
【10】李成涛，李晓钢，程学群，等. 316L不锈钢、690合金在氢氧化钠溶液中的电化学性能[J]. 腐蚀与防护,2011,32(4):252-255.
【11】陈石富，秦鹤勇，张文云,等. 700 ℃超超临界锅炉用镍基合金管材的研究进展[J]. 机械工程材料,2012,36(11):1-4.
【12】杨文斗. 反应堆材料学[M]. 北京:原子能出版社,2000.
【13】孙汉虹. 第三代核电技术AP1000[M]. 北京:中国电力出版社,2010.
【14】张春明,宋琛修,侯伟,等. 田湾核电站1号机组蒸汽发生器传热管缺陷处理过程的核安全监督[J]. 核安全,2006,4(2):16-21.
【15】曾正明. 实用钢铁材料便查手册[M]. 北京:中国电力出版社,2005.
【16】CORIOU H,GRALL L,MAHIEU C,et al. Sensitivity to stress corrosion and intergranular attack of high nickel austenitic alloys[J]. Corrosion,1966,22(10):280-290.
【17】白新德. 材料腐蚀与控制[M]. 北京:清华大学出版社,2005.
【18】刘建章. 核结构材料[M]. 北京:化学工业出版社,2007.
【19】EPRI TR-1012987Steam generator integrity assessment guidelines[R]. Palo Alto,CA,USA:EPRI,2006.
【20】YANG Z G,GONG Y,YUAN J Z. Failure analysis of leakage on titanium tubes within heat exchangers in a nuclear power plant.Part I:Electrochemical corrosion[J]. Materials & Corrosion,2012,63(1):7-17.
【21】曹松彦,孙本达,黄万启,等. 乙醇胺的热稳定性试验及其在核电站二回路系统的应用[J]. 腐蚀与防护,2012,33(11):1019-1021.
【22】丁训慎. 核电站蒸汽发生器传热管的点腐蚀及其防护[J]. 腐蚀与防护,2007,28(7):364-366.
【23】唐辉,张乐福,孙华. 表面喷丸对800合金点蚀性能影响[J]. 腐蚀与防护,2012,33(10):853-856.
【2】窦一康. 核电厂生命周期全过程的老化管理[J]. 金属热处理,2011,36(S1):10-14.
【3】丁亚平,徐雪莲. 压水堆核电厂长寿命化的腐蚀损伤问题[J]. 腐蚀与防护,2001,22(11):489-494.
【4】龚嶷. 石化、火电工业用换热管的腐蚀失效分析及其性能评价[D]. 上海: 复旦大学博士学位论文,2012.
【5】乔培鹏,张乐福,徐雪莲,等. 形变及热处理对国产690合金晶间腐蚀性能影响[J]. 腐蚀与防护,2010,31(5):331-334.
【6】丁训慎. 核电站蒸汽发生器传热管的腐蚀与防护[J]. 腐蚀与防护,2000,21(1):15-19.
【7】IAEA TECDOC-1668Assessment and management of ageing of major nuclear power plant components important to safety:steam generators[R]. Vienna,Austria:IAEA,2011.
【8】臧希年,申世飞. 核电厂系统及设备[M]. 北京:清华大学出版社,2003.
【9】EPRI TR-103824Steam generator reference book,vol.1[R]. Palo Alto,CA,USA:EPRI,1994.
【10】李成涛，李晓钢，程学群，等. 316L不锈钢、690合金在氢氧化钠溶液中的电化学性能[J]. 腐蚀与防护,2011,32(4):252-255.
【11】陈石富，秦鹤勇，张文云,等. 700 ℃超超临界锅炉用镍基合金管材的研究进展[J]. 机械工程材料,2012,36(11):1-4.
【12】杨文斗. 反应堆材料学[M]. 北京:原子能出版社,2000.
【13】孙汉虹. 第三代核电技术AP1000[M]. 北京:中国电力出版社,2010.
【14】张春明,宋琛修,侯伟,等. 田湾核电站1号机组蒸汽发生器传热管缺陷处理过程的核安全监督[J]. 核安全,2006,4(2):16-21.
【15】曾正明. 实用钢铁材料便查手册[M]. 北京:中国电力出版社,2005.
【16】CORIOU H,GRALL L,MAHIEU C,et al. Sensitivity to stress corrosion and intergranular attack of high nickel austenitic alloys[J]. Corrosion,1966,22(10):280-290.
【17】白新德. 材料腐蚀与控制[M]. 北京:清华大学出版社,2005.
【18】刘建章. 核结构材料[M]. 北京:化学工业出版社,2007.
【19】EPRI TR-1012987Steam generator integrity assessment guidelines[R]. Palo Alto,CA,USA:EPRI,2006.
【20】YANG Z G,GONG Y,YUAN J Z. Failure analysis of leakage on titanium tubes within heat exchangers in a nuclear power plant.Part I:Electrochemical corrosion[J]. Materials & Corrosion,2012,63(1):7-17.
【21】曹松彦,孙本达,黄万启,等. 乙醇胺的热稳定性试验及其在核电站二回路系统的应用[J]. 腐蚀与防护,2012,33(11):1019-1021.
【22】丁训慎. 核电站蒸汽发生器传热管的点腐蚀及其防护[J]. 腐蚀与防护,2007,28(7):364-366.
【23】唐辉,张乐福,孙华. 表面喷丸对800合金点蚀性能影响[J]. 腐蚀与防护,2012,33(10):853-856.
相关信息