镀锌钢在模拟不同服役环境中的腐蚀行为
Corrosion Behavior of Galvanized Steel in Different Simulated Service Environments
摘 要
采用极化曲线法研究了输电杆塔锌镀层在模拟海洋环境、模拟工业环境以及模拟海洋工业环境中的初期腐蚀行为。结果表明, 在模拟海洋环境中, 锌镀层的腐蚀速率随着NaCl浓度的增加先增大后减小; 在模拟工业环境中, 锌镀层腐蚀速率随着NaHSO3浓度增加而逐渐增大; 在模拟海洋工业环境中, 锌镀层腐蚀速率随着NaCl和NaHSO3混合溶液浓度的增加而增大。
腐蚀速率
模拟海洋环境
模拟工业环境
模拟海洋工业环境
galvanized steel
corrosion rate
simulated marine environment
simulated industrial environment
simulated marine industrial environment
Abstract
The corrosion behaviors of galvanized steel in simulated marine, industrial and marine industrial environments were investigated by polarization curve measurements. The results show that in simulated marine environment, the corrosion rate of galvanized steel first increases and then decreases with the increase of Cl- ions concentration. In simulated industrial environment, as the concentration of HSO3- increases, the corrosion rate of galvanized steel increases. In simulated marine industrial environment, the corrosion rate increases with the increases of concentration of Cl- and HSO3-.
中图分类号 TG174.2
所属栏目 试验研究
基金项目 国家自然科学基金(51271110); 上海市教委科研创新重点资助项目(12ZZ170); 国家电网福建省电力公司科研资助项目(NC2012068)
收稿日期 2013/8/14
修改稿日期
网络出版日期
作者单位点击查看
备注张俊喜(1963-), 教授, 博士, 从事金属材料腐蚀相关研究,
引用该论文: TAN Tian,CHEN Tong,ZHANG Jun-xi,XING Yi-jun,HONG Yi-cheng. Corrosion Behavior of Galvanized Steel in Different Simulated Service Environments[J]. Corrosion & Protection, 2014, 35(4): 307
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】王凤平, 严川伟, 张学元. 石英晶体微天平研究Zn在薄液膜下的腐蚀动力学[J]. 物理化学学报, 2001, 17(4):319-323.
【2】安百刚, 张学元, 韩恩厚, 等. Zn在模拟酸雨溶液中及其液膜下的腐蚀[J]. 金属学报, 2004, 40(2):202-206.
【3】邱妮, 姚强, 苗玉龙, 等. 电力铁塔角钢镀锌层在NaCl介质中的腐蚀行为研究[J]. 表面技术, 2011, 40(5):5-8.
【4】Q/GDW 152-2006电力系统污区分级与外绝缘选择标准[S].
【5】BERNARD M C, HUGOT L A, PHILIPS N. Under paint corrosion of zinc coated steel sheet studied by in situ Raman spectroscopy[J]. Corros Sci, 1993, 35(5/8):13-20.
【6】原徐杰, 张俊喜, 季羡武, 等. 电力输电杆塔用镀锌钢在污染环境中的腐蚀行为研究[J]. 腐蚀科学与防护技术, 2013, 25(1):13-18.
【7】严川伟, 史志明, 林海潮, 等. Zn在SO2环境中大气腐蚀初期表面特性研究[J]. 腐蚀科学与防护技术, 2000, 12(3): 151-153.
【8】SVENSSON J E, JOHANSSON L G. The temperature dependence of the SO2 induced atmospheric corrosion of zinc, a laboratory study[J]. Corrosion Science, 1996, 38: 2221-2233.
【9】屈庆, 严川伟, 张蕾, 等. Zn初期大气腐蚀中NaCl和SO2的协同效应[J]. 中国有色金属学报, 2002, 12(6):1272-1276.
【10】MATTSSON E. The atmospheric corrosion properties of some common structural metals[J]. Mater Perform, 1982, 21:9-19.
【11】SVENSSON J E, JOHANNSSON L G. A laboratory study of the initial stages of the atmospheric corrosion of zinc in the presence of NaCl:influence of SO2 and NO2[J]. Corrosion Science, 1993, 34:721-740.
【2】安百刚, 张学元, 韩恩厚, 等. Zn在模拟酸雨溶液中及其液膜下的腐蚀[J]. 金属学报, 2004, 40(2):202-206.
【3】邱妮, 姚强, 苗玉龙, 等. 电力铁塔角钢镀锌层在NaCl介质中的腐蚀行为研究[J]. 表面技术, 2011, 40(5):5-8.
【4】Q/GDW 152-2006电力系统污区分级与外绝缘选择标准[S].
【5】BERNARD M C, HUGOT L A, PHILIPS N. Under paint corrosion of zinc coated steel sheet studied by in situ Raman spectroscopy[J]. Corros Sci, 1993, 35(5/8):13-20.
【6】原徐杰, 张俊喜, 季羡武, 等. 电力输电杆塔用镀锌钢在污染环境中的腐蚀行为研究[J]. 腐蚀科学与防护技术, 2013, 25(1):13-18.
【7】严川伟, 史志明, 林海潮, 等. Zn在SO2环境中大气腐蚀初期表面特性研究[J]. 腐蚀科学与防护技术, 2000, 12(3): 151-153.
【8】SVENSSON J E, JOHANSSON L G. The temperature dependence of the SO2 induced atmospheric corrosion of zinc, a laboratory study[J]. Corrosion Science, 1996, 38: 2221-2233.
【9】屈庆, 严川伟, 张蕾, 等. Zn初期大气腐蚀中NaCl和SO2的协同效应[J]. 中国有色金属学报, 2002, 12(6):1272-1276.
【10】MATTSSON E. The atmospheric corrosion properties of some common structural metals[J]. Mater Perform, 1982, 21:9-19.
【11】SVENSSON J E, JOHANNSSON L G. A laboratory study of the initial stages of the atmospheric corrosion of zinc in the presence of NaCl:influence of SO2 and NO2[J]. Corrosion Science, 1993, 34:721-740.
相关信息