某天然气井13Cr油管腐蚀原因
Corrosion Causes of Tubing in a Gas Well
摘 要
对某天然气井13Cr油管腐蚀进行了调查研究和全面检测, 掌握了不同井段油管腐蚀分布规律和油管接头腐蚀集中位置。取样对油管化学成分、腐蚀形貌和腐蚀产物等进行了试验分析, 结果表明, 油管腐蚀介质为CO2、Cl-和水等, 腐蚀位置集中分布的原因主要与接头结构形状及加工精度有关。依据失效分析结果采取预防措施后收到了很好效果。
特殊螺纹接头
13Cr不锈钢
腐蚀
tubing
special thread jointer
13Cr stainless steel
corrosion
Abstract
The corrosion of 13Cr tubing in a gas well was investigated and roundly inspected, and the tubing corrosion distribution status and corrosion concentration position of the tubing were obtained. It is considered that the tubing corrosion was due to CO2 , Cl- and water. Some measures for preventing tubing from corrosion were taken according to failure analysis results.
中图分类号 TG174
所属栏目 应用技术
基金项目
收稿日期 2013/6/19
修改稿日期
网络出版日期
作者单位点击查看
备注谢俊峰(1980-),工程师,硕士,从事石油专用管及装备腐蚀与防护工作,
引用该论文: XIE Jun-feng,SONG Wen-wen,CHANG Ze-liang,LV Shuan-lu,WEN Zhi-ming,WU Yun-cai,QIN You-de. Corrosion Causes of Tubing in a Gas Well[J]. Corrosion & Protection, 2014, 35(7): 754
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】吕拴录, 韩勇. 特殊螺纹接头油、套管使用及展望[J]. 石油工业技术监督,2003,3:1-4.
【2】何庆龙, 孟惠民, 俞宏英, 等. N80油套管钢CO2腐蚀的研究进展[J]. 中国腐蚀与防护学报,2007,27(3):186-192.
【3】茅春浦编著. 流体力学[M]. 上海:上海交通大学出版社,1995.
【4】POSTLETH W J,NESIC S. Erosion in disturbed liquid/particle pipe flow:effects of flow geometry and particle surface roughness[J]. Corrosion,1993,49(10):850-856.
【5】LEVY A V. Erosion-corrosion of metals[J]. Corrosion,1995,51(11):872-875.
【6】LU S L,ZHANG G Z,LU M X,et al. Analysis of N80 BTC downhole tubing corrosion[J]. Material Performance October 2004, 43(10): 35-38.
【7】赵国仙,严密林. 影响碳钢CO2腐蚀速率的研究[J]. 石油矿场机械, 2001,30:72-74.
【8】高林,吕拴录,李鹤林,等. 油、套管脱扣、挤毁和破裂失效分析[J]. 理化检验-物理分册, 2013,49(3): 177-181.
【9】刘建勋,吕拴录,高运宗,等. 塔里木油田非API油、套管失效分析及预防[J]. 理化检验-物理分册, 2013,49(6): 416-418.
【10】吕拴录,赵国仙,王新虎,等. 特殊螺纹接头油管腐蚀原因分析[J]. 腐蚀与防护, 2005,26(4):179-181.
【11】LU S L,XIANG J M,CHANG Z L,et al. Analysis of premium connection downhole tubing corrosion[J]. Material Performance, 2008, 47(5):66-69.
【12】刘会, 赵国仙, 韩勇, 等. Cl-对油套管用P110钢腐蚀速率的影响[J]. 石油矿场机械, 2008, 37(11): 44-48.
【13】YUAN P B,GUO S W,LU S L. Failure analysis of high-alloy oil well tubing coupling[J]. Material Performance,2010,49(8):68-71.
【14】林玉珍,杨德钧. 腐蚀和腐蚀控制原理[M]. 北京: 中国石化出版社,2007.
【15】张福祥,吕拴录,王振彪, 等. 某高压气井套压升高及特殊螺纹接头不锈钢油管腐蚀原因分析[J]. 中国特种设备安全, 2010,26(5): 65-68.
【16】吕拴录, 李元斌, 王振彪, 等. 某高压气井13Cr油管柱泄漏和腐蚀原因分析[J]. 腐蚀与防护, 2010, 31(11): 902-904.
【2】何庆龙, 孟惠民, 俞宏英, 等. N80油套管钢CO2腐蚀的研究进展[J]. 中国腐蚀与防护学报,2007,27(3):186-192.
【3】茅春浦编著. 流体力学[M]. 上海:上海交通大学出版社,1995.
【4】POSTLETH W J,NESIC S. Erosion in disturbed liquid/particle pipe flow:effects of flow geometry and particle surface roughness[J]. Corrosion,1993,49(10):850-856.
【5】LEVY A V. Erosion-corrosion of metals[J]. Corrosion,1995,51(11):872-875.
【6】LU S L,ZHANG G Z,LU M X,et al. Analysis of N80 BTC downhole tubing corrosion[J]. Material Performance October 2004, 43(10): 35-38.
【7】赵国仙,严密林. 影响碳钢CO2腐蚀速率的研究[J]. 石油矿场机械, 2001,30:72-74.
【8】高林,吕拴录,李鹤林,等. 油、套管脱扣、挤毁和破裂失效分析[J]. 理化检验-物理分册, 2013,49(3): 177-181.
【9】刘建勋,吕拴录,高运宗,等. 塔里木油田非API油、套管失效分析及预防[J]. 理化检验-物理分册, 2013,49(6): 416-418.
【10】吕拴录,赵国仙,王新虎,等. 特殊螺纹接头油管腐蚀原因分析[J]. 腐蚀与防护, 2005,26(4):179-181.
【11】LU S L,XIANG J M,CHANG Z L,et al. Analysis of premium connection downhole tubing corrosion[J]. Material Performance, 2008, 47(5):66-69.
【12】刘会, 赵国仙, 韩勇, 等. Cl-对油套管用P110钢腐蚀速率的影响[J]. 石油矿场机械, 2008, 37(11): 44-48.
【13】YUAN P B,GUO S W,LU S L. Failure analysis of high-alloy oil well tubing coupling[J]. Material Performance,2010,49(8):68-71.
【14】林玉珍,杨德钧. 腐蚀和腐蚀控制原理[M]. 北京: 中国石化出版社,2007.
【15】张福祥,吕拴录,王振彪, 等. 某高压气井套压升高及特殊螺纹接头不锈钢油管腐蚀原因分析[J]. 中国特种设备安全, 2010,26(5): 65-68.
【16】吕拴录, 李元斌, 王振彪, 等. 某高压气井13Cr油管柱泄漏和腐蚀原因分析[J]. 腐蚀与防护, 2010, 31(11): 902-904.
相关信息