掺杂纳米钛导静电涂层的耐蚀性能
Corrosion Resistance of Static Electricity Conductive Coating Doped with Nano Titanium
摘 要
采用电化学阻抗技术(EIS)研究了掺杂纳米钛导静电涂层在3.5% NaCl水溶液中的耐蚀性能。与参考涂层相比, 掺杂纳米钛涂层在短时期内具有更好的防腐蚀性能, 而且在腐蚀溶液中浸泡一段时间后阻抗值有明显回升现象。长时间试验后两种涂层耐蚀性能逐渐趋于相当, 都有稳定而良好的防腐蚀性能。
掺杂纳米钛涂层
导静电涂层
耐蚀性能
EIS
nano-titanium doped coating
static electricity conductive coating
corrosion resistance
Abstract
The corrosion resistance of static electricity conductive coating doped with nano-titanium powder in 3.5% NaCl solution was studied by electrochemical impedance spectroscopy (EIS). The coating doped with nano-titanium showed better corrosion resistance compared with the contrasted coating in a short time, and the impedance value of nano-titanium doped coating increased obviously when immersed in the corrosive solution for an extended time period. For longer periods of time,these two coatings tended to have the same impedance value, and both exhibited stable and good corrosion resistance.
中图分类号 TG174.46
所属栏目 试验研究
基金项目
收稿日期 2014/2/10
修改稿日期
网络出版日期
作者单位点击查看
备注赵景茂(1965-),教授,博士,从事材料腐蚀与防护研究工作,13911968706.
引用该论文: ZHA Xin-tang,ZHAO Jing-mao. Corrosion Resistance of Static Electricity Conductive Coating Doped with Nano Titanium[J]. Corrosion & Protection, 2014, 35(12): 1240
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】魏仁华. 油罐防腐涂料市场综述[J]. 涂料技术与文摘,2008,3(3): 14-15.
【2】潘莹,张三平,周建龙,等. 导静电涂料导静电性能与防腐蚀性能的关系[J]. 腐蚀与防护, 2009,30(3):190.
【3】童剑. 纳米浆料的制备及其在水性涂料中的应用[D]. 广州: 华南理工大学硕士学位论文, 2010.
【4】孔凡静. 利用EIS研究几种单涂层与复合涂层在不同条件下的腐蚀失效行为[D]. 北京: 北京化工大学硕士学位论文, 2012.
【5】掌继锋. 纳米钛改性聚合物的制备及其在防腐涂料中的应用[D]. 哈尔滨: 哈尔滨工业大学硕士学位论文, 2006.
【6】张鉴清, 曹楚南. 电化学阻导谱方法研究评价有机涂层[J]. 腐蚀与防护,1998, 19(3):101-102.
【2】潘莹,张三平,周建龙,等. 导静电涂料导静电性能与防腐蚀性能的关系[J]. 腐蚀与防护, 2009,30(3):190.
【3】童剑. 纳米浆料的制备及其在水性涂料中的应用[D]. 广州: 华南理工大学硕士学位论文, 2010.
【4】孔凡静. 利用EIS研究几种单涂层与复合涂层在不同条件下的腐蚀失效行为[D]. 北京: 北京化工大学硕士学位论文, 2012.
【5】掌继锋. 纳米钛改性聚合物的制备及其在防腐涂料中的应用[D]. 哈尔滨: 哈尔滨工业大学硕士学位论文, 2006.
【6】张鉴清, 曹楚南. 电化学阻导谱方法研究评价有机涂层[J]. 腐蚀与防护,1998, 19(3):101-102.
相关信息