正交法研究PE100管材料熔体强度测试的影响因素
Influencing Factors on Measurement of PE100 Melt Strength Researched by Orthogonal Method
摘 要
温度、挤出速率、拉伸长度、拉伸加速度、测试轮对间的距离对测试PE100管材专用树脂的熔体强度有一定的影响, 用正交试验考察了测试PE100管材专用树脂熔体强度时影响因子的显著性, 确定测试PE100熔体强度主要影响因素是温度, 次要影响因素是拉伸加速度, 而测量轮对间距对测试结果的波动影响仅次于温度, 最佳条件为A1(205 ℃), B1(0.1 mm/s), C3(102 mm), D3(24 mm/s2), E1(0.3 mm)。
PE100
熔体强度
正交法
影响因素
polyethylene
PE100
melt strength
orthogonal method
influencing factors
Abstract
Some factors affecting melt strength of PE100 tubing resin were analyzed such as temperature, extrusion rate, tensile length, tensile acceleration, distance of take-off-wheel pair. The significance of influencing factors on melt strength of PE100 tubing resin was studies by orthogonal experiment. The results showed that the main factors were the temperature and the distance in measuring wheel pair, the secondary cause was the tensile acceleration. The optimum conditions were A1(205 ℃), B1(0.1 mm/s), C3(102 mm), D3(24 mm/s2), E1(0.3 mm).
中图分类号 TQ320.6
所属栏目 试验技术与方法
基金项目
收稿日期 2013/3/18
修改稿日期
网络出版日期
作者单位点击查看
备注吴春霜(1970-), 女, 副高级工程师。
引用该论文: WU Chun-shuang,ZHANG Gui-mian,GUAN Li. Influencing Factors on Measurement of PE100 Melt Strength Researched by Orthogonal Method[J]. Physical Testing and Chemical Analysis part A:Physical Testing, 2014, 50(1): 34～37
吴春霜,张贵棉,关莉. 正交法研究PE100管材料熔体强度测试的影响因素[J]. 理化检验－物理分册, 2014, 50(1): 34～37
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】李行温.PE结构对聚合物熔体强度行为的影响[J].国外塑料, 1996(1): 40-43.
【2】占国荣, 周南桥, 彭响方.聚合物的熔体强度及其测试技术[J].中国塑料, 2003, 17(8): 79-82.
【3】鞠伟, 王雪梅.聚烯烃树脂结构对其熔体强度的影响[J].齐鲁石油化工, 2008, 36(1): 4-7.
【4】王雪梅, 贾秀丽, 刘文华.聚烯烃熔体强度测试方法及其影响因素[J].齐鲁石油化工, 2006, 34(4): 436-438.
【5】王红英, 胡徐腾, 李振宇, 等.高熔体强度聚丙烯的制备与表征[J].化学进展, 2007, 19(6): 932-958.
【2】占国荣, 周南桥, 彭响方.聚合物的熔体强度及其测试技术[J].中国塑料, 2003, 17(8): 79-82.
【3】鞠伟, 王雪梅.聚烯烃树脂结构对其熔体强度的影响[J].齐鲁石油化工, 2008, 36(1): 4-7.
【4】王雪梅, 贾秀丽, 刘文华.聚烯烃熔体强度测试方法及其影响因素[J].齐鲁石油化工, 2006, 34(4): 436-438.
【5】王红英, 胡徐腾, 李振宇, 等.高熔体强度聚丙烯的制备与表征[J].化学进展, 2007, 19(6): 932-958.
相关信息