电气化铁路接触网铜合金中锚线夹失效分析
Failure Analysis on Mid-anchor Clamp of Copper Alloy for Contact Wire in Electrification Railway Contact Net
摘 要
采用化学成分分析、金相检验、断口与能谱分析等方法, 对开裂的电气化铁路接触网零件——接触线中锚线夹进行了分析。结果表明: 该铜合金中锚线夹所含的杂质元素铋在晶界处的偏聚是导致其开裂的主要原因。
裂纹
杂质元素
晶界偏聚
mid-anchor clamp for contact wire
crack
impurity element
grain boundaries segregation
Abstract
The cracked mid-anchor clamp for contact wire in electrification railway contact net was analyzed by means of chemical composition analysis, metallographic examination, fracture and energy spectrum analysis. The results showed that the impurity element Bi segregation at grain boundaries of mid-anchor clamp of copper alloy was the major reason for cracking.
中图分类号 TG758
所属栏目 质量控制与失效分析
基金项目
收稿日期 2013/5/21
修改稿日期
网络出版日期
作者单位点击查看
备注师静蕊(1976-), 女, 工程师, 工学硕士。
引用该论文: SHI Jing-rui,YUAN Ze-xi. Failure Analysis on Mid-anchor Clamp of Copper Alloy for Contact Wire in Electrification Railway Contact Net[J]. Physical Testing and Chemical Analysis part A:Physical Testing, 2014, 50(1): 57～60
师静蕊,袁泽喜. 电气化铁路接触网铜合金中锚线夹失效分析[J]. 理化检验－物理分册, 2014, 50(1): 57～60
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】刘平, 任凤章, 贾淑果, 等.铜合金及其应用[M].北京: 化学工业出版社, 2007.
【2】丁惠麟,辛志华.实用铝、铜及其合金金相热处理和失效分析[M].北京: 机械工业出版社, 2007.
【3】麦克林D.金属中的晶粒间界[M].杨顺华, 译.北京:科学出版社,1965.
【4】吴成建,陈国良,强文江.金属材料学[M].北京:冶金工业出版社, 2005.
【5】陈国桢,肖柯则,姜不居.铸件缺陷和对策手册[M].北京:机械工业出版社, 1996.
【2】丁惠麟,辛志华.实用铝、铜及其合金金相热处理和失效分析[M].北京: 机械工业出版社, 2007.
【3】麦克林D.金属中的晶粒间界[M].杨顺华, 译.北京:科学出版社,1965.
【4】吴成建,陈国良,强文江.金属材料学[M].北京:冶金工业出版社, 2005.
【5】陈国桢,肖柯则,姜不居.铸件缺陷和对策手册[M].北京:机械工业出版社, 1996.
相关信息