Reason Analysis on Substandard Elongation after Fracture of U75V Rail Web of Flash Welding Joint
摘 要
采用化学成分分析、力学性能测试、金相检验和断口分析等方法, 分析了U75V钢轨闪光焊接头轨腰拉伸断后伸长率不合格的原因。结果表明: 钢轨接头和钢轨母材轨腰大量密集分布MnS夹杂物(评级达到3.0级), 长条状的MnS夹杂物经闪光焊顶锻后, 随金属流线偏转45°方向, 当与拉伸过程中的45°最大剪切应力平行时, 相当于MnS夹杂物受到横向拉伸剪切, 裂纹容易在夹杂物中开裂和扩展, 故断后伸长率很低。
Abstract
Using chemical composition analysis, mechanical properties testing, metallographic examination and fracture analysis to find out the reason of substandard elongation after fracture of U75V rail web of flash welding joint. The results showed that there were numerous dense inclusions (MnS ratings reached 3.0 grade) in rail joint and rail web, the long stripe of MnS inclusion after welding upsetting, was deflected with the metal flow, and the deflecting direction was 45°, when it was parallel to the tensile process of 45° maximum shear stress, that means was the MnS inclusion subjected to transverse tensile shear, the cracks was so easy dehisced and expanded in MnS inclusion, elongation properties was so low.
中图分类号 U213.4 TG407
所属栏目 质量控制与失效分析
基金项目
收稿日期 2013/2/25
修改稿日期
网络出版日期
作者单位点击查看
备注李大东(1963-),男, 教授级高级工程师。
引用该论文: LI Da-dong,GONG Li-jun,YU Teng-yi,LIU Jin-yan. Reason Analysis on Substandard Elongation after Fracture of U75V Rail Web of Flash Welding Joint[J]. Physical Testing and Chemical Analysis part A:Physical Testing, 2014, 50(1): 61~66
李大东,龚利军,余腾义,刘锦燕. U75钢轨闪光焊接头轨腰断后伸长率不合格原因分析[J]. 理化检验-物理分册, 2014, 50(1): 61~66
被引情况:
【1】韩晓乾,于辉,刘帅帅,张正伟, "U71Mn钢轨矫直断裂原因分析",理化检验-物理分册 51, 911-913(2015)
共有人对该论文发表了看法,其中:
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】杨满存.高频焊缝组织及缺陷分析[J].焊管, 1994, 17(4): 8-13.
【2】北京钢铁学院, 东北工学院.工程力学(中册) 第二分册[M].北京: 高等教育出版社, 1979: 221.
【2】北京钢铁学院, 东北工学院.工程力学(中册) 第二分册[M].北京: 高等教育出版社, 1979: 221.
相关信息