超级13Cr马氏体不锈钢油管表面缺陷原因分析
Cause Analysis on Surface Defects of Super 13Cr Martensite Stainless Steel Tubing
摘 要
通过宏观检验、化学成分分析、金相检验和力学性能测试等方法, 对超级13Cr马氏体不锈钢油管表面缺陷的形成原因进行了分析。结果表明: 油管表面缺陷为折叠裂纹和轧制沟槽, 其产生原因主要是工厂轧制工艺不当所致。针对该表面缺陷对油管使用寿命的影响、油管表面缺陷的修磨和检验标准等进行了探讨, 建议严格油管表面质量验收标准。
油管
折叠裂纹
轧制沟槽
应力腐蚀开裂
13Cr martensite stainless steel
tubing
fold crack
rolling groove
stress corrosion cracking
Abstract
By means of macroscopic examination, chemical composition analysis, metallographic examination, mechanical property testing and so on, the cause of surface defects on super 13Cr martensite stainless steel tubing was analyzed. The results showed that the surface defects on tubing were fold cracks and rolling grooves caused by improper rolling technology. It was suggested that the inspection standard of tubing should be more strict, based on the discussion about the effect of tubing surface defects to use life, the repair for tubing surface defects and the inspection standard.
中图分类号 TE973
所属栏目 质量控制与失效分析
基金项目
收稿日期 2012/7/6
修改稿日期
网络出版日期
作者单位点击查看
备注滕学清(1965-), 男,高级工程师, 学士。
引用该论文: TENG Xue-qing,LV Shuan-lu,ZHOU Li-zhi,JI Xiao-hong,RAO Wen-yi,LI Jin-feng,SHEN Zhao-xi,LI Lei,GENG Hai-long,YANG Shao-long. Cause Analysis on Surface Defects of Super 13Cr Martensite Stainless Steel Tubing[J]. Physical Testing and Chemical Analysis part A:Physical Testing, 2014, 50(1): 67～70
滕学清,吕拴录,周理志,季晓红,饶文艺,李金凤,申昭熙,李磊,耿海龙,杨绍龙. 超级13Cr马氏体不锈钢油管表面缺陷原因分析[J]. 理化检验－物理分册, 2014, 50(1): 67～70
被引情况:
【1】滕学清,吕拴录,冯春,周理志,彭建新,刘明球,饶文艺,耿海龙,李金凤,周威, "某井114.3 mm油管接箍破裂原因分析",理化检验－物理分册 50, 376-379(2014)
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】丁毅,历建爱,张国正,等.110钢级88.9 mm×6.45 mm超级13Cr钢油管刺穿失效分析[J].理化检验-物理分册,2011,47(10): 663-667.
【2】刘克斌, 周伟民.超级13Cr钢在含CO2的CaCl2完井液中应力腐蚀开裂行为[J].石油与天然气化工,2007, 36(3):222-226.
【3】吕拴录,韩勇,李金凤,等. 输气管道无缝管线管表面发纹检验和判定[J].钢管, 2010, 39(3): 48-51.
【4】吕拴录, 李元斌, 王振彪, 等.某高压气井13Cr油管柱泄漏和腐蚀原因分析[J].腐蚀与防护, 2010, 31(11): 902-904.
【5】LU Shuan-lu, HAN Yong, QIN Chang-yi, et al. Crack and fitness for service assessment of ERW crude oil pipeline[J].Engineering Failure Analysis,2005(3):565-571.
【6】YUAN Peng-bin, GUO Sheng-wu, LV Shuan-lu. Failure analysis of high-alloy oil well tubing coupling[J].Material Performance,2010,49(8):68-71.
【7】吕拴录, 骆发前, 周杰, 等.钻杆接头纵向裂纹原因分析[J].机械工程材料, 2006, 30(4): 95-97.
【8】吕拴录, 高林, 迟军, 等.石油钻柱减震器花健体外筒断裂原因分析[J].机械工程材料, 2008, 32(2): 71-73.
【2】刘克斌, 周伟民.超级13Cr钢在含CO2的CaCl2完井液中应力腐蚀开裂行为[J].石油与天然气化工,2007, 36(3):222-226.
【3】吕拴录,韩勇,李金凤,等. 输气管道无缝管线管表面发纹检验和判定[J].钢管, 2010, 39(3): 48-51.
【4】吕拴录, 李元斌, 王振彪, 等.某高压气井13Cr油管柱泄漏和腐蚀原因分析[J].腐蚀与防护, 2010, 31(11): 902-904.
【5】LU Shuan-lu, HAN Yong, QIN Chang-yi, et al. Crack and fitness for service assessment of ERW crude oil pipeline[J].Engineering Failure Analysis,2005(3):565-571.
【6】YUAN Peng-bin, GUO Sheng-wu, LV Shuan-lu. Failure analysis of high-alloy oil well tubing coupling[J].Material Performance,2010,49(8):68-71.
【7】吕拴录, 骆发前, 周杰, 等.钻杆接头纵向裂纹原因分析[J].机械工程材料, 2006, 30(4): 95-97.
【8】吕拴录, 高林, 迟军, 等.石油钻柱减震器花健体外筒断裂原因分析[J].机械工程材料, 2008, 32(2): 71-73.
相关信息