铸态双相不锈钢彩色金相异常组织分析
Analysis on Abnormal Structure in Color Metallography of As-cast Duplex Stainless Steel
摘 要
采用金相分析、扫描电镜及能谱分析、X射线衍射分析、透射电镜分析以及显微硬度测试等方法研究了铸态2507双相不锈钢中各相的形貌和特征。结果表明: 采用彩色金相侵蚀剂(1 g偏重亚硫酸钠+10 mL浓盐酸+50 mL水)侵蚀后, 彩色金相组织中的土黄色相为奥氏体相, 黄绿色相为铁素体相, 斑马纹状组织为(σ+γ2)共析组织。
彩色金相
异常组织
(σ+γ2)共析组织
as-cast duplex stainless steel
color metallography
abnormal structure
(σ+γ2) eutectid
Abstract
The phase morphology and characteristics of as-cast 2507 duplex stainless steel were studied by using optical microscopy, scanning electronic microscopy, energy spectroscopy, X-ray diffractometer, transmission electronic microscopy and micro-hardness tester. The results show that after erosion by the color metallographic erosion agent (1 g Na2S2O5 + 10 mL HCl + 50 mL H2O), the khaki phase of the steel was austenite phase, the yellow-green phase was ferrite phase, and the zebra grain structure was (σ+γ2) eutectid structure.
中图分类号 TG115.21
所属栏目 试验技术与方法
基金项目
收稿日期 2013/6/8
修改稿日期
网络出版日期
作者单位点击查看
备注郭海霞(1981-),女,工程师。
引用该论文: GUO Hai-xia,ZHANG Jin-min,XIA Shen-lin. Analysis on Abnormal Structure in Color Metallography of As-cast Duplex Stainless Steel[J]. Physical Testing and Chemical Analysis part A:Physical Testing, 2014, 50(4): 273～276
郭海霞,张金民,夏申琳. 铸态双相不锈钢彩色金相异常组织分析[J]. 理化检验－物理分册, 2014, 50(4): 273～276
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】吴玖. 双相不锈钢[M]. 北京: 冶金工艺出版社, 1999:31-34.
【2】李炯辉. 金属材料金相图谱[M]. 北京: 机械工艺出版社, 2006: 930-931.
【3】孟祥娟, 孟繁印, 宋文文, 等. 两种热处理工艺对2205双相不锈钢腐蚀行为的影响[J]. 腐蚀与防护,2012,32(7):25-28,32.
【4】郭海霞, 韩顺昌, 李雪峰, 等. 铁素体奥氏体型双相不锈钢的侵蚀方法[J]. 理化检验-物理分册, 2009, 45(11): 684-685.
【2】李炯辉. 金属材料金相图谱[M]. 北京: 机械工艺出版社, 2006: 930-931.
【3】孟祥娟, 孟繁印, 宋文文, 等. 两种热处理工艺对2205双相不锈钢腐蚀行为的影响[J]. 腐蚀与防护,2012,32(7):25-28,32.
【4】郭海霞, 韩顺昌, 李雪峰, 等. 铁素体奥氏体型双相不锈钢的侵蚀方法[J]. 理化检验-物理分册, 2009, 45(11): 684-685.
相关信息