发动机缸盖螺栓断裂原因分析
Analysis on Fracture Reason of Cylinder Blot in Motor
摘 要
某发动机缸盖螺栓在装配后发生断裂。通过宏观、微观检验以及化学成分分析、力学性能测试、氢脆试验等对断裂原因进行了分析。结果表明: 缸盖螺栓发生了氢脆断裂。其原因是缸盖螺栓在表面磷化后的去氢处理不当, 导致装配后缸盖螺栓在拉应力的作用下产生氢脆裂纹, 并最终发生断裂。
缸盖螺栓
氢脆断裂
拉应力
motor
cylinder bolt
hydrogen brittleness
tensile stress
Abstract
The cylinder blot of motor fractured after assembly. The fracture reason was analyzed by means of macro and micro examination, chemical composition analysis, mechanical property testing, hydrogen brittleness test and so on. The results showed that the hydrogen brittleness occurred in the bolt. The fracture of bolt was due to hydrogen during parkerizing and dehydrogen process under tensile stress.
中图分类号 U464.132
所属栏目 质量控制与失效分析
基金项目
收稿日期 2013/6/21
修改稿日期
网络出版日期
作者单位点击查看
备注史霞(1981-), 女, 工程师。
引用该论文: SHI Xia,LIU Zhi-ying. Analysis on Fracture Reason of Cylinder Blot in Motor[J]. Physical Testing and Chemical Analysis part A:Physical Testing, 2014, 50(5): 359～362
史霞,刘志莹. 发动机缸盖螺栓断裂原因分析[J]. 理化检验－物理分册, 2014, 50(5): 359～362
被引情况:
【1】俞圆,怀华培,戴立强,凌国平, "尼龙丝切口形貌与旋转剃须刀锋利度关系",理化检验－物理分册 51, 874-879(2015)
【2】姚兵印,张志博,马剑民,王玉兴,卢正欣, "风力发电机组叶片连接高强螺栓的断裂原因分析",理化检验－物理分册 52, 339-344(2016)
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】恩格 L, 克林格 H.金属损伤图谱: 金属失效的扫描电子显微镜研究[M].北京: 机械工业出版社, 1990: 108-109.
【2】陈南平, 顾守仁, 沈万慈.脆性失效分析[M].北京: 机械工业出版社, 1993: 140-141.
【3】惠卫军, 董瀚, 翁宇庆.高强度螺栓钢的发展动向[J].机械工程材料, 2002, 26(11): 1-5.
【4】胡晓辉.3Cr13钢弹簧片断裂分析[J].理化检验-物理分册, 2005, 41(10): 515-517.
【2】陈南平, 顾守仁, 沈万慈.脆性失效分析[M].北京: 机械工业出版社, 1993: 140-141.
【3】惠卫军, 董瀚, 翁宇庆.高强度螺栓钢的发展动向[J].机械工程材料, 2002, 26(11): 1-5.
【4】胡晓辉.3Cr13钢弹簧片断裂分析[J].理化检验-物理分册, 2005, 41(10): 515-517.
相关信息