锅炉对流管开裂原因分析
Analysis on Cracking Reason of Boiler Convection Pipe
摘 要
针对某锅炉相邻部位的对流管在使用过程中第二次出现开裂漏水的现象, 采用化学成分分析、力学性能测试、宏观及微观检验等方法, 对造成锅炉对流管开裂漏水的原因进行了分析。结果表明: 该对流管局部超温运行, 使该段管子使用强度明显下降, 最终导致开裂漏水。
对流管
超温运行
裂纹
boiler
convection tube
overtemperature operation
crack
Abstract
Aiming at the phenomenon of cracking and water leakage appearing secondly on convection tube of neighborhood positions in some boiler during operation, testing methods such as chemical composition analysis, mechanical property testing, macroscopic and microscopic examination were applied to identify the cracking and water leakage reasons on boiler convection tube. The results showed that overtemperature operation of local pipe made its strength reduce significantly, and led to cracking and water leakage finally.
中图分类号 TK223.3
所属栏目 质量控制与失效分析
基金项目
收稿日期 2013/8/12
修改稿日期
网络出版日期
作者单位点击查看
备注黄卫冲(1963-), 男, 高级工程师。
引用该论文: HUANG Wei-chong. Analysis on Cracking Reason of Boiler Convection Pipe[J]. Physical Testing and Chemical Analysis part A:Physical Testing, 2014, 50(5): 365～367
黄卫冲. 锅炉对流管开裂原因分析[J]. 理化检验－物理分册, 2014, 50(5): 365～367
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】李炯辉, 林德成, 李静媛,等.金属材料金相图谱[M].北京: 机械工业出版社, 2006.
【2】姜求志, 王金瑞, 马士林, 等.火力发电厂金属材料手册[M].北京: 中国电力出版社, 2001.
【3】王立坤, 王艳芳, 赵久国,等.某热电厂炉管开裂失效分析[J].理化检验-物理分册,2012(12): 828-830.
【4】于显龙, 张瑞, 黄维浩.机械设备失效分析[M].上海: 上海科学技术出版社, 2009.
【5】黄卫冲, 杨烨.SZL15-1.25-A锅炉对流管爆裂原因分析[J].理化检验-物理分册,2001(8): 351-353.
【2】姜求志, 王金瑞, 马士林, 等.火力发电厂金属材料手册[M].北京: 中国电力出版社, 2001.
【3】王立坤, 王艳芳, 赵久国,等.某热电厂炉管开裂失效分析[J].理化检验-物理分册,2012(12): 828-830.
【4】于显龙, 张瑞, 黄维浩.机械设备失效分析[M].上海: 上海科学技术出版社, 2009.
【5】黄卫冲, 杨烨.SZL15-1.25-A锅炉对流管爆裂原因分析[J].理化检验-物理分册,2001(8): 351-353.
相关信息