29340推力滚子轴承失效分析
Failure Analysis on 29340 Thrust Roller Bearing
摘 要
通过宏观观察、化学成分分析、硬度测试、金相及断口分析等方法, 对29340推力滚子轴承失效的原因进行了分析。结果表明: 29340推力滚子轴承在试验安装时, 由于施加压力方法不当, 内外圈产生偏心, 致使外圈受到较大载荷的挤压, 产生塑性变形, 在压痕和非金属夹杂物处发生断裂。
轴承偏心
塑性变形
脆性断裂
rolling bearing
bearing eccentricity
plastic deformation
brittle fracture
Abstract
Failure analysis was investigated by external pattern observation for the bearing, chemical composition analysis, hardness testing, metallographic examination and fracture analysis. The results showed that the bearing was fractured at the indentation and nonmetallic inclusions because of the eccentricity between the inner and outer rings making the outer ring extruded with a large load, due to the improper method during the test installation of 29340 thrust roller bearing.
中图分类号 TH133.33+1
所属栏目 质量控制与失效分析
基金项目
收稿日期 2013/9/11
修改稿日期
网络出版日期
作者单位点击查看
备注高秋然(1985-), 女, 助理工程师。
引用该论文: GAO Qiu-ran,LI Lu-jiang,LI Sheng-wei,ZHANG Zuo-chao. Failure Analysis on 29340 Thrust Roller Bearing[J]. Physical Testing and Chemical Analysis part A:Physical Testing, 2014, 50(5): 368～370
高秋然,李鲁江,李省伟,张作超. 29340推力滚子轴承失效分析[J]. 理化检验－物理分册, 2014, 50(5): 368～370
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】GB/T 18254-2002高碳铬轴承钢[S].
【2】JB/T 1255-2001高碳铬轴承钢滚动轴承零件 热处理技术条件[S].
【3】JB/T 7361-2007滚动轴承 零件硬度试验方法[S].
【2】JB/T 1255-2001高碳铬轴承钢滚动轴承零件 热处理技术条件[S].
【3】JB/T 7361-2007滚动轴承 零件硬度试验方法[S].
相关信息