SS400钢热轧板表面纵裂纹成因分析
Reason Analysis on Longitudinal Cracks on Surface of Hot Rolled Plate of SS400 Steel
摘 要
采用显微组织观察、扫描电镜和能谱分析等手段探讨了SS400钢热轧板表面纵裂纹的形成机理。结果表明: SS400钢热轧板表面纵裂纹在轧制过程中形成, 其裂纹源是连铸过程中结晶器保护渣卷入形成的皮下夹渣。
薄板坯连铸连轧
纵裂纹
SS400 steel
compact strip production
longitudinal crack
Abstract
The reason of longitudinal cracks on the surface of hot rolled plate of SS400 steel was investigated by means of optical microscope, SEM, EDS and so on. The results showed that the reason led to the surface cracks during rolling was the oxide which distributed under the surface.
中图分类号 TF704.7
所属栏目 质量控制与失效分析
基金项目
收稿日期 2013/8/5
修改稿日期
网络出版日期
作者单位点击查看
备注师静蕊(1976-), 女, 工程师。
引用该论文: SHI Jing-rui,SHEN Dong-dong,YUAN Ze-xi. Reason Analysis on Longitudinal Cracks on Surface of Hot Rolled Plate of SS400 Steel[J]. Physical Testing and Chemical Analysis part A:Physical Testing, 2014, 50(5): 380～382
师静蕊,沈冬冬,袁泽喜. SS400钢热轧板表面纵裂纹成因分析[J]. 理化检验－物理分册, 2014, 50(5): 380～382
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】殷瑞钰.关于中国薄板坯连铸连轧的工艺装备优化和投资问题[J].钢铁, 2003,38(8): 1-9.
【2】孙彦辉, 赵长亮, 蔡开科, 等.CSP板卷边部裂纹影响因素分析[J].钢铁研究学报, 2007,19(4): 39-43.
【3】KAMETAL H. Fractal analysis of the surface cracks on continuouly cast steel slab[J].Metallurgical and Materials Transcation B29B,1998(6): 1261-1267.
【4】王新华.钢铁冶金——炼钢学[M].北京: 高等教育出版社, 2007: 359.
【2】孙彦辉, 赵长亮, 蔡开科, 等.CSP板卷边部裂纹影响因素分析[J].钢铁研究学报, 2007,19(4): 39-43.
【3】KAMETAL H. Fractal analysis of the surface cracks on continuouly cast steel slab[J].Metallurgical and Materials Transcation B29B,1998(6): 1261-1267.
【4】王新华.钢铁冶金——炼钢学[M].北京: 高等教育出版社, 2007: 359.
相关信息