固溶处理温度对Inconel600合金组织和性能的影响
Influence of Solution Treatment Temperature on Microstructure and Properties of Inconel600 Alloy
摘 要
研究了Inconel600合金在950~1 200 ℃保温5 min后的组织与性能的关系。结果表明: 固溶处理后Inconel600合金的硬度随温度的升高先增大后减小, 在1 050 ℃达到最大值。进行了硫酸铁-硫酸晶间腐蚀试验, 结果表明: 固溶处理后的合金耐50%(质量分数)硫酸-硫酸铁晶间腐蚀性能良好。
固溶处理
耐蚀性能
Inconel600 alloy
solution treatment
corrosion resistance
Abstract
The relationship between microstructure and properties of Inconel600 alloy which were solution treated at 950~1 200 ℃ was researched. The test results showed that the hardness of Inconel600 alloy raised firstly then declined with temperature increasing, and reached maximum at 1 050 ℃. The ferric sulfate-sulfuric acid test results indicated that the Inconel600 alloy had a good corrosion resistant property after solution treatment.
中图分类号 TG161
所属栏目 试验与研究
基金项目
收稿日期 2014/4/21
修改稿日期
网络出版日期
作者单位点击查看
备注王健美(1985-), 女, 工程师。
引用该论文: WANG Jian-mei. Influence of Solution Treatment Temperature on Microstructure and Properties of Inconel600 Alloy[J]. Physical Testing and Chemical Analysis part A:Physical Testing, 2014, 50(7): 487～489
王健美. 固溶处理温度对Inconel600合金组织和性能的影响[J]. 理化检验－物理分册, 2014, 50(7): 487～489
被引情况:
【1】赵卓, "690耐蚀合金管材晶粒度和碳化物形貌分析用金相侵蚀剂的选择",理化检验－物理分册 52, 859-863(2016)
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】杨瑞成, 聂福荣, 郑丽平, 等.镍基耐蚀合金特性、进展及其应用[J].甘肃工业大学学报, 2002, 28(4): 29-33.
【2】刘海定, 王东哲, 魏捍东, 等.高性能镍基耐腐蚀合金的开发进展[C]//The 6th China Corrosion Conference. Yinchuan:2011:1368-1373.
【3】白红军, 丁五洲, 李林.Inconel600镍基合金热轧板表面起皮缺陷原因分析[J].中国钛业, 2011, 3:26-30.
【4】郭永安.热处理对镍基高温合金组织和性能的影响[D].沈阳: 沈阳工业大学, 2007.
【5】赵雪会, 白真权, 冯耀荣, 等.热处理温度及析出相对镍基合金腐蚀性能的影响[J].材料热处理学报, 2012, 33(8): 39-44.
【2】刘海定, 王东哲, 魏捍东, 等.高性能镍基耐腐蚀合金的开发进展[C]//The 6th China Corrosion Conference. Yinchuan:2011:1368-1373.
【3】白红军, 丁五洲, 李林.Inconel600镍基合金热轧板表面起皮缺陷原因分析[J].中国钛业, 2011, 3:26-30.
【4】郭永安.热处理对镍基高温合金组织和性能的影响[D].沈阳: 沈阳工业大学, 2007.
【5】赵雪会, 白真权, 冯耀荣, 等.热处理温度及析出相对镍基合金腐蚀性能的影响[J].材料热处理学报, 2012, 33(8): 39-44.
相关信息