Properties Testing of M40J High Modulus Carbon Fiber
摘 要
对日本东丽公司生产的M40J碳纤维复丝和单向板的性能进行了试验研究, 提供了5套可分析对比的试验数据; 对化学试验选用方法、注意环节、影响因素等进行了探讨; 对力学试验使用标准、试验过程和失效模式等进行了论述; 讨论了纤维体积含量、胶含量和空隙率的控制范围, 以及对M40J碳纤维单向板力学性能的影响。
Abstract
The properties of M40J carbon fiber multifilament and unidirectional laminates which produced by Japanese Dongli company were studied. From five data, the method of chemical experiment, matters needing attention and influence factors were researched. The standard of mechanical tests, test process and failure mode were analyzed. At last the influence on mechanical properties of unidirectional M40J carbon fiber laminates by fiber volume content, gum content and void ratio were discussed.
中图分类号 TQ342+.742
所属栏目 试验技术与方法
基金项目
收稿日期
修改稿日期
网络出版日期
作者单位点击查看
引用该论文: WANG Bao-rui. Properties Testing of M40J High Modulus Carbon Fiber[J]. Physical Testing and Chemical Analysis part A:Physical Testing, 2014, 50(7): 495~498
王宝瑞. M40J高模量碳纤维的性能测试[J]. 理化检验-物理分册, 2014, 50(7): 495~498
共有人对该论文发表了看法,其中:
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】王宝瑞, 李建国.纤维密度测定的研究[J].纤维复合材料, 2009(3): 43-46.
【2】施琪, 吴亚平.碳纤维复合材料抗拉性能测试结构的影响因素分析[J].兰州交通大学学报, 2008(8): 51-53.
【3】李超, 丘哲明.树脂含量对碳布/环氧复合材料拉伸、压缩性能的影响[J].玻璃钢, 2003(4): 15-17.
【4】李丽.高强度、高模量碳纤维复合材料拉伸性能测试方法的研究[J].理化检验-物理分册, 2004(7): 337-340.
【5】宋亚吉, 赵子津.高模量复合材料力学性能测试[J].航天器工程, 2003(2): 47-53.
【6】龚博安, 韦娟芳.高强度和高模量碳纤维复合材料失效模式比较[J].高科技纤维与应用, 2007(6): 25-29.
【2】施琪, 吴亚平.碳纤维复合材料抗拉性能测试结构的影响因素分析[J].兰州交通大学学报, 2008(8): 51-53.
【3】李超, 丘哲明.树脂含量对碳布/环氧复合材料拉伸、压缩性能的影响[J].玻璃钢, 2003(4): 15-17.
【4】李丽.高强度、高模量碳纤维复合材料拉伸性能测试方法的研究[J].理化检验-物理分册, 2004(7): 337-340.
【5】宋亚吉, 赵子津.高模量复合材料力学性能测试[J].航天器工程, 2003(2): 47-53.
【6】龚博安, 韦娟芳.高强度和高模量碳纤维复合材料失效模式比较[J].高科技纤维与应用, 2007(6): 25-29.
相关信息
标题 | 相关频次 | |
碳纤维复丝的拉伸性能 | 2 | |
碳纤维复丝和单丝拉伸性能测试方法 | 2 | |
国内外超声探头性能测试标准的比较与分析 | 1 | |
基于NB/T47013-2015的涡流检测系统性能测试要求的探讨 | 1 | |
排烟空冷塔用防腐蚀涂料体系性能对比 | 1 | |
热电材料的应用、研究及性能测试进展 | 1 | |
小径薄壁管环缝用超声波聚焦探头性能测试的特殊试块的设计及使用 | 1 | |
用于水下探测的宽带超声换能器设计 | 1 |