Rupture Analysis on Dyeing Machine Shell in High Temperature and High Pressure
摘 要
通过现场勘察、化学成分分析、金相检验、能谱分析等手段对不锈钢制高温高压染色机壳体破裂的原因进行了分析。结果表明: 壳体破裂的原因是304不锈钢制染色机壳体在含有高浓度氯离子的染液环境中, 并在操作应力及焊接残余应力的联合作用下, 发生了应力腐蚀开裂。
Abstract
The rupture reason of dyeing machine shell of stainless steel in high temperature and high pressure was analyzed by means of site investigation, chemical composition analysis, metallographic examination, energy spectrum analysis and so on. The results showed that the failure reason was the SCC occurred in the material of dyeing machine shell in the dye liquor with high concentration of chloride ion, and in the combined effect of operation stress and welding residual stress.
中图分类号 X788
所属栏目 质量控制与失效分析
基金项目
收稿日期 2013/7/31
修改稿日期
网络出版日期
作者单位点击查看
备注黎华(1964-), 男, 高级工程师, 承压类特种设备高级检验师。
引用该论文: LI Hua,WANG Lian,LIN Jin-mei. Rupture Analysis on Dyeing Machine Shell in High Temperature and High Pressure[J]. Physical Testing and Chemical Analysis part A:Physical Testing, 2014, 50(7): 512~514
黎华,王恋,林金梅. 高温高压染色机壳体破裂分析[J]. 理化检验-物理分册, 2014, 50(7): 512~514
共有人对该论文发表了看法,其中:
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】GB 50235-2010工业金属管道工程施工规范[S].
【2】TSG D0001-2009压力管道安全技术监察规程——工业管道[S].
【3】刘劲松, 常治平, 吴进强.316L不锈钢人孔盖板破裂原因分析[J].理化检验-物理分册, 2012, 48(3): 197-205.
【4】张龙娟.304和316L不锈钢在印染环境中的应力腐蚀试验研究[D].杭州: 浙江大学, 2010:3-9.
【5】郭演星.J型高温高速染色机常见缺陷与检测要点[J].理化检验-物理分册, 2010, 46(4): 251-253.
【6】任凌波, 任晓蕾.压力容器腐蚀与控制[M].北京: 化学工业出版社, 2003: 78, 254.
【2】TSG D0001-2009压力管道安全技术监察规程——工业管道[S].
【3】刘劲松, 常治平, 吴进强.316L不锈钢人孔盖板破裂原因分析[J].理化检验-物理分册, 2012, 48(3): 197-205.
【4】张龙娟.304和316L不锈钢在印染环境中的应力腐蚀试验研究[D].杭州: 浙江大学, 2010:3-9.
【5】郭演星.J型高温高速染色机常见缺陷与检测要点[J].理化检验-物理分册, 2010, 46(4): 251-253.
【6】任凌波, 任晓蕾.压力容器腐蚀与控制[M].北京: 化学工业出版社, 2003: 78, 254.
相关信息