60Si2Mn弹簧钢力学性能不合格原因分析
Reason Analysis on Unqualified Mechanical Property of 60Si2Mn Spring Steel
摘 要
采用宏观及微观断口分析、金相检验、化学成分分析等方法, 对60Si2Mn圆钢材料力学性能检测不合格的原因进行了分析。结果表明: 由于材料内部的氢未完全扩散出去, 且材料内部存在偏析缺陷, 氢原子在偏析区聚集, 在材料内部产生氢致裂纹是造成力学性能不合格的主要原因。
力学性能
氢致裂纹
60Si2Mn spring steel
mechanical property
hydrogen induced crack
Abstract
By means of macro and micro fracture analysis, metallographic examination, chemical compositions analysis and so on, the reason of unqualified mechanical property of 60Si2Mn spring steel was investigated. The results showed that the main reasons were due to hydrogen in material was not fully spreaded out, and there was segregation defects in material, hydrogen assembled in the segregation defects and produced hydrogen induced cracking.
中图分类号 TF762+.5
所属栏目 质量控制与失效分析
基金项目
收稿日期 2013/7/1
修改稿日期
网络出版日期
作者单位点击查看
备注王月祥(1987-), 男, 助理工程师, 学士。
引用该论文: WANG Yue-xiang,SUN Jing-hua. Reason Analysis on Unqualified Mechanical Property of 60Si2Mn Spring Steel[J]. Physical Testing and Chemical Analysis part A:Physical Testing, 2014, 50(7): 515～517
王月祥,孙景花. 60Si2Mn弹簧钢力学性能不合格原因分析[J]. 理化检验－物理分册, 2014, 50(7): 515～517
被引情况:
【1】吴 睿,张晓清,侯丽华, "65Si2MnWA弹簧钢线状缺陷分析",理化检验－物理分册 52, 435-437(2016)
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】钟群鹏, 赵子华.断口学[M].北京: 高等教育出版社, 2006:270-290.
【2】黄振东.钢铁金相图谱[M].北京: 中国科技文化出版社, 2005:1314-1317.
【3】姜锡山, 赵晗.钢铁显微断口速查手册[M].北京: 机械工业出版社, 2010:182-191.
【2】黄振东.钢铁金相图谱[M].北京: 中国科技文化出版社, 2005:1314-1317.
【3】姜锡山, 赵晗.钢铁显微断口速查手册[M].北京: 机械工业出版社, 2010:182-191.
相关信息