双列圆锥滚子轴承外圈断裂分析
Fracture Analysis on Outer Ring of Double Row Tapered Roller Bearing
摘 要
通过宏观检验、化学成分分析、金相检验、表面残余应力测试等方法, 对双列圆锥滚子轴承外圈断裂的原因进行了分析。结果表明: 在运转过程中由于套圈外径面与鞍座之间异常接触, 致使外径面受到剧烈摩擦, 产生磨热层并萌生裂纹, 最终导致轴承外圈贯穿断裂。
外圈
摩擦
裂纹
double row tapered roller bearing
outer ring
friction
crack
Abstract
By means of macroscopic examination, chemical composition analysis, metallographic examination, stress test, the fracture reasons of outer ring of double row tapered roller bearing were analyzed. The results showed that in the process of operation the abnormal contact between the outside diameter surface and the saddle led to friction and crack, and to fracture along the crack propagation.
中图分类号 TH133.33
所属栏目 质量控制与失效分析
基金项目
收稿日期 2013/7/16
修改稿日期
网络出版日期
作者单位点击查看
备注杨争(1984-), 女, 硕士。
引用该论文: YANG Zheng,WU Yong-gang,WEI Jian-wen,CHEN Cui-li,ZHANG Ling. Fracture Analysis on Outer Ring of Double Row Tapered Roller Bearing[J]. Physical Testing and Chemical Analysis part A:Physical Testing, 2014, 50(7): 528～531
杨争,仵永刚,魏建文,陈翠丽,张玲. 双列圆锥滚子轴承外圈断裂分析[J]. 理化检验－物理分册, 2014, 50(7): 528～531
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】雷建中, 杨晓蔚.滚动轴承零件废品分析及图谱[M].洛阳:洛阳轴承研究所, 2001:84-87.
【2】李大东, 刘锦燕, 余腾义.PG4热处理钢轨落锤断裂原因分析[J].理化检验-物理分册, 2011, 47(6):373-374.
【2】李大东, 刘锦燕, 余腾义.PG4热处理钢轨落锤断裂原因分析[J].理化检验-物理分册, 2011, 47(6):373-374.
相关信息