35CrMo钢螺栓断裂原因分析
Failure Analysis on Fracture of 35CrMo Steel Bolts
摘 要
某电梯用10.9级35CrMo钢螺栓在安装一段时间后发生断裂,采用直读光谱仪、扫描电子显微镜、光学显微镜以及维氏硬度计等仪器设备对螺栓断裂原因进行了分析。结果表明: 该螺栓在氢和静拉力的共同作用下发生了氢致延迟断裂。
断裂
氢致延迟断裂
bolt
fracture
hydrogen induced delay fracture
Abstract
The 10.9 grade 35CrMo steel bolts for elevators fractured after being installed for a period of time, and the fracture reasons were analyzed by direct-reading spectrometer, scanning electronic microscope, optical microscope, Vickers hardness test machine and so on. The results show that the fracture of the bolts was hydrogen induced delay fracture under the co-action of hydrogen and static tensile stress.
中图分类号 TH131.3 TG115
所属栏目 质量控制与失效分析
基金项目
收稿日期 2014/6/3
修改稿日期
网络出版日期
作者单位点击查看
备注陈瑗元(1976-), 女, 工程师, 学士。
引用该论文: CHEN Yuan-yuan,LU Hui. Failure Analysis on Fracture of 35CrMo Steel Bolts[J]. Physical Testing and Chemical Analysis part A:Physical Testing, 2014, 50(8): 616～618
陈瑗元,陆慧. 35CrMo钢螺栓断裂原因分析[J]. 理化检验－物理分册, 2014, 50(8): 616～618
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】机械工业理化检验人员技术培训和资格鉴定委员会. 金相检验[M]. 北京: 中国计量出版社, 2008: 268.
【2】王春亮. 8.8级螺栓断裂原因分析[J]. 理化检验-物理分册, 2013, 49(增刊2): 305-311.
【2】王春亮. 8.8级螺栓断裂原因分析[J]. 理化检验-物理分册, 2013, 49(增刊2): 305-311.
相关信息