双相不锈钢阀门漏水原因分析
Analysis on Leakage Reason of Duplex Stainless Steel Valve
摘 要
S44 DN200阀门在使用中因为挡圈锈蚀而漏水。通过化学成分分析、金相检验以及点腐蚀试验等手段对挡圈锈蚀的原因进行了分析。结果表明: 挡圈的点蚀当量偏低, 热处理过程不充分, 在含有高浓度氯离子的海水系统的共同作用下, 挡圈发生腐蚀而使阀门漏水。
阀门
挡圈
漏水
点腐蚀
缝隙腐蚀
duplex stainless steel
valve
seat retainer
leakage
pitting corrosion
crevice corrosion
Abstract
The S44 DN200 valve was leaked during operation because of the seat retainer corrosion. By means of chemical composition analysis, metallographic examination, pitting corrosion and so on, the corrosion reason of seat retainer was analyzed. The results showed that the PREN of retainer was lower than standard, the heat treatment process was not according to the specification, the seat retainer corrosion led to the valve leaked in seawater containing high concentrations of chloride.
中图分类号 TG172.5
所属栏目 质量控制与失效分析
基金项目
收稿日期 2013/8/5
修改稿日期
网络出版日期
作者单位点击查看
备注甄玉洁(1976-), 女, 工程师, 学士。
引用该论文: ZHEN Yu-jie. Analysis on Leakage Reason of Duplex Stainless Steel Valve[J]. Physical Testing and Chemical Analysis part A:Physical Testing, 2014, 50(9): 681～684
甄玉洁. 双相不锈钢阀门漏水原因分析[J]. 理化检验－物理分册, 2014, 50(9): 681～684
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】张文华.不锈钢及其热处理[M].沈阳: 辽宁科学技术出版社, 2010: 199, 201.
【2】吴玖, 姜世振, 韩俊媛, 等.双相不锈钢[M].北京: 冶金工业出版社, 1999:31.
【3】赵晖,徐玲.热处理对双相不锈钢的组织和腐蚀性能的影响[J].腐蚀科学与防护技术,2009,21(3):288.
【2】吴玖, 姜世振, 韩俊媛, 等.双相不锈钢[M].北京: 冶金工业出版社, 1999:31.
【3】赵晖,徐玲.热处理对双相不锈钢的组织和腐蚀性能的影响[J].腐蚀科学与防护技术,2009,21(3):288.
相关信息