隔热条耐水性测试试验方法
Water Resistance Testing Methods of Thermal Barrier Strip
摘 要
耐水性测试是判断隔热条性能的重要手段。按照GB/T 23615.1-2009对隔热条采用两种不同的耐水测试方法进行了对比试验。结果表明:沸水试验和常温浸泡试验的结果虽然比较接近,但常温浸泡试验的条件更为苛刻,其结果更能代表隔热条的耐水性能。
耐水性试验
横向抗拉特征值
沸水试验
常温浸泡试验
thermal barrier strip
water resistant test
transverse tensile characteristic value
boiling water test
immersion test at normal temperature
Abstract
Water resistance was an important index which will determine the properties of thermal barrier strip. The comparison between the two different methods to test water resistance was performed according to GB/T 23615.1-2009 standard, including the boiling water test and the immersion test at normal temperature. It was found that the testing results of the different methods were close, but the immersion test at normal temperature was more severe and more representative of the water resistance property of thermal barrier strip.
中图分类号 TU111.2+4
所属栏目 试验技术与方法
基金项目
收稿日期 2014/1/3
修改稿日期
网络出版日期
作者单位点击查看
备注张红菊(1983-),女,工程师。
引用该论文: ZHANG Hong-ju,LI Pu,FAN Zhi-gang,ZHANG Dong-hui,WANG Fu-sheng. Water Resistance Testing Methods of Thermal Barrier Strip[J]. Physical Testing and Chemical Analysis part A:Physical Testing, 2014, 50(11): 816～817
张红菊,李璞,樊志罡,张东晖,王福生. 隔热条耐水性测试试验方法[J]. 理化检验－物理分册, 2014, 50(11): 816～817
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】方万漂.断桥铝型材用尼龙隔热条材料耐老化性能的研究［J］.门窗,2012(3):40-44.
【2】郑金峰.关注节能铝门窗幕墙发展与存在的质量问题——隔热条、穿条式隔热铝型材［J］.中国建筑金属结构,2009(5):23-24.
【3】吴亚龙,梁珍贵.隔热条——隔热铝门窗的“芯”［J］.中国建筑金属结构,2009(4):38-43.
【4】纪红,崔佳,李永丰,等.隔热条的轴钉应力开裂试验方法［J］.理化检验-物理分册,2013,49(3):168-170.
【2】郑金峰.关注节能铝门窗幕墙发展与存在的质量问题——隔热条、穿条式隔热铝型材［J］.中国建筑金属结构,2009(5):23-24.
【3】吴亚龙,梁珍贵.隔热条——隔热铝门窗的“芯”［J］.中国建筑金属结构,2009(4):38-43.
【4】纪红,崔佳,李永丰,等.隔热条的轴钉应力开裂试验方法［J］.理化检验-物理分册,2013,49(3):168-170.
相关信息