Discussion on Some Problems in Anti-slip Coefficient Testing of High Strength Bolt Friction-type Joint Surface
摘 要
抗滑移系数是检查高强度螺栓摩擦型连接面涂层质量的重要参数。从涉及该参数的4个现行有效的国家及行业标准入手,分析了试样的型式、板宽、螺栓孔径、螺栓中心距等因素对抗滑移系数检测造成的影响。结果表明:两栓连接试样较三栓连接试样更能减小试样不均匀变形对检测结果的影响;随着试样螺栓孔径的增大,抗滑移系数随之降低;受到偏心拉伸荷载时,抗滑移系数检测结果偏小。最后对现有检测标准的不足之处进行了讨论,提出了相应的建议。
Abstract
Anti-slip coefficient is an important parameter for checking the coating quality of high strength bolt friction-type joint surface. From the parameter which was involved in four existing effective national and industry standards, the influence of specimen type, plate width, bolt aperture, bolt center distance and other factors in anti-slip coefficient testing was analyzed. The results showed that the two bole joint specimen could reduce the influence of inhomogeneous deformation of specimen to the test results compared with three bole joint specimen;as the bolt aperture increased, anti-slip coefficient decreased;under eccentric tensile load, anti-slip coefficient was small. Finally, the shortcomings of the existing test standard were discussed, and some suggestions were put forward.
中图分类号 TH131
所属栏目 标准化
基金项目
收稿日期 2014/1/9
修改稿日期
网络出版日期
作者单位点击查看
备注叶君龙(1984-),男,工程师,学士。
引用该论文: YE Jun-long,YUE Ying,ZOU Li-sha. Discussion on Some Problems in Anti-slip Coefficient Testing of High Strength Bolt Friction-type Joint Surface[J]. Physical Testing and Chemical Analysis part A:Physical Testing, 2014, 50(11): 822~825
叶君龙,岳莹,邹莉莎. 高强度螺栓摩擦型连接面抗滑移系数检测过程中若干问题的探讨[J]. 理化检验-物理分册, 2014, 50(11): 822~825
被引情况:
【1】韦俏斌,陈贤水,荀志国, "硬度差在核电站反应堆压力容器主螺栓验收时的特殊应用",理化检验-物理分册 51, 626-627(2015)
共有人对该论文发表了看法,其中:
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】于翔,陈绪宏,杨章程.高强度大六角头螺栓联接副的扭矩系数和抗滑移系数的测定方法[J].理化检验-物理分册,2008,44(9):475-478.
【2】何武,杨小敏.浅析钢结构栓接板面抗滑移系数试验方法[J].管理与技术,2005,1:33-36.
【3】彭铁红,侯兆欣,文双玲,等.螺栓孔径与孔型对高强度螺栓摩擦型连接承载能力影响的试验[J].钢结构,2007,22(8):30-34.
【2】何武,杨小敏.浅析钢结构栓接板面抗滑移系数试验方法[J].管理与技术,2005,1:33-36.
【3】彭铁红,侯兆欣,文双玲,等.螺栓孔径与孔型对高强度螺栓摩擦型连接承载能力影响的试验[J].钢结构,2007,22(8):30-34.
相关信息