17-4PH马氏体沉淀硬化不锈钢磁粉检测磁痕分析
The Indication Analysis of Magnetic Particle Testing on 17-4PH Martensitic Precipitation-hardening Stainless Steel
摘 要
针对17-4PH马氏体沉淀硬化不锈钢在磁粉检测过程中出现的线性磁痕显示，结合金相试验对磁痕显示的微观组织形貌进行了分析，最终确定了磁痕的形成原因。试验发现，组织中存在一定量细针状δ-铁素体是造成17-4PH沉淀硬化不锈钢零件在进行磁粉探伤工序时出现线性显示的原因。结论为航空制造过程中马氏体不锈钢的磁粉检测的磁痕判定提供了依据。
磁粉检测
铁素体
微观组织
Martensitic stainless steel
Magnetic particle testing
Ferrite
Microstructure
Abstract
In this paper, the linear indication detected on the magnetic particle testing of 17-4PH martensitic precipitation-hardening stainless steel and the microstructure of indication is analyzed by metallography testing method, and the indication cause is finally made sure.It is found that the linear indication detected in the magnetic particle testing process is mainly caused by acerate δ-Ferrite. The conclusion supplies foundation for indication determinant in the magnetic particle testing process of martensitic precipitation-hardening stainless steel to aviation manufacture engineering.
中图分类号 TG115.28
所属栏目 试验研究
基金项目
收稿日期 2013/6/24
修改稿日期
网络出版日期
作者单位点击查看
备注王树志(1980-)，男，工程师，主要从事磁粉和渗透检测方面的研究。
引用该论文: WANG Shu-zhi,QIAO Hai-yan,GE Zi-liang,REN Xue-dong,ZHAO Meng. The Indication Analysis of Magnetic Particle Testing on 17-4PH Martensitic Precipitation-hardening Stainless Steel[J]. Nondestructive Testing, 2014, 36(1): 64～66
王树志,乔海燕,葛子亮,任学冬,赵梦. 17-4PH马氏体沉淀硬化不锈钢磁粉检测磁痕分析[J]. 无损检测, 2014, 36(1): 64～66
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】李进驰，关晓燕.17-4PH不锈钢转子热处理工艺的研究［J］.热加工工艺,2011(6):164-166.
【2】胡春燕，刘新灵，陶春虎，等.0Cr17Ni4Cu4Nb钢制螺钉断裂原因分析［J］.材料工程,2012(12):21-28.
【3】程健云.0Cr17Ni4Cu4Nb钢中的细小硫化物夹杂及其对策［J］.理化检验-物理分册,2007,23(10):487-493.
【4】国防科技工业无损检测人员资格鉴定与认证培训教材编审委员会.磁粉检测［M］.北京：机械工业出版社2004:98.
【2】胡春燕，刘新灵，陶春虎，等.0Cr17Ni4Cu4Nb钢制螺钉断裂原因分析［J］.材料工程,2012(12):21-28.
【3】程健云.0Cr17Ni4Cu4Nb钢中的细小硫化物夹杂及其对策［J］.理化检验-物理分册,2007,23(10):487-493.
【4】国防科技工业无损检测人员资格鉴定与认证培训教材编审委员会.磁粉检测［M］.北京：机械工业出版社2004:98.
相关信息