航天铝合金锻件缺陷检测与成因
Defect Detection and Reason of Aerospace Aluminum Alloy Forgings
摘 要
针对航天型号某批次铝合金锻件在超声A扫描检测过程中存在较多超标缺陷的问题，采用超声相控阵、工业CT、渗透及金相分析等多种检测方法对缺陷进行了定性分析。结果表明：造成该批次锻件不合格的原因为原材料夹杂缺陷，以为后续锻件原材料采购及质量控制提供一定的参考依据。
无损检测
缺陷分析
Aluminum alloy forgings
Nondestructive test
Defect analysis
Abstract
The excessive defects in aerospace aluminum alloy forgings were found during the processing in ultrasonic A-scan inspection. Qualitative analysis of defects was performed by means of ultrasonic phased array inspection, industrial computed tomography, penetrant testing, metallographic analysis and so on. The results showed that the cause for disqualified forgings was inclusion defects in the aluminum alloy bar, and this conclusion would provide certain reference basis for subsequent raw materials procurement and quality control.
中图分类号 TG115.28
所属栏目 试验研究
基金项目
收稿日期 2013/7/9
修改稿日期
网络出版日期
作者单位点击查看
备注王飞(1986-)，男，工程师，主要从事无损检测技术应用研究工作。
引用该论文: WANG Fei,ZHOU Jun,HUANG Yun. Defect Detection and Reason of Aerospace Aluminum Alloy Forgings[J]. Nondestructive Testing, 2014, 36(3): 36～38
王飞,周军,黄云. 航天铝合金锻件缺陷检测与成因[J]. 无损检测, 2014, 36(3): 36～38
被引情况:
【1】张 振,许有昌,耿永健,卜雄洙,王新征, "大型锥筒形锻件超声波C扫描成像自动检测系统",无损检测 38, 6-8(2016)
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】史亦韦.超声检测［M］.北京：机械工业出版社,2006:48-53.
【2】王伟，吴一全.超声相控阵用于无损检测的一种新方法［J］.传感器与微系统,2009,5(28):61-64.
【3】王爱华，李华.CT技术在航天产品检测中的应用［J］.航天控制,2001(2):11-14.
【2】王伟，吴一全.超声相控阵用于无损检测的一种新方法［J］.传感器与微系统,2009,5(28):61-64.
【3】王爱华，李华.CT技术在航天产品检测中的应用［J］.航天控制,2001(2):11-14.
相关信息