The Attenuation Effect of Pierced Delamination Corrosion on Magnetostrictive Guided Wave
摘 要
磁致伸缩导波检测技术对管道具有高效、全横截面检测等优点,但导波的检测效果易受多种因素,如弯头、支架和焊缝等的影响。针对检测试验中发现的分层腐蚀缺陷,通过解剖等试验手段,开展其对磁致伸缩导波信号的衰减影响的试验。试验结果表明,穿透分层腐蚀缺陷对导波信号的衰减影响剧烈,且难于用其他检测方法验证。
Abstract
The technology of magnetostrictive guided waves has been extensively applied in pipeline detection because of the excellent advantages, high efficiency and comprehensive detection of cross section, for example. However, the effectiveness of guided wave detection technique is affected by various factors, such as elbow, bracket bearing and welds, which might lead to detection failure. In this paper, based on corroded lamination defects which are discovered in the experiments, the attenuation effect of magnetostrictive guided waves caused is investigated with careful anatomy. The results show that the laminated corrosion defect has severe impact on the signals loss and it is also difficult to be determined by other non-destructive testing methods also.
中图分类号 TG115.28
所属栏目 试验研究
基金项目
收稿日期 2013/9/20
修改稿日期
网络出版日期
作者单位点击查看
备注张晓斌(1972-),男,博士,高级工程师,主要从事先进无损检测技术研究、失效分析。
引用该论文: ZHANG Xiao-bin,HUANG Zhen,HUANG Long-peng,LI Kun-xiang,WEI Yu-wei. The Attenuation Effect of Pierced Delamination Corrosion on Magnetostrictive Guided Wave[J]. Nondestructive Testing, 2014, 36(5): 52~54
张晓斌,黄震,黄龙鹏,黎坤祥,魏玉伟. 穿透分层腐蚀缺陷对磁致伸缩导波信号的衰减影响[J]. 无损检测, 2014, 36(5): 52~54
共有人对该论文发表了看法,其中:
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】PAVLAKOVIC B, LOWE M J S, ALLEYNE D N, et al. Disperse: a general purpose program for creating dispersion curves[C]// Review of Progress in Quantitative NDE. New York: Plenum Press,1997:185-192.
【2】BAY H, SHAH A, POPPLEWELL N, et al. Scattering of guided waves by circumferential cracks in steel pipes[C]// Review of progress in Quantitative NDE. New York: Plenum Press,2001:188-194.
【3】VOGT T, ALLEYNE D, PAVLAKOVIC B. Application of guided wave technology to tube inspection[C]// Berlin: ECNDT, 2006.
【4】王禹钦,王维斌,陈长坤,等.输气管道超声导波检测技术[J].无损检测,2008,30(9):617-619.
【5】董为荣,帅健,许葵.管道T(0,1)模态导波检测数值模拟研究[J].无损检测,2008,30(3):149-152.
【2】BAY H, SHAH A, POPPLEWELL N, et al. Scattering of guided waves by circumferential cracks in steel pipes[C]// Review of progress in Quantitative NDE. New York: Plenum Press,2001:188-194.
【3】VOGT T, ALLEYNE D, PAVLAKOVIC B. Application of guided wave technology to tube inspection[C]// Berlin: ECNDT, 2006.
【4】王禹钦,王维斌,陈长坤,等.输气管道超声导波检测技术[J].无损检测,2008,30(9):617-619.
【5】董为荣,帅健,许葵.管道T(0,1)模态导波检测数值模拟研究[J].无损检测,2008,30(3):149-152.
相关信息