一种压水堆核电站主管道窄间隙自动焊焊缝的超声检测方法
A Ultrasonic Examination Method of Primary Coolant Pipelines in PWR
摘 要
核电站主管道是连接核岛主设备的大管径、大厚壁承压管道，主管道母材由奥氏体-铁素体不锈钢材料铸造而成，其内部晶粒粗大并具有各向异性，因此在主管道焊缝上实施超声检测难度很大。介绍了一种采用多角度双晶聚焦探头、多通道超声检测分析系统、与主管道同材质的试块及分层扫查方法以适用厚壁铸造不锈钢焊缝的超声检测方法。该方法提高了对未熔合缺陷的检出率和定位精度，与射线检测方法形成良好互补，确保了焊接质量。
自动焊
不锈钢
超声检测
焊缝
Primary coolant pipeline
Automatic welding
Stainless steel
Ultrasonic examination
Weld joint
Abstract
The main coolant pipelines(MCL) is the large diameter and thick walled pipeline in the nuclear island of PWR. The MCL base metal is austenitic-ferrite stainless steel formed by casting, and its internal structure contains coarse columnar crystal and anisotropy. So it is rather difficult to apply ultrasonic inspection for the MCL welds. But with the application of multi-angle twin crystal focusing probes, multi channel automatic UT system, and by using test block of the same material with the pipe and layered scanning method, the inspection technology is well suited for the MCL welding. Present UT inspection is complementary with the RT for the weld and is well required to guarantee the quality of the welds.
中图分类号 TG115.28
所属栏目 试验研究
基金项目
收稿日期 2013/1/22
修改稿日期
网络出版日期
作者单位点击查看
备注朱德才(1981-)，男，硕士研究生，主要从事核电安装施工管理工作。
引用该论文: ZHU De-cai,WANG dong,LI Yu-wei,LI Fu-liang. A Ultrasonic Examination Method of Primary Coolant Pipelines in PWR[J]. Nondestructive Testing, 2014, 36(5): 58～61
朱德才,王东,李予卫,李付良. 一种压水堆核电站主管道窄间隙自动焊焊缝的超声检测方法[J]. 无损检测, 2014, 36(5): 58～61
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】聂勇，李晓梅.核设备不锈钢堆焊层下裂纹超声波检测技术［J］.无损检测,2011,33(7):70-74.
【2】张鹰，雷毅，程真喜，等.奥氏体不锈钢焊接接头超声波检测研究［J］.石油化工设备,2004(2):14-17.
【3】张鹰，张延丰，雷毅.奥氏体不锈钢焊缝的超声波检测方法研究［J］.无损检测,2006,3(28):119-122.
【4】孙晓娜，雷毅.厚板奥氏体不锈钢焊缝显微组织分析［J］.金属热处理,2006(10):21-23.
【2】张鹰，雷毅，程真喜，等.奥氏体不锈钢焊接接头超声波检测研究［J］.石油化工设备,2004(2):14-17.
【3】张鹰，张延丰，雷毅.奥氏体不锈钢焊缝的超声波检测方法研究［J］.无损检测,2006,3(28):119-122.
【4】孙晓娜，雷毅.厚板奥氏体不锈钢焊缝显微组织分析［J］.金属热处理,2006(10):21-23.
相关信息