在用换热器管箱内表面渗透检测
The Penetrant Testing on Stainless Steel Inner Surfaces of Heat Exchanger Tube Tank in Use
摘 要
对某换热器管箱内表面的不锈钢焊缝和堆焊层进行渗透检测时, 发现大量密集点蚀孔和局部少量裂纹等缺陷, 分析了缺陷产生的原因, 并根据返修方案对缺陷进行返修。实例表明: 在用压力容器定期检验中, 必须对不锈钢设备可能产生缺陷的部位进行渗透检测, 才能保证容器的使用安全。
渗透检测
点蚀孔
裂纹
lean-rich amine heat exchanger
Penetrant testing
Spot corrosion hole
Crack
Abstract
The paper discusses that a large number of spot corrosion hole and a little cracks were found in the inner surfaces of stainless steel welding seams and overlay cladding of a lean- rich amine heat exchanger tube tank in use; analyses the causes and processes the defects. The example indicated that it is essential to carry out penetrant testing on the key parts of stainless steel equipment where may be have defects so as to guarantee the safety while in use.
中图分类号 TG115.28
所属栏目 实践经验
基金项目
收稿日期 2013/12/4
修改稿日期
网络出版日期
作者单位点击查看
备注武金宇(1974-), 男, 工程师, 本科, 从事锅炉、压力容器、压力管道定期检验和监督检验工作。
引用该论文: WU Jin-yu,FENG Zuo-ming,WANG Peng-wei,PENG Jun,PENG Zhao-hua,LIU Hong-cun,LIN Yin-geng. The Penetrant Testing on Stainless Steel Inner Surfaces of Heat Exchanger Tube Tank in Use[J]. Nondestructive Testing, 2014, 36(10): 64～65
武金宇,冯作明,王鹏威,彭军,彭朝华,刘宏村,林银庚. 在用换热器管箱内表面渗透检测[J]. 无损检测, 2014, 36(10): 64～65
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】JB/T 47305—2005承压设备无损检测［S］.
【2】文佳卉, 胡传顺, 肖凯316L不锈钢焊缝的点腐蚀行为［J］.特钢技术, 2009(2): 12-14.
【2】文佳卉, 胡传顺, 肖凯316L不锈钢焊缝的点腐蚀行为［J］.特钢技术, 2009(2): 12-14.
相关信息