GH648合金的热处理适应性
Adaptability of Heat Treatment for GH648 Alloy
摘 要
通过对GH648合金在不同热处理后的力学性能及显微组织进行试验研究, 获得了GH648合金制零(组)件热处理工艺的可行性评价, 从而达到确保零(组)件产品质量的目的。结果表明: GH648合金棒材经950 ℃渗铝处理、850 ℃长时除应力处理, 板材经1 050 ℃或950 ℃短时退火处理, 其力学性能均满足规定要求, 零(组)件热工艺可行。
热处理
固溶时效
力学性能
显微组织
GH648 alloy
heat treatment
solution and aging
mechanical properties
microstructure
Abstract
The mechanical properties and microstructure of GH648 alloy under different heat treatment state were studied in order to evaluate the feasibility of heat treatment process of components (assemblies) made of GH648 alloy and ensure the quality of products. The results showed that after aluminized at 950 ℃ and stress released at 850 ℃ for bar, or annealed at 1 050 ℃ or 950 ℃ for sheet, the mechanical properties of GH648 alloy could meet the requirements of specification. Therefore, the process of components (assemblies) was practicable.
中图分类号 TG156 TG144
所属栏目 试验与研究
基金项目
收稿日期 2014/8/24
修改稿日期
网络出版日期
作者单位点击查看
备注董晓峰(1971-), 男, 高级工程师, 学士。
引用该论文: DONG Xiao-feng,ZHANG Yan,GUO Zi-jing,HUO Shi-jun,WEI Lei,ZHU Hui-fang. Adaptability of Heat Treatment for GH648 Alloy[J]. Physical Testing and Chemical Analysis part A:Physical Testing, 2015, 51(1): 18～21
董晓峰,张艳,郭子静,霍世军,魏磊,朱慧芳. GH648合金的热处理适应性[J]. 理化检验－物理分册, 2015, 51(1): 18～21
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】朱日彰.高温腐蚀及耐高温腐蚀材料［M］.上海: 上海科学技术出版社, 1995.
【2】陈国良.高温合金学［M］.北京: 冶金工业出版社, 1988.
【3】黄乾尧, 李汉康.高温合金［M］.北京: 冶金工业出版社, 2000.
【4】马惠萍, 颜晓峰.时效处理对GH648合金析出相和力学性能的影响［J］.钢铁研究学报,2003,15(7):123-126.
【5】张颖, 韦廷立.热暴露对TA19钛合金锻件拉伸性能的影响［J］.理化检验-物理分册,2013,49(4):216-218.
【2】陈国良.高温合金学［M］.北京: 冶金工业出版社, 1988.
【3】黄乾尧, 李汉康.高温合金［M］.北京: 冶金工业出版社, 2000.
【4】马惠萍, 颜晓峰.时效处理对GH648合金析出相和力学性能的影响［J］.钢铁研究学报,2003,15(7):123-126.
【5】张颖, 韦廷立.热暴露对TA19钛合金锻件拉伸性能的影响［J］.理化检验-物理分册,2013,49(4):216-218.
相关信息