HSn70-1船用冷凝管腐蚀穿孔失效分析
Failure Analysis of Corrosion Perforation of HSn70-1 Brass Tube Used for Ship
摘 要
某船用HSn70-1冷凝管使用过程中出现腐蚀穿孔。通过化学成分、金相组织和能谱分析以及扫描电镜等方法对失效样品进行了分析。结果表明, 介质中的Cl-引起管内壁局部点蚀, 加上冲刷腐蚀、脱锌腐蚀、晶间腐蚀的交互作用, 引起腐蚀加速, 最终导致穿孔。提出了预防或延缓腐蚀穿孔的措施。
腐蚀穿孔
失效分析
冲刷腐蚀
脱锌腐蚀
晶间腐蚀
HSn70-1
corrosion perforation
failure analysis
erosion-corrosion
dezincification corrosion
intergranular corrosion
Abstract
Corrosion perforation occurred on HSn70-1 brass tubes used for ship. The failure samples were analyzed by means of chemical composition analysis, metallographic observation, energy spectroscopy analysis and scanning electron microscopy (SEM). The results showed that the pitting corrosion caused by Cl- was the major reason for corrosion perforation, combined with the interaction of erosion-corrosion, dezincification corrosion and intergranular corrosion, resulting in accelerated corrosion and finally leading to corrosion perforation of the HSn70-1 brass tube. Some prevention measures were put forward.
中图分类号 TG178
所属栏目 失效分析
基金项目
收稿日期 2010/8/16
修改稿日期 2010/10/8
网络出版日期
作者单位点击查看
备注蒋长乐,工程师,
引用该论文: JIANG Chang-le,CUI Wen-yuan,WEI Shao-lin. Failure Analysis of Corrosion Perforation of HSn70-1 Brass Tube Used for Ship[J]. Corrosion & Protection, 2011, 32(1): 74
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】中国腐蚀与防护学会“金属腐蚀手册”编辑委员会主编. 金属腐蚀手册[M]. 上海:上海科学技术出版社,1987.
【2】谢苏江,马玉录,张斌,等. 凝汽器铜管的腐蚀和防护研究[J]. 化工设备与防腐蚀, 2003(2):56-61.
【3】曲政,张奎志,孙彬,等. 滨海电厂凝汽器及相连管道的腐蚀与防护[J]. 腐蚀与防护,2005,29(2):72-74.
【4】王碧文,王涛,王祝堂. 铜合金及其加工技术[M]. 北京:化学工业出版社,2007.
【5】朱祖芳编著. 有色金属的耐腐蚀性及其应用[M]. 北京:化学工业出版社,1994.
【2】谢苏江,马玉录,张斌,等. 凝汽器铜管的腐蚀和防护研究[J]. 化工设备与防腐蚀, 2003(2):56-61.
【3】曲政,张奎志,孙彬,等. 滨海电厂凝汽器及相连管道的腐蚀与防护[J]. 腐蚀与防护,2005,29(2):72-74.
【4】王碧文,王涛,王祝堂. 铜合金及其加工技术[M]. 北京:化学工业出版社,2007.
【5】朱祖芳编著. 有色金属的耐腐蚀性及其应用[M]. 北京:化学工业出版社,1994.
相关信息