紫铜摩擦集电材料在阴雨环境中的腐蚀与磨损行为
Corrosion and Abrasion Behaviors of T2 Sliding-collecting-current Material in Rainy Environment
摘 要
在HST-100载流高速摩擦磨损试验机上, 考察了紫铜摩擦集电材料在阴雨环境下的腐蚀与磨损行为, 采用扫描电镜(SEM)对磨损表面形貌进行了观测, 并对磨损表面宏观温度进行了测量。结果表明,阴雨环境中的水雾,一方面降低了磨损面的温度起到润滑及减磨作用; 另一方面电弧产生的频率增加了电弧侵蚀的几率, 但总的来说, 水雾可以有效地改善该摩擦集电材料的腐蚀与磨损行为。紫铜摩擦集电材料在阴雨环境中的腐蚀与磨损机理表现为电弧侵蚀和轻微的粘着磨损。
腐蚀与磨损
电弧侵蚀
水润滑
机理
sliding-collecting-current material
corrosion and abrasion
arc erosion
waterlubrication
mechanism
Abstract
The corrosion and abrasion behaviors of T2/QCr0.5 rubbing pairs in rainy environment were studied using a friction and wear tester of HST-100 under current-carrying condition. The morphology and macroscopic temperature of worn surfaces were observed and measured by scanning electron microscopy(SEM) and thermocouple respectively. The results show that the fog simutating rainy environment could improve the corrosion and abrasion behaviors of T2 sliding-collecting-current material by lowering temperature of worn surfaces. The corrosion and abrasion mechanism with fog was arc erosion and slight adhesive wear.
中图分类号 TG146.1
所属栏目 试验研究
基金项目 国家自然科学基金项目(50432020); 国家重点基础研究发展计划(973计划)资助项目(2007CB607603); 台州职业技术学院重点课题(2010ZD04)
收稿日期 2010/4/9
修改稿日期 2010/5/24
网络出版日期
作者单位点击查看
备注胡道春,讲师,
引用该论文: HU Dao-chun,WANG Lei. Corrosion and Abrasion Behaviors of T2 Sliding-collecting-current Material in Rainy Environment[J]. Corrosion & Protection, 2011, 32(2): 90
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】Paul G Hegda, Gordon J Thackray. Computer evaluation of electric railway catenary equipment by the method of normal modes[J]. IEEE Trans. Ind., 1981, 17(9):139-145.
【2】于涤. 高速接触网受流的理论分析[J]. 铁道学报, 1998, 20(5): 58-64.
【3】He Da Hai, Rafael R Manory, Norm Grady. Wear of railway contact wires against current collector materials[J]. Wear,1998,215: 146-155.
【4】李鹏. 载流摩擦磨损性能研究[D]. 河南: 河南科技大学硕士学位论文, 2003.
【5】胡道春.滑板材料载流摩擦磨损中电弧侵蚀特性研究[D]. 河南: 河南科技大学硕士学位论文, 2008.
【6】侯明. 铬青铜/黄铜摩擦副载流条件下摩擦学特性研究[D]. 河南: 河南科技大学硕士学位论文, 2006.
【7】赵彦文. 碳材料高速载流摩擦磨损性能研究[D]. 河南: 河南科技大学硕士学位论文, 2006.
【8】戴南山. 高速受流性能探讨[J]. 电力机车技术, 2001, 24(1):17-18.
【9】王蕾, 胡道春. C/C复合材料抗电弧侵蚀性能研究[J]. 中国腐蚀与防护学报, 2009, 29(3):235-240.
【10】Shunichi Kubo,Koji Kato. Effect of arc discharge on wear rate of Cu-impregnated carbon strip in unlubricated sliding against Cu trolley under electric current[J]. Wear, 1998, 216:172-178.
【11】李鹏, 张永振, 孙乐民. 有无电流条件下铬青铜/纯铜摩擦副摩擦磨损性能[J]. 润滑与密封,2003(2):56-57.
【12】Hiroki Nagasawa,Koji Kato. Wear mechanism of copper alloy wire sliding against iron-base strip under electric current[J]. Wear, 1998, 216:179-183.
【13】胡道春, 孙乐民, 上官宝. 动载荷条件下紫铜铬青铜受流摩擦磨损性能研究[J]. 中国腐蚀与防护学报, 2009, 29(1):35-39.
【14】支龙,吴新跃,崔玉舸.青铜-石墨热喷涂层在干摩擦和水润滑条件下的摩擦磨损性能[J]. 润滑与密封,2006(3):53-55.
【15】贾均红, 周惠娣, 王静波, 等. 青铜-石墨复合材料在干摩擦和水润滑下的摩擦磨损性能及磨损机理研究[J]. 摩擦学学报, 2002, 22(1):36-39.
【16】陆峰, 张晓云, 汤智慧,等. 碳纤维复合材料与铝合金电偶腐蚀行为研究[J]. 中国腐蚀与防护学报, 2005, 25(1):39-43.
【2】于涤. 高速接触网受流的理论分析[J]. 铁道学报, 1998, 20(5): 58-64.
【3】He Da Hai, Rafael R Manory, Norm Grady. Wear of railway contact wires against current collector materials[J]. Wear,1998,215: 146-155.
【4】李鹏. 载流摩擦磨损性能研究[D]. 河南: 河南科技大学硕士学位论文, 2003.
【5】胡道春.滑板材料载流摩擦磨损中电弧侵蚀特性研究[D]. 河南: 河南科技大学硕士学位论文, 2008.
【6】侯明. 铬青铜/黄铜摩擦副载流条件下摩擦学特性研究[D]. 河南: 河南科技大学硕士学位论文, 2006.
【7】赵彦文. 碳材料高速载流摩擦磨损性能研究[D]. 河南: 河南科技大学硕士学位论文, 2006.
【8】戴南山. 高速受流性能探讨[J]. 电力机车技术, 2001, 24(1):17-18.
【9】王蕾, 胡道春. C/C复合材料抗电弧侵蚀性能研究[J]. 中国腐蚀与防护学报, 2009, 29(3):235-240.
【10】Shunichi Kubo,Koji Kato. Effect of arc discharge on wear rate of Cu-impregnated carbon strip in unlubricated sliding against Cu trolley under electric current[J]. Wear, 1998, 216:172-178.
【11】李鹏, 张永振, 孙乐民. 有无电流条件下铬青铜/纯铜摩擦副摩擦磨损性能[J]. 润滑与密封,2003(2):56-57.
【12】Hiroki Nagasawa,Koji Kato. Wear mechanism of copper alloy wire sliding against iron-base strip under electric current[J]. Wear, 1998, 216:179-183.
【13】胡道春, 孙乐民, 上官宝. 动载荷条件下紫铜铬青铜受流摩擦磨损性能研究[J]. 中国腐蚀与防护学报, 2009, 29(1):35-39.
【14】支龙,吴新跃,崔玉舸.青铜-石墨热喷涂层在干摩擦和水润滑条件下的摩擦磨损性能[J]. 润滑与密封,2006(3):53-55.
【15】贾均红, 周惠娣, 王静波, 等. 青铜-石墨复合材料在干摩擦和水润滑下的摩擦磨损性能及磨损机理研究[J]. 摩擦学学报, 2002, 22(1):36-39.
【16】陆峰, 张晓云, 汤智慧,等. 碳纤维复合材料与铝合金电偶腐蚀行为研究[J]. 中国腐蚀与防护学报, 2005, 25(1):39-43.
相关信息