摘 要
国内不少工程中使用的钢筋阻锈剂大都含有亚硝酸盐成分, 对环境有一定危害作用。由于钼酸盐具有低毒和较好的缓蚀作用, 制备了钼酸盐系阻锈剂。采用盐水浸渍试验、干湿冷热循环试验、失重和硬化砂浆等方法, 对新型阻锈剂阻锈性能进行系统的评价, 并与市售阻锈剂的性能进行了比较。在模拟液中对其阻锈性能作进一步的验证。结果表明, 该阻锈剂是一种高效、环保的阻锈剂, 在掺量3%时, 能发挥最佳阻锈效果。
Abstract
In many domestic projects, most of rebar inhibitors contains the nitrite ingredient, which harms the environment. Due to the low poison and good inhibition function, a new kind of molybdate inhibitor was prepared. Its anti-rust performance was analyzed systematically by salt water immersion test, dry-wet-cold-hot circulation test, weight loss experiment and hardened mortar test, and was compared with a commercial inhibitor. The performance was verified further in concrete simulation liquid. The results show that it is an efficient, environmentally friendly rust inhibitor, and the best rust resistant effect was exhibited in a dosage of 3%.
中图分类号 TG174.42
所属栏目 试验研究
基金项目
收稿日期 2010/4/16
修改稿日期 2010/5/7
网络出版日期
作者单位点击查看
备注于爱红,硕士研究生,
引用该论文: YU Ai-hong,XU Bin,PANG Lu-feng,FANG Juan-juan. A New Kind of Rebar Inhibitor[J]. Corrosion & Protection, 2011, 32(2): 109
共有人对该论文发表了看法,其中:
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】洪乃丰. 氯盐腐蚀与钢筋阻锈剂[J]. 混凝土,2004,171(1):58-60.
【2】洪乃丰. 混凝土中钢筋腐蚀与防护技术(6)[J]. 工业建筑,2000,30(1):57-60.
【3】Kalman D G. Sodium molybdate as a corrosion inhibitor of mild steel in natural waters[J]. Corrosion,1993,49(8):43-45.
【4】Mustafa C M. Corrosion inhibition of Al by molybdate citric acid & nitrite in simulated cooling water[J]. Corrosion Prevention & Control,1997,44(2):49-52.
【5】Devasenapath A. Effect of externally added malybdate on repassivation & stress corrosion cracking of type 304 stainless steel in HCl[J]. Corrosion,1996,52(4):243-246.
【6】张大利,王元,陈翠红,等. 一种低碱低掺量钢筋混凝土阻锈剂[J]. 商品混凝土,2009(10):28-30.
【2】洪乃丰. 混凝土中钢筋腐蚀与防护技术(6)[J]. 工业建筑,2000,30(1):57-60.
【3】Kalman D G. Sodium molybdate as a corrosion inhibitor of mild steel in natural waters[J]. Corrosion,1993,49(8):43-45.
【4】Mustafa C M. Corrosion inhibition of Al by molybdate citric acid & nitrite in simulated cooling water[J]. Corrosion Prevention & Control,1997,44(2):49-52.
【5】Devasenapath A. Effect of externally added malybdate on repassivation & stress corrosion cracking of type 304 stainless steel in HCl[J]. Corrosion,1996,52(4):243-246.
【6】张大利,王元,陈翠红,等. 一种低碱低掺量钢筋混凝土阻锈剂[J]. 商品混凝土,2009(10):28-30.
相关信息