环保型镀锌家电板表面性能比较
Surface Performance of Environment-friendly Galvanized Sheets
摘 要
采用盐雾试验、电化学阻抗法和辉光光谱法对三种环保型家电镀锌板表面的涂层进行研究, 发现涂层的结构和涂层中缓蚀剂的分布对涂层表面性能有较大影响, 提高涂层中Si和缓蚀剂的含量, 保持缓蚀剂分布均匀可以有效提高镀锌板的表面性能。表面涂层中有机高聚合物含量较多时, 高温下容易发生氧化变色。
环保
表面性能
galvanised sheet
environment-protection
surface performance
Abstract
The surface performance of three kinds of environment-friendly galvanized sheets was studied by salt spray test, eletrochemical impedance spectroscopy (EIS) and glow discharge spectrometer (GDS). The results showed that the coating performance was greatly influenced by the structure and distribution of inhibitor on the suface of film. Surface performance could be enhanced by increasing the content of inhibitor and Si, and by keeping umform inhibitor distribution. It would be oxidated when the surface of film contained more organic polymer.
中图分类号 TG174.4
所属栏目 应用技术
基金项目
收稿日期 2010/3/22
修改稿日期 2010/6/2
网络出版日期
作者单位点击查看
引用该论文: CHEN Yong,PAN Yan-fang,LI Guo-bin,ZHOU Xiao-zhou. Surface Performance of Environment-friendly Galvanized Sheets[J]. Corrosion & Protection, 2011, 32(2): 143
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】张启富. 有机涂层钢板[M]. 北京:化学工业出版社2003.
【2】钱余海,李平,申龙. 宝钢电镀锌无铬耐指纹钢板的特性研究[J]. 宝钢技术,2005(1): 42-45.
【3】曹楚南,张鉴清. 电化学阻抗谱导论[M]. 北京:科学出版社,2002.
【4】曹旭,李宁,黎德育. 镀锌板无铬耐指纹涂料助剂的研究[J]. 材料保护,2007,40(10): 38-41.
【5】宫丽,卢燕平. 纳米硅溶胶/丙烯酸复合防蚀薄膜的研究[J]. 材料保护,2005,38(1): 17-19.
【6】于武刚,岳远广,张启富,等. 纳米SiO2对热镀锌钢板耐指纹涂层性能的影响研究[J]. 材料保护,2007,40(11): 56-58.
【2】钱余海,李平,申龙. 宝钢电镀锌无铬耐指纹钢板的特性研究[J]. 宝钢技术,2005(1): 42-45.
【3】曹楚南,张鉴清. 电化学阻抗谱导论[M]. 北京:科学出版社,2002.
【4】曹旭,李宁,黎德育. 镀锌板无铬耐指纹涂料助剂的研究[J]. 材料保护,2007,40(10): 38-41.
【5】宫丽,卢燕平. 纳米硅溶胶/丙烯酸复合防蚀薄膜的研究[J]. 材料保护,2005,38(1): 17-19.
【6】于武刚,岳远广,张启富,等. 纳米SiO2对热镀锌钢板耐指纹涂层性能的影响研究[J]. 材料保护,2007,40(11): 56-58.
相关信息