Inhibition of EDBDP for Q235 Steel in Sulfuric Acicl Solution
摘 要
合成了O, O′-二苄基二硫代磷酸-N, N-二乙铵(EDBDP), 采用电化学法和静态悬挂失重法研究了EDBDP在5% H2SO4介质中对Q235钢的缓蚀性能。静态悬挂失重法研究表明, 25 ℃时, 在5% H2SO4溶液中, 当缓蚀剂浓度为100 mg/L时, 缓蚀率高达99.29%; 动电位极化曲线研究表明, 该缓蚀剂受H2SO4浓度、温度和浸泡时间的影响较小, 属于混合型缓蚀剂; 吸附拟合表明, 缓蚀剂在Q235钢表面的吸附符合Langmuir吸附等温式, 属于自发进行的化学吸附。
Abstract
A new corrosion inhibitor named N, N-diethylammonium O, O′-dibenzydithiophosphate (EDBDP) had been synthesized and the inhibition was investigated for Q235 steel in 5% H2SO4 solution by weight loss tests and electrochemical techniques. The studies of weight loss showed that the inhibition efficiency was up to 99.29% when the inhibitor concentration was 100 mg/L in 5% H2SO4 solution at 25±1 ℃, and the adsorption of EDBDP on Q235 steel surface obeyed the Langmuir's isotherm. The electrochemical studies revealed that the inhibitor was mixed-type inhibitor, whose inhibition efficiency was hardly affected by concentration of H2SO4, temperature and immersion time.
中图分类号 TG174.42
所属栏目 试验研究
基金项目 材料腐蚀与防护四川省高校重点实验室重点项目(2008CL03); 四川省教育厅重点项目(09ZA057); 四川省科技厅科技支撑计划项目(2010GZ0130); 四川省自贡市科技局重点项目(08X01)
收稿日期 2010/5/2
修改稿日期 2010/5/19
网络出版日期
作者单位点击查看
引用该论文: XIE Bin,LAI Chuan,ZOU Li-ke,HUANG Chun,FENG Jian-shen,ZHAO Bin,HE Lin-xin. Inhibition of EDBDP for Q235 Steel in Sulfuric Acicl Solution[J]. Corrosion & Protection, 2011, 32(3): 166
共有人对该论文发表了看法,其中:
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】张军, 胡松青, 王勇, 等. 1-(2-羟乙基)-2-烷基-咪唑啉缓蚀剂缓蚀机理的理论研究[J]. 化学学报, 2008, 66(22):2469-2475.
【2】余国骏, 汤兵. 缓蚀剂研究中的电化学方法[J]. 中国腐蚀与防护学报, 2009, 29(1):76-80.
【3】余志强, 徐强, 任志峰, 等. 金属在酸性介质中有机缓蚀剂的研究进展[J]. 电镀与精饰, 2008, 30(11):19-23.
【4】陈云, 唐永明, 杨文忠, 等. 盐酸介质中3, 5-二(2-噻吩基)-1, 2, 4-三唑(2-TAT)对紫铜的缓蚀作用[J]. 腐蚀科学与防护技术, 2009, 21(4):406-409.
【5】汤兵, 陈欣义. 酸洗过程中的缓蚀剂[J]. 清洗世界, 2006, 22(2):22-28.
【6】Hong T, Sun Y H, Jepson W P. Study on corrosion inhibitor in large pipelines under multiphase flow using EIS[J]. Corrosion Science, 2002, 44(1):101-112.
【7】Siddiqui R A, Abdullah H A. Hydrogen embrittlement in 0.31% carbon steel for petrochemical application[J]. Journal of Materials Processing Technology, 2005, 170: 430-435.
【8】Bentiss F, Bouanis M, Mernari B, et al. Understanding the adsorption of 4H-1, 2, 4-triazole derivativeson mild steel surface in molar hydrochloric acid[J]. Applied Surface Science, 2007, 253:3696-3704.
【9】谢斌, 吴士业. (5, 7, 7, 12, 14, 14-六甲基-1, 4, 8, 11-四氮杂环十四-4, 11-二烯合镍双(O, O′-二烃基二硫代磷酸酯)的合成与研究[J]. 高等学校化学学报, 1998, 19(1):74-77.
【10】Quraishi M A, Sharma H K. 4-Amino-3-butyl-5-mercapto-1, 2, 4-triazole:a new corrosion inhibitor for mild steel in sulphuric acid[J]. Materials Chemistry and Physics, 2002, 78:18-21.
【11】曹楚南. 腐蚀电化学原理[M]. 第三版.北京:化学工业出版社, 2008.
【12】Shukla S K, Quraishi M A. The efects of pharmaceutically active compound doxycycline on the corrosion of mild steel in hydrochloric acid solution[J]. Corrosion Science, 2010, 52(2):314-321.
【2】余国骏, 汤兵. 缓蚀剂研究中的电化学方法[J]. 中国腐蚀与防护学报, 2009, 29(1):76-80.
【3】余志强, 徐强, 任志峰, 等. 金属在酸性介质中有机缓蚀剂的研究进展[J]. 电镀与精饰, 2008, 30(11):19-23.
【4】陈云, 唐永明, 杨文忠, 等. 盐酸介质中3, 5-二(2-噻吩基)-1, 2, 4-三唑(2-TAT)对紫铜的缓蚀作用[J]. 腐蚀科学与防护技术, 2009, 21(4):406-409.
【5】汤兵, 陈欣义. 酸洗过程中的缓蚀剂[J]. 清洗世界, 2006, 22(2):22-28.
【6】Hong T, Sun Y H, Jepson W P. Study on corrosion inhibitor in large pipelines under multiphase flow using EIS[J]. Corrosion Science, 2002, 44(1):101-112.
【7】Siddiqui R A, Abdullah H A. Hydrogen embrittlement in 0.31% carbon steel for petrochemical application[J]. Journal of Materials Processing Technology, 2005, 170: 430-435.
【8】Bentiss F, Bouanis M, Mernari B, et al. Understanding the adsorption of 4H-1, 2, 4-triazole derivativeson mild steel surface in molar hydrochloric acid[J]. Applied Surface Science, 2007, 253:3696-3704.
【9】谢斌, 吴士业. (5, 7, 7, 12, 14, 14-六甲基-1, 4, 8, 11-四氮杂环十四-4, 11-二烯合镍双(O, O′-二烃基二硫代磷酸酯)的合成与研究[J]. 高等学校化学学报, 1998, 19(1):74-77.
【10】Quraishi M A, Sharma H K. 4-Amino-3-butyl-5-mercapto-1, 2, 4-triazole:a new corrosion inhibitor for mild steel in sulphuric acid[J]. Materials Chemistry and Physics, 2002, 78:18-21.
【11】曹楚南. 腐蚀电化学原理[M]. 第三版.北京:化学工业出版社, 2008.
【12】Shukla S K, Quraishi M A. The efects of pharmaceutically active compound doxycycline on the corrosion of mild steel in hydrochloric acid solution[J]. Corrosion Science, 2010, 52(2):314-321.
相关信息