用一种进口水基含铝高温防腐蚀涂料制备了金属陶瓷涂层, 介绍了制备的工艺, 对该涂层的性能进行了研究。结果表明, 按照一定的喷涂压力和喷涂距离进行喷涂, 可获得表面均匀、结合良好的涂层。喷涂一层IPcote9183可以获得厚度为0.01 mm～0.02 mm的涂层; 可进行多层喷涂。厚度为0.02～0.03 mm的涂层, 中性盐雾试验可达到1000 h不出现红锈。

An aluminium containing high-temperature anti-corrosion water-based paint was used to prepare metallic-ceramic coating, and performance of the coating was studied. The results showed that the coating was uniform and had good adhesion under the conditions of a certain spray pressure and nozzle/sample distance. The coating thickness was 0.01 ～ 0.02 mm for every IPcote9183 layer. The thickness could increase by repeating spray + dry. The coating with thickness of 0.02 ～ 0.03 mm was used to salt fog test and there was no red rust after 1000 h.