通过正交试验确定了稀土镧盐钝化镀锌钢板的最佳工艺条件为: 30 g/L硝酸镧、20 ml/L双氧水、pH值为4、40 ℃下钝化30 s。利用碱浸失重试验、中性盐雾试验和电化学阻抗谱评价了钝化膜的耐腐蚀性能。结果表明, 经稀土镧盐处理后的试样阻抗值相对于空白试样大幅度提高, 腐蚀速率降低1个数量级, 抗白锈时间达54 h。扫描电镜(SEM)结果表明, 稀土镧盐钝化膜对基体的覆盖度较高。
Abstract
The process of rare earth lanthanum conversion coating for galvanized steel was studied by orthogonal experiment. The optimized passivation parameters were obtained as follows. the concentration of La(NO3) 30 g/L, H2O2 20 ml/L, pH 4 and passivation at 40 ℃ for 30 s. The corrosion resistance was examined by weight loss test, neutral salt spray test and electrochemical impedance spectruscopy. The results showed that the corrosion impedance of the pretreated sample was significantly improved, the corrosion rate was decreased by one order of magnitude, and the anti-white rust time was 54 h. Scanning electron microscopy (SEM) showed that the conversion coat covered the surface of zinc compactly.
中图分类号 TG178
所属栏目 应用技术
基金项目
收稿日期 2010/7/25
修改稿日期 2010/9/3
网络出版日期
作者单位点击查看
联系人作者曹晓燕(caoxxyu@126.com)
引用该论文: LIU Xiao-feng,CAO Xiao-yan,MAN Rui-lin. Rare Earth Lanthanum Passivation Technology of Galvanized Steel[J]. Corrosion & Protection, 2011, 32(6): 483
被引情况:
【1】姜琴,李伟华,侯保荣,张璐, "镀锌板无铬钝化技术进展",腐蚀与防护 34, 101-106(2013)
【2】李红玲, "6061铝合金镧转化膜工艺参数的正交优化",腐蚀与防护 34, 933-936(2013)
共有人对该论文发表了看法,其中:
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】Mekhalif Z, Forget L, Delhalle J. Investigation of the protective action of chromate coatings on hot-dip galvanized steel: role of wetting agents[J]. Corrosion Science, 2005, 47(3): 547-566.
【2】Hua L, Chan Y C, Wu Y P. The determination of hexavalent chromium (Cr6+) in electronic and electrical components and products to comply with RoHS regulations[J]. Journal of Hazardous Materials, 2009, 163(2/3): 1360-1368.
【3】杨宁, 龙晋明. 稀土钝化——金属防腐蚀表面处理新技术[J]. 稀土, 2002, 23(2): 55-61.
【4】Lu J, Wu H, Kong G, et al. Growth and corrosion behavior of rare earth film on hot-dip galvanized steel[J]. Transactions of Nonferrous Metals Society of China, 2006, 16(6): 1397-1401.
【5】Trabelsi W, Cecilio P, Ferreira M G, et al. Electrochemical assessment of the self-healing properties of Ce-doped silane solutions for the pre-treatment of galvanized steel substrates[J]. Progress in Organic Coatings, 2005, 54(4): 276-279.
【2】Hua L, Chan Y C, Wu Y P. The determination of hexavalent chromium (Cr6+) in electronic and electrical components and products to comply with RoHS regulations[J]. Journal of Hazardous Materials, 2009, 163(2/3): 1360-1368.
【3】杨宁, 龙晋明. 稀土钝化——金属防腐蚀表面处理新技术[J]. 稀土, 2002, 23(2): 55-61.
【4】Lu J, Wu H, Kong G, et al. Growth and corrosion behavior of rare earth film on hot-dip galvanized steel[J]. Transactions of Nonferrous Metals Society of China, 2006, 16(6): 1397-1401.
【5】Trabelsi W, Cecilio P, Ferreira M G, et al. Electrochemical assessment of the self-healing properties of Ce-doped silane solutions for the pre-treatment of galvanized steel substrates[J]. Progress in Organic Coatings, 2005, 54(4): 276-279.
相关信息