Influence of Additives on Room Temperature Hard Anodizing of Aluminum Alloy
摘 要
传统的铝硬质阳极氧化工艺需要较低的温度和较高的电压, 能耗大且工件易烧损。本工作通过在阳极氧化电解液中添加草酸、丙三醇及NiSO4, 提高阳极氧化温度上限实现了常温下的硬质氧化, 并采用正交试验法对添加剂含量进行优化, 获得了最佳的常温硬质阳极氧化工艺。
Abstract
The traditional process of hard anodic oxidation of aluminum has some shortcomings such as high energy consumption, easy burn, needs of low-temperature and high voltage. Oxalic acid, glycerol and NiSO4 were added into the electrolyte of anodic oxidation to raise the temperature limit of anodic oxidation, which made the hard anodizing can be carried out at room temperature. And by using orthogonal experiment method, the content of electrolyte additives was optimized and the best hard anodizing process at room temperature was obtained.
中图分类号 TG174
所属栏目 试验研究
基金项目
收稿日期 2010/9/6
修改稿日期 2010/11/1
网络出版日期
作者单位点击查看
备注王顺, 硕士研究生,
引用该论文: WANG Shun,ZHAO Zhan-xi,YIN Xiao-san. Influence of Additives on Room Temperature Hard Anodizing of Aluminum Alloy[J]. Corrosion & Protection, 2011, 32(7): 535
共有人对该论文发表了看法,其中:
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】朱祖芳. 铝合金阳极氧化与表面处理技术[M]. 北京: 化学工业出版社, 2004:94-96.
【2】周谟银. 铝合金常温硬质阳极氧化工艺Ⅱ: 有机添加剂的作用及槽液维护[J]. 电镀与环保, 2002, 22(3): 28-30.
【3】任雅勋. 铝及其合金常温草酸绝缘阳极氧化工艺[J]. 材料保护, 2002, 9(12): 31-32.
【4】周谟银. 铝合金常温硬质阳极氧化Ⅰ常温硬质氧化工艺及影响膜质量的因素[J]. 电镀与环保, 2002, 22(2): 26-28.
【2】周谟银. 铝合金常温硬质阳极氧化工艺Ⅱ: 有机添加剂的作用及槽液维护[J]. 电镀与环保, 2002, 22(3): 28-30.
【3】任雅勋. 铝及其合金常温草酸绝缘阳极氧化工艺[J]. 材料保护, 2002, 9(12): 31-32.
【4】周谟银. 铝合金常温硬质阳极氧化Ⅰ常温硬质氧化工艺及影响膜质量的因素[J]. 电镀与环保, 2002, 22(2): 26-28.
相关信息